摘要
以废弃柚子皮瓤和氧化石墨烯(GO)为碳源,氨水为掺杂剂,采用水热与真空抽滤相结合的方法,制备氮掺杂石墨烯(N-G)、氮掺杂水热碳膜(N-HC)和氮掺杂水热碳/石墨烯复合膜[N-HC/G-X,X=1、2、4、5,X代表柚子皮瓤(g)与GO(mg)的质量比],利用扫描电镜、X射线衍射、拉曼光谱和红外光谱表征碳材料的物理化学性质,并进行了吸附Zn(Ⅱ)和截留Cr(Ⅵ)的实验。结果表明:N-G、N-HC和N-HC/G-X均为典型片层结构,N-HC是获得薄膜的必要成分,N-HC/G-1和N-HC/G-2的成膜效果优于N-HC/G-4和N-HC/G-5,N-HC/G-1的膜厚度大约为65μm,C、N和O的质量分数分别为65.63%、15.06%和19.31%。N-G、N-HC和N-HC/G-X都是无定形碳材料,N-HC的d002片层间距最大,随着N-HC/G-X中N-G质量的逐渐增多,N-HC/G-X的片层间距逐渐减小,表面缺陷和混乱程度有所增大,且N-HC/G-X表面存在大量的含氧和含氮官能团,可以提供更多活性吸附位点,有利于提升对重金属的吸附效果。N-HC/G-1和N-HC/G-2对Zn(Ⅱ)的吸附效果优于N-HC,N-HC/G-2对Zn(Ⅱ)的吸附率可达79.13%,而N-HC/G-4和N-HC/G-5对Zn(Ⅱ)的吸附效果较N-HC差。N-HC和N-HC/G-X对Cr(Ⅵ)的截留率随复合材料中N-G质量的增多而逐渐增大,水通量则逐渐减小,N-HC/G-5对Cr(Ⅵ)的截留率高达86.45%,水通量为18.20L/(m2·h)。
Abstract
In this paper,nitrogen-doped graphene (N-G),nitrogen-doped hydrothermal carbon films (N-HC),and nitrogen-doped hydrothermal carbon/graphene composite films (N-HC/G-X,X=1,2,4,5,X represents the mass ratio of pomelo peel pulp (g) to GO (mg)) were prepared via a combined hydrothermal and vacuum filtration process using waste pomelo peel pulp and graphene oxide (GO) as carbon sources,as well as ammonia as dopant.The physicochemical properties of N-G,N-HC and N-HC/G-X were characterized by SEM,XRD,Raman and FTIR,and the experiments of Zn(Ⅱ) adsorption and Cr(Ⅵ) retention were also carried out.Research results showed that:N-G,N-HC and N-HC/G-X were all typical lamellar-like structures.N-HC was a necessary component to obtain the thin films.The film-forming effects of N-HC/G-1 and N-HC/G-2 were better than those of N-HC/G-4 and N-HC/G-5.The film thickness of N-HC/G-1 was about 65 μm,and the mass percentages of C,N and O were 65.63%,15.06% and 19.31%,respectively.N-G,N-HC and N-HC/G-X samples were all amorphous carbon materials.The d002 lamellar spacing of N-HC was the largest.With the increasing of N-G mass in N-HC/G-X samples,the lamellar spacing of N-HC/G-X decreased gradually,while the degree of surface defects and disorder increased.Furthermore,there were a large number of oxygen-containing and nitrogen-containing functional groups on the surface of N-HC/G-X,which could provide more active adsorption sites and improve the adsorption properties of heavy metals.The adsorption effect of N-HC/G-1 and N-HC/G-2 for Zn(Ⅱ) was better than that of N-HC,and the Zn(Ⅱ) adsorption rate on N-HC/G-2 was 79.13%,while the adsorption effect of N-HC/G-4 and N-HC/G-5 for Zn(Ⅱ) was worse than that of N-HC.The interception rate of N-HC and N-HC/G-X for Cr(Ⅵ) increased gradually with the increasing of N-G mass in the composites,while the water flux decreased gradually.The interception rate of N-HC/G-5 for Cr(Ⅵ) reached 86.45%,and the water flux was 18.20L/(m2·h).
关键词
氮掺杂
/
水热碳
/
复合膜
/
石墨烯
/
重金属
Key words
nitrogen-doped
/
hydrothermal carbon
/
composite films
/
graphene
/
heavy metals
氮掺杂水热碳/石墨烯复合膜的制备及其性能研究[J].
