采用水热法合成了Fe3O4/GO磁性纳米复合材料,对其进行X射线衍射(XRD)、红光谱(FT-IR)、扫描电镜(SEM)表征及磁性能测试,并应用于水体6种不同染料的吸附对比,筛选出对该吸附剂具备较强选择性吸附能力的龙胆紫(GV)染料,进一步优化吸附条件,最后对吸附剂的循环应用效果进行了测试。结果表明:所制备的Fe3O4/GO磁性纳米材料对GV的最佳吸附条件为温度20℃、染料初始浓度为30mg/L,吸附剂投加量0.04g/50mL,溶液pH=9、吸附时间30min。在最佳条件下,Fe3O4/GO对GV的移除率高达91.06%,吸附量为34.35mg/g。5次循环利用的移除率仍可达到68.46%。该吸附剂能很好地分散在水中,并可通过磁场从废水中实现快速回收,具有绿色、高效、可循环利用的特点,可用于工业废水处理系统。
Abstract
In this study,Fe3O4/GO magnetic nanocomposite material was successfully synthesized by hydrothermal method.It was characterized by XRD,FT-IR,SEM and magnetic property test,and then applied to the adsorption of six various dyes in water.By comparison,gentian violet (GV) dye with strong selective adsorption capacity for the adsorbent was selected,and the adsorption conditions were further optimized.Finally,the cycling application effect of the adsorbent was tested.The results showed that the optimal adsorption conditions of the prepared Fe3O4/GO magnetic nanomaterials for GV were as follows:temperature of 20℃,initial concentration of dye 30mg/L,adsorbent dosage of 0.04g/50mL,pH=9,and adsorption time of 30 min.Under the optimal conditions,the removal rate of GV by Fe3O4/GO was 91.06%,and the adsorption capacity was 34.35mg/g.The removal rate after 5 cycles could still reach 68.46%.The adsorbent was well dispersed in water and could be quickly recovered from wastewater by magnetic field.It was green,efficient and recyclable,and could be used in industrial wastewater treatment system.
关键词
四氧化三铁/氧化石墨烯
/
磁性复合材料
/
龙胆紫
/
吸附
Key words
Fe3O4/GO
/
magnetic composite material
/
gentian violet
/
adsorption
Fe3O4/GO磁性纳米材料的合成及其对龙胆紫染料的吸附研究[J].
化工新型材料, 2023, 51(11): 295-300 DOI:10.19817/j.cnki.issn1006-3536.2023.11.021
[1] Ariaeenejad S,Motamedi E,Salekdeh G H.Highly efficient removal of dyes from wastewater using nanocellulose from quinoa husk as a carrier for immobilization of laccase[J].Bioresource Technology,2022,349(1):126833.
[2] Maria C,Garcia A H,Silva F,et al.Amido Black 10B a widely used azo dye causes DNA damage in pro-and eukaryotic indicator cells[J].Chemosphere,2019,217:430-436.
[3] Paz A,Carballo J,Jose Perez M,et al.Biological treatment of model dyes and textile wastewaters[J].Chemosphere,2017,181:168-177.
[4] 谢艳新,刘海娟,尚磊,等.染料废水处理最新研究进展[J].印染助剂,2020,37(7):11-16.
[5] 董振,刘亮,郝艳,等.偶氮染料废水处理技术的研究进展[J].水处理技术,2017,43(4):6-10.
[6] Sheng D Y,Yan G,Ji L F.Preparation of FMA flocculant and its effect on the flocculating properties in printing and dyeing wastewater[J].Industrial Water Treatment,2000,20(1):19-21.
[7] El-Kousy Salah M,El-Shorbagy Hadeel G,Abd El-Ghaffar M A.Chitosan/montmorillonite composites for fast removal of methylene blue from aqueous solutions[J].Materials Chemistry and Physics,2020,254:123236.
[8] Sun Q,Yang L.The adsorption of basic dyes from aqueous solution on modified peat-resin particle[J].Water Research,2003,37(7):1535-1544.
[9] Chen K,Du L,Gao P,et al.Super and selective adsorption of cationic dyes onto carboxylate-modified passion fruit peel biosorbent[J].Frontiers in Chemistry,2021,9:646492.
[10] Jing X U,Wen H L,Ouyang J B,et al.Adsorption kinetics of methylene blue on graphene oxide-chitosan composite[J].Journal of Shanghai University(Natural Science),2013,19(4):400-404.
[11] Rajivgandhi G,Rtv V,Raju N,et al.Adsorption of nickel ions from electroplating effluent by graphene oxide and reduced graphene oxide[J].Environmental Research,2021,199(2019):111322.
[12] 弓子伟,王公正,王娇娇,等.磁性氧化石墨烯高分子复合微球的制备及对染料吸附性能的研究[J].西北大学学报(自然科学版),2018,48(3):385-392.
[13] Ren R P,Li W,Lv Y K.A robust,superhydrophobic graphene aerogel as a recyclable sorbent for oils and organic solvents at various temperatures[J].Journal of Colloid and Interface Science,2017,500:63-68.
[14] 王旭珍,周泉,任素贞,等.溶剂热法制备Fe3O4/氧化石墨烯复合材料及其性能研究[J].功能材料,2015,46(3):3045-3049.
[15] 张磊磊.基于氧化石墨烯的复合材料(Fe3O4/GO和GO/EY)制备及其应用[D].成都:成都理工大学,2017.
[16] 陈宁宁,丁长坤,张宇鑫,等.磁性GO的制备及其对亚甲基蓝的吸附性能研究[J].天津化工,2021,35(4):25-28.
基金资助
河南省高等学校重点科研项目(22B150023);河南省大学生创新项目(202312949008);郑州师范学院大学生创新项目(DCZ2022043)