使用混酸对碳纳米管表面进行酸化改性,研究了酸化改性碳纳米管(MWCNTs-COOH)在丙酮中的分散稳定性。采用长时超声的方法将MWCNTs-COOH分散在双马树脂(BMI)体系中,制备了烯丙基双酚A改性双马树脂/酸化改性碳纳米管复合材料(BMI-DBA/MWCNTs-COOH)。通过场发射扫描电镜(FE-SEM)观察MWCNTs-COOH在复合材料中的分散性,研究了复合材料的机械性能、热机械性能和耐热性能。结果表明:与BMI相比,当加入0.2%(质量分数)MWCNTs-COOH时,复合材料的拉伸强度从61.9MPa提高到87.6MPa,提高了42%;弯曲强度从77.6MPa提高到102.9MPa,提高了33%;抗冲击强度从4.84kJ/cm2提高到7.04kJ/cm2,提高了约1.5倍。MWCNTs-COOH的引入可有效改善碳纳米管与树脂基体间的界面作用力,显著提高复合材料的模量和玻璃化转变温度(Tg);与BMI相比,加入MWCNTs-COOH的复合材料在N2氛围下800℃的残炭率提高了约8%。
Carbon nanotubes were acidified by mixtural acid and the obtained acidified carbon nanotubes (MWCNTs-COOH) were dispersed in acetone which the dispersion stability was investigated.Allyl bisphenol A modified bismaleimide resin/acidified carbon nanotubes composite (BMI-DBA/MWCNTs-COOH) was prepared by dispersing acidified carbon nanotubes in bismaleimide resin (BMI) system which using long time sonication method.The dispersion of acidified carbon nanotubes in the composite was investigated by field emission scanning electronic microscope (FE-SEM).The mechanical,thermo-mechanical and heat resistant properties of composite were studied.The results indicated that,comparing with the neat resin system,when 0.2wt% acidified carbon nanotubes were added,the tensile strength of composite was increased by about 42% from around 61.9MPa to 87.6MPa.The flexural strength was increased from around 77.6MPa to 102.9MPa with an increment of 33%,and the impact strength was elevated up to 7.04kJ/m2 which was about 1.5 times of 4.84kJ/cm2 of neat resin.The addition of acidified carbon nanotubes could improve the interface interaction between carbon nanotubes and resin matrix efficiently,then improved the modulus and Tg of composite obviously.Also,comparing with neat resin,the char yield at 800 ℃ in nitrogen of composite with acidified carbon nanotubes was increased by about 8%.
[1] Landman D.Developments in reinforced plastics-5[M].Netherlands:Springer,1986,39-81.
[2] 梁国正,顾爱娟.双马来酰亚胺树脂[M].北京:化学工业出版社,1997,1-19.
[3] Wu Guanglei,Kou Kaichang,Li Ning,et al.Electrically conductive adhesive based on bismaleimide-triazine resin filled with microcoiled carbon fibers[J].J Appl Polym Sci,2013,128(2):1164-1169.
[4] Zeng Xiaoliang,Yu Shuhui,Sun Rong.Thermal behavior and dielectric property analysis of boron nitride-filled bismaleimide-triazine resin composites[J].J Appl Polym Sci,2013,128(3):1353-1359.
[5] Zhang Baoyan,Li Ping,Chen Xiangbao.Studies of modified bismaleimide resins part Ⅰ:the influence of resin composition on thermal and impact properties[J].J Mater Sci,1998,33(23):5683-5687.
[6] Qin Haihu,Mather P T,Baek J B,et al.Modification of bisphenol-A based bismaleimide resin (BPA-BMI) with an allyl-terminated hyperbranched polyimide (AT-PAEKI)[J].Polymer,2006,47(8):2813-2821.
[7] Tang Haoyu,Li Wanwan,Fan Xinghe,et al.Synthesis,preparation and properties of novel high-performance allyl-maleimide resins[J].Polymer,2009,50(6):1414-1422.
[8] Boey F,Xiong Y,Rath S K.Glass-transition temperature in the curing process of bismaleimide modified with diallylbisphenol A[J].J Appl Polym Sci,2010,91(5):3244-3247.
[9] Cheng Qunfeng,Bao Jianwen,Park Jingyu,et al.High mechanical performance composite conductor:multi-walled carbon nanotube sheet/bismaleimide nanocomposites[J].Adv Funct Mater,2010,19(20):3219-3225.
[10] Yao Wei,Gu Aijuan,Liang Guozheng,et al.Preparation and properties of hollow silica tubes/bismaleimide/diallylbisphenol a composites with improved toughness,dielectric properties,and flame retardancy[J].Polym Adv Technol,2012,23(3):326-335.
[11] 吴广荣,郑建邦,郝娟.纳米SiO2改性BOZ/BMI/BADCy共聚物的制备及性能研究[J].工程塑料应用,2012,40(6):25-28.
[12] Surender R,Mahendran A,Thamaraichelvan A,et al.Curing studies of bisphenol A based bismaleimide and cloisite 15a nanoclay blends using differential scanning calorimetry and model-free kinetics[J].J Appl Polym Sci,2013,128(1):712-724.
[13] 郑国栋,张清杰,邓火英,等.不同官能化碳纳米管对MWCNTs-碳纤维/环氧树脂复合材料力学性能的影响[J].复合材料学报,2015,32(3):640-648.
[14] Xie Xiaolin,Mai Yiuwing,Zhou Xingping.Dispersion and alignment of carbon nanotubes in polymer matrix:a review[J].Mater Sci Eng,2005,49(4):89-112.
[15] Sun Yaping,Fu Kefu,Lin Yi,et al.Functionalized carbon nanotubes:properties and applications[J].Acc Chem Res,2002,35(12):1096-1104.
[16] Liu Lin,Song Jing,Wang Chong.Effects of modified carbon nanotubes on curing and mechanical properties of N-phenyl maleimide/bismaleimide composites[J].Adv Mater Res,2011,335-336:285-292.
[17] Saito T,Matsushige K,Tanaka K.Chemical treatment and modification of multi-walled carbon nanotubes[J].Physica B Condensed Matter,2002,323(1-4):280-283.
[18] Eklund P C,Holden J M,Jishi R A.Vibrational modes carbon nanotubes:spectroscopy theory[J].Carbon,1995,33(7):959-972.
[19] Hu Xiao,Meng Jingru.Effect of organoclay on the curing reactions in bismaleimide/diallyl bisphenol A resin[J].J Polym Sci:Part A:Polym Chem,2005,43(5):994-1006.
[20] Hwang G,Shieh Y,Hwang K C.Efficient load transfer to polymer-grafted multiwalled carbon nanotubes in polymer composites[J].Adv Funct Mater,2004,14(5):487-491.
基金资助
广东普通高校青年创新人才项目(2015KQNCX168);五邑大学青年基金(2015zk04);五邑大学青年基金创新团队项目(2015td01)
PDF
(3156KB)