化工新型材料, 2023, 51(11): 105-110 DOI:10.19817/j.cnki.issn1006-3536.2023.11.013
[1] Wang Z,Li Z.Removal of Cr(Ⅵ) from aqueous solution by newspapers[J].Desalination,2009,249(1):175-181.
[2] 郑德论,张锐龙,张彩云,等.石墨烯复合功能材料及其在重金属离子检测的电化学研究与应用[J].化学世界,2020,61(1):16-32.
[3] Yang L,Hu J,He L,et al.One-pot synthesis of multifunctional magnetic N-doped graphene composite for SERS detection,adsorption separation and photocatalytic degradation of Rhodamine 6G[J].Chemical Engineering Journal,2017,327:694-704.
[4] Ai L,Jiang J.Removal of methylene blue from aqueous solution with self-assembled cylindrical graphene-carbon nanotube hybrid[J].Chemical Engineering Journal,2012,192:156-163.
[5] Cheng Y,Li H,Fang C,et al.Facile synthesis of reduced graphene oxide/silver nanoparticles composites and their application for detecting heavy metal ions[J].Journal of Alloys and Compounds,2019,787:683-693.
[6] 李帆.杂原子掺杂石墨烯类新材料的研制及其在样品前处理中的应用[D].重庆:重庆大学,2019.
[7] 白秋红,舒羽,李聪,等.基于农林废弃生物质的功能性多孔碳材料构筑及应用研究[C].扬州:中国化学会第一届农业化学学术讨论会,2019.
[8] 孙晓旭,徐进,储智强.不同方法改性柚皮制备的活性炭吸附亚甲基蓝试验[J].河海大学学报(自然科学版),2021,49(6):536-542.
[9] 王琼,黄丽媛,古黄玲,等.生物质废弃物柚子皮作为潜在吸附剂用于废水处理[J].湖南工业大学学报,2019,33(6):89-94.
[10] Huang Y,Lee X,Macazo F C,et al.Fast and efficient removal of chromium(Ⅵ) anionic species by a reusable chitosan-modified multi-walled carbon nanotube composite[J].Chemical Engineering Journal,2018,33(9):259-267.
[11] 高小转.葡萄糖水热碳化制备多孔碳电极材料及改性研究[D].太原:太原理工大学,2018.
[12] 赖润燊.生物质炭增强复合材料的制备及其性能研究[D].福州:福建农林大学,2019.
[13] Ping C,Wang L K,Gan W,et al.Nitrogen-doped nanoporous carbon nanosheets derived from plant biomass:an efficient catalyst for oxygen reduction reaction[J].Energy & Environmental Science,2014,7(12):4095-4103.
[14] Deng H,Li Q,Liu J,et al.Active sites for oxygen reduction reaction on nitrogen-doped carbon nanotubes derived from polyaniline[J].Carbon,2017,11(2):219-229.
[15] Wang J,Hao J,Liu D,et al.Porous boron carbon nitride nanosheets as efficient metal-free catalysts for the oxygen reduction reaction in both alkaline and acidic solutions[J].ACS Energy Letters,2017,2(2):306-312.
[16] Chen F,Zhang M,Ma L,et al.Nitrogen and sulfur codoped micro-mesoporous carbon sheets derived from natural biomass for synergistic removal of chromium(Ⅵ):adsorption behavior and computing mechanism[J].Science of the Total Environment,2020,730:138930.
[17] 马东兴.功能化水热炭材料的制备及应用[D].秦皇岛:燕山大学,2014.
[18] Liu Z,Zhang Z,Jia Z,et al.New strategy to prepare ultramicroporous carbon by ionic activation for superior CO2 capture[J].Chemical Engineering Journal,2018,337:290-299.
[19] 张飞飞.多孔生物质炭及其复合物的制备与铀吸附性能研究[D].哈尔滨:哈尔滨工程大学,2019.
[20] 田强.生物质基电极材料的制备及其在超级电容器中的应用[D].天津:天津大学,2019.
[21] 朱林林.生物质碳制备氧化石墨烯及氧化石墨烯、异氰酸酯对聚苯并噁嗪的改性研究[D].合肥:合肥工业大学,2017.
[22] 王小娟,王清雯,高学理,等.胺基化氧化石墨烯复合纳滤膜对染料的截留性能研究[J].水处理技术,2017,43(1):31-35.
[23] 韩硕,王磊,孟晓荣,等.氧化石墨烯改性PVDF超滤膜截留染料性能研究[J].水处理技术,2018,44(11):50-54.
基金资助
国家自然科学基金面上项目(42172189);河南省自然科学基金青年基金项目(222300420134);河南省高等学校重点科研项目(21A610002);河南工程学院2021年度科研培育基金项目(PYXM202105)