为了提高铝镁合金粉的防氧化性和分散性,在不同反应温度条件下,采用硅烷偶联剂对40μm雾化球形镁铝合金粉进行表面改性,利用热分析、扫描电镜、电子能谱、粒度分析等手段对表面处理后的样品进行了分析,研究了硅烷偶联剂反应温度对铝镁合金粉表面改性的影响。结果表明:硅烷偶联剂能够在铝镁合金粉表面形成一层硅烷膜,从而避免铝镁合金粉体的氧化,降低其熔点、缩短氧化温度区间,可以提高铝镁合金粉的分散性;反应时间为1.5h、反应温度在40℃时表面改性效果最优。
In order to improve the dispersion and oxidation resistance,silane coupling agent was chosen for processing 40μm atomized spherical Al-50Mg alloy powder at different reaction temperature.By means of thermal analysis,SEM,EDS and particle size analysis,the surface of coated samples were analyzed.Effect of different reaction temperature of silane coupling agent coating on Al-50Mg alloy powder was be studied.Results showed that silane coupling agent can form a silane layer in Al-50Mg alloy powder surface thereby avoiding the oxidation,reducing the melting point,shortening range of oxidation temperature,improving the dispersion of Al-50Mg alloy powder.When the reaction time reached 1.5 hours and the reaction temperature reached 40℃,the modification effect was the best.
[1]王晓峰,郝仲璋.炸药发展中的新技术[J].火炸药学报,2002,25(4):35-38.
[2]胥会祥,李兴文,赵凤起,等.纳米金属粉在火炸药中应用进展[J].含能材料,2011,19(2):232-239.
[3]殷海权,潘清,张建亮,等.铝粉对炸药性能的影响[J].含能材料,2004,12(5):318-320.
[4]李凤生.特种超细粉体制备技术及应用[M].北京:国防工业出版社,2002:135-137.
[5]杨富宝,吴希俊.纳米晶Al及Al-Mg合金的合成与性能研究进展[J].材料导报,2014,18(9):30-34.
[6]Han B Q,Lee Z,Nutt S R,et al.Mechanical properties of an ultrafine-grained Al-7.5 pct Mg alloy[J].Metallurgical and Meterials Transactions A,2003,34(3):603-613.
[7]姚超,高国生,林西平,等.硅烷偶联剂对纳米二氧化钛表面改性的研究[J].无机材料学报,2006,21(2):315-318.
[8]薛茹君,吴玉程.硅烷偶联剂表面修饰纳米氧化铝[J].应用化学,2007,24(11):1236-1239.
[9]李强,朱燕娟,张仲举,等.温度及搅拌速度对纳米氢氧化镍性能的影响[J].人工晶体学报,2010,39(3):751-754.
[10]董萍.硅烷偶联剂在金属表面处理中的应用研究[D].武汉:华中师范大学,2014:21-23.
[11]郑伟超,李双寿,汤彬,等.Mg-Al二元合金组织和性能的研究[J].铸造,2006,55(1):15-16.
[12]王红霞,梁伟,赵琦,等.二元Mg-Al合金铸态及ECAP态组织与性能研究[J].稀有金属材料与工程,2008,37(11):2005-2007.
[13]邓晓燕,崔作林,杜芳林,等.纳米二氧化钛的热分析表征[J].无机材料学报,2001,16(6):1089-1093.
[14]刘子如.含能材料热分析[M].北京:国防工业出版社,2008.
[15]司林华.纳米金属燃料[J].化学教育,2007(1):11-12.
基金资助
军械工程学院原始创新基金(YSCX-1401)
PDF
(3444KB)