碳纤维已在众多领域发挥着越来越重要的作用,质量是其应用的保障,碳纤维原丝用油剂则是其中一个极其重要的质量把控点。经过多年的努力,我国中间相沥青基碳纤维已处于工程化开发进程中,因此亟需专用油剂以保障碳纤维产品的性能与质量。对国内外沥青基碳纤维原丝专用油剂的研究情况进行了总结和分析,具体涉及油剂分类、成分及其功能,以及上油工艺等,重点讨论了油剂成分及上油工艺的改进情况,并对我国中间相沥青纤维油剂今后的研发方向进行了探讨,以期为本行业的研究人员提供一定的帮助。
Carbon fibers have played an increasingly important role in many fields,and the quality is the guarantee of its applications.Oil agent for carbon fiber precursor is one of the extremely important keys for quality control.After years of great efforts,mesophase pitch-based carbon fiber has been in the process of engineering development in China.So,the corresponding oil agent is urgently needed to ensure the property and quality of carbon fiber products.In order to provide some help for the researchers in this field,the development of oil agent for precursor at home and abroad was summarized.The review contained the classification,composition of oiling agent and its corresponding functions,as well as oiling process especially for the improvement of oil agent composition and oiling process.Furthermore,the future research and development direction of oil agent for mesophase pitch-based carbon fiber precursor in China was discussed.
[1] Ye C,We H,Zhu S P,et al.Microstructure of high thermal conductivity mesophase pitch-based carbon fibers[J].Carbon,2021,36(5):980-986.
[2] Liu C J,Chen X J,Liang D C,et al.Development of pitch-based carbon fibers:a review[J].Energy Sources Part A Recovery Utilization and Environmental Effects,2020,DOI:10.1080/15567036.2020.1806952.
[3] 钱鑫,皇静,张永刚,等.国外PAN基碳纤维的研究现状及发展趋势[J].高科技纤维与应用,2011,36(3):5.
[4] 钱鑫,王雪飞,马洪波,等.国内外PAN基高模量碳纤维的技术现状与研究进展[J].合成纤维工业,2021,44(5):58-64.
[5] 高峰阁,迟卫东,张鸿翔,等.国内外MPCF发展概况与展望[J].高科技纤维与应用,2015,40(5):33-37.
[6] 贺文晋,张晓欠,刘丹,等.沥青基碳纤维制备研究进展[J].煤化工,2019,47(4):72-75,81.
[7] 徐保明,张家晖,唐强,等.沥青基炭纤维制备方法研究进展[J].炭素技术,2017,36(5):5-8.
[8] 张鹏,黄东,叶崇,等.中间相沥青炭纤维增强金属基复合材料研究进展[J].炭素技术,2021,40(5):1-7,76.
[9] 姚远.中间相沥青基碳纤维及其在飞机上的应用[J].纤维复合材料,2018,36(3):73-76.
[10] 史景利,马昌.沥青基碳纤维的研发及产业化[J].高科技纤维与应用,2014,39(3):7-14.
[11] 任蕊,皇甫慧君,曹晨茜,等.沥青基碳纤维的制备方法及其产业化研究[J].应用化工,2018,47(10):2254-2259.
[12] 田雨华,王象东,王硕,等.中间相沥青基碳纤维的生产及其性能表征[J].高科技纤维与应用,2022,47(1):21-26.
[13] 贺福.高性能碳纤维原丝与油剂[J].高科技纤维与应用,2004,29(5):1-5,10.
[14] 刘金水,伍孝,叶崇,等.一种沥青纤维氧化专用隔离油剂及其使用方法:CN110273300A[P].2019-09-24.
[15] 李正雄.有机硅在化纤油剂中的应用[J].合成纤维,2004,33(2):35-36.
[16] 关颖.碳纤维及原丝用油剂研发及应用[J].化工新型材料,2012,40(6):4.
[17] 田川徹,片山博雄.沥青基碳纤维用处理剂:JPH0345719A[P].1991-02-27.
[18] 刘春玲,马静,董文生,等.通用级沥青基碳纤维纺丝油剂:CN103757899A[P].2014-04-30.
[19] 白峰,康秀珍,伍孝.一种沥青碳纤维纺丝用油剂:CN104452270A[P].2015-03-25.
[20] 田川徹,片山博雄,末村耕二,等.沥青基碳纤维用处理剂:JPS6426720A[P].1989-01-30.
[21] 松本泰次,花谷诚二,吉田稔,等.沥青基碳纤维制造方法:JPS6468521A[P].1989-03-14.
