以结晶紫内酯(CVL)为隐色剂,双酚A(BPA)为显色剂,十四醇、十六醇和十八醇为溶剂,制备热致变色复配物,通过计算复配物变色前后色差,确定CVL/BPA/十四醇复配物、CVL/BPA/十六醇复配物和CVL/BPA/十八醇复配物最佳质量比分别为1∶4∶40、1∶3∶30和1∶4∶50。以密胺树脂为壁材,质量比最佳的复配物为芯材,通过原位聚合法制备了热致变色微胶囊,并对其性能进行了测试。结果表明热致变色复配物和微胶囊均具有良好的变色性能,微胶囊技术能够有效提升材料的耐热性和循环稳定性。
Abstract
The thermochromic compounds were fabricated with crystal violet lactone as color former,bisphenol A as color developer,and tetradecanol,hexadecanol and octadecanol as organic solvents.By calculating the color difference before and after color change,the optimal mass ratios of CVL/BPA/tetradecanol compound,CVL/BPA/hexadecanol compound and CVL/BPA/octadecanol compound were determined as 1∶4∶40,1∶3∶30 and 1∶4∶50,respectively.Then the thermochromic microcapsules were prepared by in-situ polymerization using melamine resin as wall material and the compound with the optimal mass ratio as core material,and their properties were tested.The results showed that both the thermochromic compounds and the microcapsules had good color-changing performance,and the microencapsulation technology could effectively improve the heat resistance and cyclic stability of the materials.
关键词
可逆变色材料
/
微胶囊
/
原位聚合法
Key words
reversible color-changing material
/
microencapsulation
/
in-situ polymerization
可逆热致变色材料的制备及性能研究[J].
化工新型材料, 2023, 51(11): 93-97 DOI:10.19817/j.cnki.issn1006-3536.2023.11.001
[1] 刘晖,陈国强,吕凯敏.智能纺织品分类与评价方法研究[J].针织工业,2021(10):63-67.
[2] Zhang Yuxuan,Zhai Xiaoqiang.Preparation and testing of thermochromic coatings for buildings[J].Solar Energy,2019,191:504-548.
[3] Seeboth A,Klukowska A,Ruhmann R,et al.Thermochromic polymer materials[J].Chinese Journal of Polymer Science,2007,25(2):123-135.
[4] Cheng Youliang,Zhang Xiaoqiang,Fang Changqing,et al.Discoloration mechanism,structures and recent applications of thermochromic materials via different methods:a review[J].Journal of Materials Science & Technology,2018,34(12):2225-2234.
[5] 胡勇.有机可逆热致变色材料微胶囊制备及性能研究[D].武汉:武汉轻工大学,2015.
[6] 耿晓叶.可逆热致变色相变储能材料微胶囊的制备、表征及性能研究[D].天津:天津工业大学,2021.
[7] Wang Hao,Luo Jie,Yang Yanyang,et al.Fabrication and characterization of microcapsulated phase change materials with an additional function of thermochromic performance[J].Solar Energy,2016,139:591-598.
[8] 牟明鹏.有机可逆热致变色材料的制备研究[D].沈阳:沈阳理工大学,2020.
[9] Liu Bingxin,Rasines Mazo Alicia,Gurr Paul A,et al.Reversible nontoxic thermochromic microcapsules[J].ACS Applied Materials & Interfaces,2020,12(8):9782-9789.
[10] Hakami Abdullatif,Indrakar Sharan,Krishnegowda Ashwini,et al.Microencapsulation of thermochromic material by silicon oxide nanoparticles[J].Key Engineering Materials,2021,6125:41-48.
[11] 张书圣,温永红,丁彩凤.有机化合物系统鉴定手册[M].第八版.北京:化学工业出版社,2007.
基金资助
北京市教委项目(KM201910012009)