以丙烯酸(AA)为原料,过硫酸钾为引发剂,乙二醇为交联剂,添加含量不同(摩尔分数为0.5%,1%,5%和10%)的苯乙烯,制备了聚丙烯酸/苯乙烯二元无规共聚物[P(AA-co-S)]高吸水性树脂。采用傅里叶变换红外光谱仪、扫描电子显微镜,热重分析仪表征了样品的结构、形貌和热稳定性,并系统研究了苯乙烯含量对P(AA-co-S)高吸水性树脂性能的影响。结果表明:P(AA-co-S)高吸水性树脂热稳定性好,苯乙烯的引入提高了树脂的吸液性能,苯乙烯含量为1%(摩尔分数)时,其吸水倍率最高,为784g/g,吸液速率为12.21s。与聚丙烯酸钠(PAA)相比,P(AA-co-S)高吸水性树脂吸水倍率提高了36%,吸液速率提高了16%。
Abstract
Using acrylic acid as raw materials,potassium persulfate as initiator,ethylene glycol as cross-linker,different molar contents (0.5%,1%,5% and 10%) of styrene were added to prepare poly(acrylic acid-co-styrene)[P(AA-co-S)]based superabsorbent resin by aqueous solution.The chemical structure,microstructure and thermal behavior of the resin were characterized by fourier transform infrared spectrometer (FT-IR),scanning electron microscope (SEM) and thermal gravimetric (TG),respectively.The liquid absorption performance of the resin was measured,and the effect of styrene addition on the properties of the resin was investigated.The results showed that when the addition amount of styrene was 1%,the water absorption capacity of the P(AA-co-S) was significantly increased,with water absorption rate of 784g/g and liquid absorption rate of 12.21s.Compared with the sodium polyacrylate superabsorbent resin,the water absorption rate was increased by 36%,and the liquid absorption rate was increased by 16%.
关键词
高吸水性树脂
/
聚丙烯酸钠
/
苯乙烯
/
吸水性能
Key words
superabsorbent resin
/
sodium polyacrylate
/
styrene
/
water absorption ability
P(AA-co-S)高吸水性树脂的制备及性能研究[J].
化工新型材料, 2020, 48(4): 231-233 DOI:
[1] 严小妹,沈慧芳.耐盐性聚丙烯酸类高吸水性树脂的研究进展[J].化工新型材料,2013,41(4):30-32.
[2] 马斐,程冬炳,王颖,等.聚丙烯酸类高吸水性树脂的合成及吸水机理研究进展[J].武汉工程大学学报,2011,33(1):4-9.
[3] 张小红,崔英德,潘湛昌.聚丙烯酸/海藻酸钠高吸水性树脂的制备及生物降解性能[J].化工学报,2005,56(6):1134-1137.
[4] 潘鸽,吴广峰,李欣鹤,等.磺化聚苯乙烯纳米微球-聚丙烯酰胺杂化水凝胶的制备及性能[J].功能高分子学报,2017,30(4):457-463.
[5] 顾文娟,陆亚明,张幼维,等.PMAA纳米水凝胶的水相制备[J].功能高分子学报,2016,29(1):61-67.
[6] Kiatkamjornwong S,Nuisin R,Ma Guanghui,et al.Synthesis of styrenic toner particles by spg emulsification technique[J].高分子科学(英文版),2000,18(4):309-322.
[7] 乌兰.高吸水性树脂的吸水机理及制备方法[J].化学与粘合,2006,28(3):36-39.
[8] 张亚涛,张林,陈欢林.聚(丙烯酸-丙烯酰胺)/水滑石纳米复合高吸水性树脂的制备及表征[J].化工学报,2008,59(6):1565-1570.
[9] 安建科,刘毅,王爱勤.PSY-g-PAA/Na-MMT复合高吸水性树脂的制备及其对Cu2+的吸附[J].功能高分子学报,2011,24(2):186-190.
[10] 刘立华,刘冬莲,沈玉龙,等.聚丙烯酸钠/高岭土复合高吸水性树脂的制备及性能研究[J].南开大学学报:自然科学版,2017,50(6):79-84.
[11] 王进,于善普,李旭东.超高吸水性树脂的吸水性和抗电解质性能的研究[J].印染,2000,26(9):16-18.
[12] 陈密峰,张秀娟.反相悬浮共聚法合成耐盐快吸水性树脂[J].化工学报,2003,54(11):128-132.
[13] Lim D W,Song K G,Yoon K J,et al.Synthesis of acrylic acid-based superabsorbent interpenetrated with sodium PVA sulfate using inverse-emulsion polymerization[J].European Polymer Journal,2002,38(3):579-586.
[14] 胡灯,李琼,赵彦生,等.改性聚天冬氨酸/聚(丙烯酸-丙烯酰胺)互穿网络吸水性树脂的制备及表征[J].高分子材料科学与工程,2016,32(10):30-35.
[15] 刘丽君,张含,张雪莹,等.聚丙烯酸类互穿聚合物网络高吸水性树脂的合成[J].天津科技大学学报,2018,33(2):43-48.
基金资助
国家自然科学基金(21703194);江苏省自然科学基金(BK20180178);徐州市科技计划项目(KC18010)