[22] 小峰喜久治,日野隆,黑田博之.碳纤维及石墨纤维制造方法:JPH01111018A[P].1989-04-27.
[23] 伍孝,王斌,林源,等.一种沥青基炭纤维连续长丝的制备方法:CN103046165A[P].2013-04-17.
[24] Koga S,Okajima T,Yamaguchi S,et al.Process for producing a carbon fiber from pitch material:EP0133457A1[P].1985-02-27.
[25] Kagizaki M,Takakura T,Tahara H.Process for producing a carbon fiber from pitch material:EP0175200A2[P].1986-03-26.
[26] 嵯峨三男,神下识,三好史洋,等.沥青基碳纤维制备方法:JPS6278218A[P].1987-04-10.
[27] 木村功,木森强.碳纤维制备方法:JPS591724A[P].1984-01-07.
[28] 键崎正己,高合刚,田原博志.沥青基碳纤维制备方法:JPS6170017A[P].1986-04-10.
[29] 键崎正己,高合刚.沥青基碳纤维制备方法:JPH06102852B2[P].1994-12-14.
[30] 小峰喜久治,宫崎诚,崛真治郎碳纤维及石墨纤维制造方法:JPH0359116A[P].1991-03-14.
[31] 彭密雪,孙祝林,吕永根.集束液对中间相沥青纤维的集束性和抗并丝性的影响[J].合成纤维工业,2020,43(4):1-6.
[32] 松本泰次,花谷诚二,吉田稔,等.沥青基碳纤维制造方法:JPS63182416A[P].1988-07-27.
[33] 小峰喜久治,加藤寿夫,御前博之,等.碳纤维及石墨纤维的制造方法:JPH0637726B2[P].1994-05-18.
[34] 小峰喜久治,日野隆,黑田博之.碳纤维及石墨纤维制造方法:JPH01111019A[P].1989-04-27.
[35] 小峰喜久治,伊庭良知,间濑清年.丝束数小于1000的沥青基碳纤维及其制造方法:JPH01229820A[P].1989-09-13.
[36] 进藤昭男.沥青基碳纤维制备方法:JPH0319921A[P].1991-01-29.
[37] 陈龙,刘辉,迟伟东,等.苯基硅油集束剂对中间相沥青纤维不熔化过程影响[J].碳素技术,2010,29(4):36-40.
[38] 胡洁,臧红霞,王波.煤沥青基纤维的制备与性能[J].实验室研究与探索,2020,39(7):45-47.
[39] 贺福.硅油剂及其硅污染[J].高科技纤维与应用,2010,35(6):11-17.
[40] Shiromoto K,Adachi Y,Naba K.Process for producing carbon fiber:US4944932A[P].1990-07-31.
[41] Masaki T,Komatsubara T,Tanaka Y,et al.Finish for carbon fiber precursors:US5783305A[P].1988-07-21.
[42] 小松原知夫,中西诚司,中川干生.碳纤维用前体油剂组合物:JPH08260254A[P].1996-10-08.
[43] 小松原知夫,中西诚司,中川干生.碳纤维用前体油剂组合物:JP3481342B2[P].2003-10-10.
[44] 田中文彦,山崎胜美.碳纤维前驱体用油剂:JP2005264361A[P].2005-09-29.
[45] 于波,徐勤梅.上油方式对碳纤维原丝质量及生产成本的影响[J].合成纤维工业,2014,37(4):64-66.
[46] 白峰.沥青纤维上油率测试溶剂的选择[J].广东化工,2015,42(24):67-68.
[47] 刘金水,叶崇,黄东.等.一种中间相沥青纤维上油的方法:CN110284218A[P].2019-09-27.
[48] 黑田博之,小峰喜久治,内藤勉.碳纤维及石墨纤维的制造方法:JPS62289616A[P].1987-12-16.
[49] 刘中越明,山田铁男,関口博之.沥青基碳纤维制备方法:JPS62299518A[P].1987-12-26.
[50] 青木宏幸,田村孝三郎,西井勇人,等.异形无机纤维及其制造方法:JPH0291222A[P].1990-03-30.
[51] 刘金水,黄东,叶崇,等.一种中间相沥青纤维快速预氧化的方法:CN110230126A[P].2019-09-13.
[52] 刘金水,黄东,叶崇,等.一种中间相沥青纤维快速预氧化的方法:CN110273198A[P].2019-09-24.
[53] 庞守德,高强,查凌驰.一种中间相沥青纤维的预氧化方法:CN111020748A[P].2020-04-17.
PDF