为改善膨润土在水处理中固液分离困难的问题,采用微波法,以石墨烯对有机膨润土进行改性,并利用聚乙烯醇(PVA)为粘结剂、淀粉为造孔剂,经高温焙烧制备石墨烯改性有机膨润土颗粒(CTMAB-GMBG、OTAC-GMBG)。利用EDS、FT-IR、SEM、XRD、BET等手段对样品进行表征分析,以明确制备过程对石墨烯改性有机膨润土颗粒内部构造变化的影响。结果表明,石墨烯与有机膨润土复合成功,石墨烯中的羧基与季铵盐离子形成了酰胺键,石墨烯改性有机膨润土颗粒的层间距由1.265nm增大至2.480nm(CTMAB-GMBG)、2.708nm(OTAC-GMBG),比表面积分别增大至60.3506m2/g(CTMAB-GMBG)和51.3482m2/g(OTAC-GMBG),且颗粒的孔隙结构优化明显。
In order to improve the effect of powder bentonite in solid-liquid separation for water treatment,graphene modified organobentonite granules (CTMAB-GMBG,OTAC-GMBG)were prepared.Graphene was chosen to modify powdery organobentonite under microwave.The granules were prepared by mixing with polyvinyl alcohol (PVA) as binder and starch as pore former under roasting.The samples were characterized by EDS,FT-IR,SEM,XRD and BET to confirm how the process of preparation would affect the internal structure of GMBG.The results showed that graphene and organobentonite were uniformly composited and the key bonds were formed between the frameworks of organobentonite.The basal spacing increased from 1.265nm to 2.480nm(CTMAB-GMBG) and 2.708nm(OTAC-GMBG),the surface area went up to 60.3506m2/g(CTMAB-GMBG)and 51.3482m2/g(OTAC-GMBG)respectively,while the pore structure of GMBG was evidently improved by granulation.
[1] 李志娟,王晓飞.阳离子改性的有机复合膨润土吸附材料的制备、表征及吸附性能研究[J].化工新型材料,2016,44(1):92-97.
[2] 王毅,张婷,冯辉霞,等.阳离子改性膨润土对水中亚甲基蓝吸附性能研究[J].非金属矿,2008,31(2):57-61.
[3] 潘洁,鲍建国,靳孟贵,等.改性膨润土处理污水处理厂二级出水的实验研究[J].环境科学与技术,2011,34(5):140-143.
[4] 陈晓磊,邓李川,关爽.有机膨润土制备表征及其应用[J].长春工业大学学报(自然科学版),2014,35(6):692-695.
[5] 金春姬,肖波,任娟,等.粉末状和颗粒状有机膨润土对克百威的吸附[J].环境污染与防治,2011,33(6):65-70.
[6] 秦雄,刘红,嵇阳远,等.微波一步法合成颗粒膨润土及其柱试验吸附废水水中2,4-二氯酚[J].硅酸盐通报,2015,34(9):2652-2661.
[7] 陈仕稳.改性膨润土颗粒制备及对微污染水中UV254和NH4-N的去除研究[D].广州:广东工业大学,2016.
[8] 罗平,张辉,吴翌辰,等.膨润土颗粒的制备及对废水中铬的吸附性能研究[J].非金属矿,2014,37(2):72-78.
[9] 原爱娟,岳钦艳,李倩,等.颗粒膨润土的制备技术及染料脱色性能的研究[J].山东大学学报,2008,38(5):88-93.
[10] 肖利萍,孙晓明,潘纯林,等.焙烧颗粒膨润土的制备及其对废水中Mn2+的吸附研究[J].给水排水,2011,37(3):133-135.
[11] 陈红燕,羊依金,张卓君,等.城市污泥-膨润土颗粒吸附剂的制备及其处理含铅废水的研究[J].非金属矿,2009,32(6):53-56.
[12] 邢奕,刘敏,洪晨,等.石墨烯改性有机膨润土吸附性能及其动力学[J].工程科学学报,2016,38(3):438-445.
[13] Pan J,Bao J G,Jin M G,et al.Modified bentonite for secondary effluent water from wastewater treatment plant[J].Environ Sci Technol,2011,34(5):140.
[14] 张景煌.石墨烯复合物在含Hg废水处理中的应用研究[J].闽西职业技术学院学报,2011,13(2):115-120.
[15] 谢伟楠,聂锦旭,邹祥俊,等.改性膨润土复合新型颗粒的制备与标准[J].硅酸盐通报,2016,35(9):2990-2994.
基金资助
河北省教育厅指导项目“改性膨润土-石墨烯颗粒处理微污染水源水技术研究”(Z2017055)
PDF
(4267KB)