聚乙烯醇(PVA)纤维具有高弹性模量且与水泥基体的粘结强度很高。为预防和控制混凝土的早期塑性裂缝,将PVA纤维掺入混凝土可以提高混凝土的增韧性和抗冲击性。对纤维长度不同的PVA纤维混凝土试件进行抗压强度和轴心抗压强度测试,考察了PVA纤维对混凝土试件力学性能的影响。结果表明:掺入PVA纤维后混凝土试件抗压强度略微下降,混凝土试件轴心抗压强度未发生明显变化。
Polyvinyl alcohol fiber(PVA)fiber has high elastic modulus and high bonding strength with cement matrix.In order to prevent and control the early plastic crack of concrete,adding PVA fiber into concrete can improve the toughness and impact resistance.The compressive strength and axial compressive strength of PVA fiber concrete specimens with different fiber lengths were tested.The results showed that the compressive strength of concrete specimens decreased slightly after adding PVA fiber,but the axial compressive strength of concrete specimens did not change significantly.
[1] 谭明轮,孙仁娟,周志东,等.PVA纤维长度与掺量对工程水泥基复合材料性能影响试验研究[J].铁道建筑,2014,35(3):115-117.
[2] 林晖.掺PVA纤维混凝土的力学及变形性能研究[D].南京:南京航空航天大学,2006.
[3] 曹源文,赵毅,王棋,等.PVA纤维水泥稳定碎石拌合均匀性研究[J].重庆大学学报:自然科学版,2018,37(5):29-33.
[4] 李彩霞.聚乙烯醇纤维增强水泥稳定碎石材料性能研究[J].交通科学与工程,2018,34(1):19-49.
[5] Kanda T,Li V C.Interface property and apparent strength of high-strength hydrophilic fiber in cement matrix[J].ASCE Journal of Materials in Civil Engineering,1998,10(1):5.
[6] 钱桂枫,高祥彪,钱春香.PVA纤维对混凝土力学性能的影响[J].混凝土与水泥制品,2010(3):52-54.
[7] 汪卫,潘钻峰,孟少平,等.国产PVA纤维增强水泥基复合材料力学性能研究[J].工业建筑,2014,44(增刊):958-964.
[8] 潘钻峰,汪卫,孟少平,等.混杂聚乙烯醇纤维增强水泥基复合材料力学性能[J].同济大学学报:自然科学版,2015,43(1):33-40.
基金资助
国家自然科学基金(51868062);内蒙古自然科学基金(2017MS(LH)0523);城市地下工程教育部重点实验室开放研究基金(TUE2017-02)
PDF
(3012KB)