摘要
采用水蒸汽为活性介质,对粉状樟子松快速热解炭(FPC)与生物油酚醛树脂(BPF)粘结剂混合模压成型物——成型热解炭进行活化处理,得到了成型活性炭(ACM)。采取正交试验方法,考察了活化温度、活化时间和活化剂流量对ACM碘值、亚甲基蓝吸附值和抗压强度三项性能指标的影响,优化了ACM活化工艺;采用比表面积及孔隙度分析仪、X射线衍射仪、傅里叶红外光谱仪、元素分析仪及场发射电镜扫描仪对ACM孔隙结构与理化性能进行了表征。结果表明:活化过程中各因素对ACM抗压强度、碘值及亚甲基蓝吸附值作用差异程度依次为活化温度、活化时间和活化介质流量;最佳活化工艺为活化温度800℃,活化时间60min,活化介质流量600mL/min;ACM碘及亚甲基蓝吸附值分别为690.64mg/g和111mg/g,BET比表面积为731.303m2/g,总孔容为0.5892cm3/g,平均孔径为3.223nm,抗压强度达到3.74MPa;ACM呈介孔吸附特点,石墨化程度较低,表面活性较强,含有酚、醇、醚、酯和烯烃等多种官能团,同时具有吸附能力和催化作用,可用于生活污水处理。
Abstract
Activated carbon monoliths(ACM) were prepared by H2O activation method using powered fast pyrolytic char(FPC) as a raw material and bio-oil phenol-formaldehyde (BPF) resin as a binder.The effect of activation temperature,activation time,and activation medium flow on the physical and mechanical properties (iodine adsorption value,methylene blue adsorption value,compressive strength) of resultant was investigated.The properties of ACM were observed using BET,XRD,FT-IR and SEM,etc.The results showed that the main influential factor was activation temperature,followed by the activation time,with the activation medium flow being relatively less.The optimum conditions were activation temperature of 800℃,activation time of 60min and activation medium flow of 600mL/min.The adsorption values of iodine and methylene blue reached 690.64mg/g and 111mg/g respectively.BET surface area,total pore volume and average pore diameter were 731.303m2/g,0.5892cm3/g and 3.223nm.The compression strength of activated carbon monolith reached 3.74MPa.ACM appeared to be mainly mesoporous with low graphitization and contained phenol,alcohol,ether,ester and olefin groups which could be used in sewage treatment.
关键词
快速热解炭
/
成型活性炭
/
活化
/
表征
Key words
pyrolytic char
/
activated carbon monolith
/
activation
/
characterization
成型生物质快速热解炭制备活性炭活化工艺研究及其性能表征[J].
化工新型材料, 2018, 46(3): 239-243 DOI:
[1] Mohan D,Pittman C U,Steele P H.Pyrolysis of wood/biomass for bio-oil:a critical review[J].Energy & Fuels,2006,20(3):848-889.
[2] 吴创之,周肇秋,阴秀丽,等.我国生物质能源发展现状与思考[J].农业机械学报,2009,40(1):91-99.
[3] Ang?n D,Altintig E,Köse T E.Influence of process parameters on the surface and chemical properties of activated carbon obtained from biochar by chemical activation[J].Bioresource Technology,2013,148(11):542-549.
[4] Ang?n D,Köse T E,Selengil U.Production and characterization of activated carbon prepared from safflower seed cake biochar and its ability to absorbreactive dyestuff[J].Applied Surface Science,2013,280(5):705-710.
[5] Saeidi N,Lotfollahi M N.A procedure to form powder activated carbon into activated carbon monolith[J].The International Journal of Advanced Manufacturing Technology,2015,81(5-8):1281-1288.
[6] Arami-Niya A,Rufford T E,Zhu Z.Activated carbon monoliths with hierarchical pore structure from tar pitch and coal powder for the adsorption of CO2,CH4 and N2[J].Carbon,2016,103:115-124.
[7] Chen C,Kennel E B,Stiller A H,et al.Carbon foam derived from various precursors[J].Carbon,2006,44(8):1535-1543.
[8] Vargas-Delgadillo D P,Giraldo L,Moreno-Piraján J C.Preparation and characterization of activated carbon monoliths with potential application as phenol adsorbents[J].E-Journal of Chemistry,2010,7(2):531-539.
[9] 方建辉,姚伯元.气相吸附用成型活性炭[J].化工进展,2009,28(S1):237-239.
[10] 丁佳丽.非沥青粘结剂煤质活性炭的制备及其用于烟气脱硫的研究[D].太原:太原理工大学,2013.
[11] Stavropoulos G G,Zabaniotou A A.Production and characterization of activated carbons fromolive-seed waste residue[J].Microporous and Mesoporous Materials,2005,82(1-2):79-85.
[12] Yorgun S,Vural N,Demiral H.Preparation of high-surface area activatedcarbon from paulownia by ZnCl2 activation[J].Microporous and Mesoporous Materials,2009,122(1-3):189-194.
[13] Aygün A,Yenisoy-Karakas S,Duman I.Production of granular activated carbon from fruit stones and nutshells and evaluation of their physical,chemical and adsorption properties[J].Microporous and Mesoporous Materials,2003,66(2):189-195.
[14] 李鑫,李伟光,王广智,等.基于ZnCl2活化法的污泥基活性炭制备及其性质[J].中南大学学报(自然科学版),2013,44(10):4362-4370.
[15] 陈鸯飞.高成炭率酚醛树脂的制备及其在C/C复合材料中的应用[D].长沙:湖南大学,2014.
[16] Liu Y,Cai Q,Li H,et al.Fabrication and characterization of mesoporous carbon nanosheets using halloysite nanotubes and polypyrrole via a template-like method[J].Journal of Applied Polymer Science,2013,128(1):517-512.
[17] Yang C S,Jang Y S,Jeong H K.Bamboo-based activated carbon for supercapacitor applications[J].Current Applied Physics,2014,14:1616-1620.
[18] 李栋.生物质活性炭的制备、成型及活化机理研究[D].烟台:烟台大学,2013.
[19] 王迪.制备过程和表面改性对煤质活性炭官能团影响规律研究[D].北京:中国矿业大学,2014.
[20] Ma C,Xiong H,Song X.Preparation and characterization of eggplant stalk activated carbon by zinc chloride[J].Journal of Functional Materials,2012,43(3):342-345.
基金资助
北京市科技计划项目(Z161100001316004)