助剂对现场成型式导电胶性能的影响

李静, 张贵恩, 李炳章, 范晋锋, 王执乾, 李克训

作者信息 +

Influenced of different additives on the property of FIP conductive adhesive

Li Jing, Zhang Guien, Li Bingzhang, Fan Jinfeng, Wang Zhiqian, Li Kexun

Author information +

文章历史 +

Received		Published
2019-01-16		2020-01-20
Issue Date	Revised Date
2020-02-11	2019-01-16

PDF (1353K)

摘要

以α,ω-二羟基聚二甲基硅氧(107胶)、铜银粉为原料,通过添加触变剂、偶联剂、抑制剂等助剂,制备了室温固化导电胶,考察了各种助剂对导电胶性能的影响。结果表明:制备的导电胶拉伸强度为3.5MPa,扯断伸长率为185%,体积电阻率为0.020Ω·cm,长宽比为0.78,具有良好的触变效果和优异的综合性能。

Abstract

RTV conductive adhesives were prepared using α,ω-dihydroxy polydimethylsiloxane and copper silver powder as raw materials,adding thixotropic agent,coupling agent and inhibitor agent as additives.The research on the effects of the additives on the properties of conductive adhesives was focused.The results showed that the tensile strength of the conductive adhesive was 3.5MPa,tensile elongation was 185%,volume resistivity was 0.020Ω·cm,and the aspect ratio was 0.78,which has good thixotropic effect and excellent comprehensive performance.

关键词

导电胶 / 助剂 / 力学性能 / 导电性能

Key words

conductive adhesive / additive / mechanical property / conductivity

引用本文

引用格式 ▾

助剂对现场成型式导电胶性能的影响[J]. 化工新型材料, 2020, 48(1): 193-195 DOI:

登录浏览全文

4963

注册一个新账户忘记密码

参考文献

原文顺序 | 出版日期 | 本文引用

[1] 湖北省电磁兼容学会.电磁兼容性原理及应用[M].北京:国防工业出版社,1996:1-8.
[2] 郑玉玲,于建军,覃竞亮,等.电磁污染的危害与防护研究进展[J].职业与健康,2011,27(6):689-691.
[3] 马颖崎,施杰,刘宇盖.一种具有电磁屏蔽性能的导电橡胶及其制造方法:中国,101050307A.12[P].2007-10-10.
[4] 王玲,赵浩峰.一种电磁屏蔽导电橡胶复合材料及其制备方法:中国,101503534A.12[P].2009-08-12.
[5] 郭建华,曾幸荣,罗全焜,等.气相白炭黑对氟橡胶/硅橡胶共混胶性能的影响[J].合成材料老化与应用,2009,38(3):4-8;27.
[6] 刘丰,李晓俊,刘小兰,等.单组分室温硫化硅橡胶的开发与应用[J].新技术新工艺,2005(3):40-43.
[7] 罗穗莲,潘慧铭,王跃林.硅烷偶联剂改性碳酸钙对室温硫化硅橡胶密封胶的性能影响[J].中国胶粘剂,2008,17(9):35-37.
[8] 邸明伟,张丽新,何世禹,等.室温硫化硅橡胶的增强改性研究进展[J].中国胶粘剂,2005,14(3):36-40.
[9] 王忠,陈立贵,付蕾,等.硅橡胶力学性能的改善[J].机械工程材料,2007,31(8):54-55.
[10] 戴丽娜,张志杰,赵云峰,等.聚硅氧烷交联剂与掺杂SiO₂协同增强RTV硅橡胶的研究[J].有机硅材料,2009,23(4):225-229.