采用溶剂热法合成制备含Co、Mn双金属节点的MOF-74材料,研究了室温下对NO的吸附性能,并通过IAST和穿透实验研究了材料的吸附选择性。结果表明,双金属Mn0.2Co0.8-MOF-74具有典型的MOF-74晶体结构,对NO的吸附量达到160.3cc/g,比单金属Mn-MOF-74提高了约19.4%。在低吸附分压时,NO/CO2的理想溶液吸附(IAST)理论吸附选择性最大可达到397,经过5次循环吸附-脱附实验后的再生性能优良。模拟烟气的双组分穿透实验中,Mn0.2Co0.8-MOF-74对NO/CO2的吸附分离性能达到35.5,可以作为一种优良的NO吸附分离材料。
A MOF-74 material containing Co and Mn bimetallic nodes was synthesized and prepared by solvothermal method.Its NO adsorption property was investigated,and the adsorption selectivity of the material was studied by IAST and breakthrough experiments.The results showed that bimetallic Mn0.2Co0.8-MOF-74 had a typical crystal structure of MOF-74,and the NO adsorption capacity could attain up to 160.3cc·g-1,which was 19.4% higher than that of the single metal Mn-MOF-74.The adsorption selectivity (IAST) calculations for NO/CO2 binary mixture could reach a maximum of 397 at low adsorption partial pressure,and the regeneration performance stability was excellent after 5 cycles of adsorption-desorption experiments.In the simulated flue gas breakthrough experiments,the selectivity of adsorptive separation of Mn0.2Co0.8-MOF-74 for NO/CO2 reached 35.5,which could be used as a prospective material for NO adsorption and separation in flue gas.
[1] Skalska K,Miller J S,Ledakowicz S.Trends in NOx abatement:a review[J].Science of the Total Environment,2010,408(19):3976-3989.
[2] 毛迪,杨爽,殷成阳.用于NH3-SCR脱硝反应的铜基沸石分子筛催化剂研究进展[J].化工新型材料,2022,50(2):234-239.
[3] Chen M Y,Zhao M M,Tang F S,et al.Effect of Ce doping into V2O5-WO3/TiO2 catalysts on the selective catalytic reduction of NOx by NH3[J].Journal of Rare Earths,2017,35(12):1206-1215.
[4] 李晨曦,孟繁伟,叶青.NH3选择性催化还原NOx催化剂及其中毒研究进展[J].化工新型材料,2022,50(2):278-281,286.
[5] Lin R B,Zhang Z J,Chen B L.Achieving high performance metal-organic framework materials through pore engineering[J].Accounts of Chemical Research,2021,54(17):3362-3376.
[6] Lin R B,Xiang S C,Zhou W,et al.Microporous metal-organic framework materials for gas separation[J].Chem,2020,6(2):337-363.
[7] Li B,Wen H M,Yu Y,et al.Nanospace within metal-organic frameworks for gas storage and separation[J].Materials Today Nano,2018,2:21-49.
[8] Li S C,Zhai Y,Wei X X,et al.Catalytic performance of MIL-88B(Ⅴ) and MIL-101(Ⅴ) MOFs for the selective catalytic reduction of NO with NH3[J].ChemCatChem,2021,13(3):940-951.
[9] Lin R B,He Y,Li P,et al.Multifunctional porous hydrogen-bonded organic framework materials[J].Chemical Society Reviews,2019,48(5):1362-1389.
[10] Yu D,Yazaydin A O,Lane J R,et al.A combined experimental and quantum chemical study of CO2 adsorption in the metal-organic framework CPO-27 with different metals[J].Chemical Science,2013,4(9):3544-3556.
[11] Easun T L,Moreau F,Yan Y,et al.Structural and dynamic studies of substrate binding in porous metal-organic frameworks[J].Chemical Society Reviews,2017,46(1):239-274.
[12] Dietzel P D C,Besikiotis V,Blom R.Application of metal-organic frameworks with coordinatively unsaturated metal sites in storage and separation of methane and carbon dioxide[J].Journal of Materials Chemistry,2009,19(39):7362-7370.
[13] Glover T G,Peterson G W,Schindler B J,et al.MOF-74 building unit has a direct impact on toxic gas adsorption[J].Chemical Engineering Science,2011,66(2):163-170.
[14] Rosi N L,Kim J,Eddaoudi M,et al.Rod packings and metal-organic frameworks constructed from rod-shaped secondary building units[J].Journal of the American Chemical Society,2005,127(5):1504-1518.
[15] Wang L J,Deng H X,Furukawa H,et al.Synthesis and characterization of metal-organic framework-74 containing 2,4,6,8,and 10 different metals[J].Inorganic Chemistry,2014,53(12):5881-5883.
[16] Hinks N J,Mckinlay A C,Bo X,et al.Metal organic frameworks as NO delivery materials for biological applications[J].Microporous & Mesoporous Materials,2010,129(3):330-334.
[17] Mckinlay A C,Bo X,Wragg D S,et al.Exceptional behavior over the whole adsorption-storage-delivery cycle for NO in porous metal organic frameworks[J].Journal of the American Chemical Society,2008,130(31):10440-10444.
[18] Botas J A,Calleja G,Sanchez-Sanchez M,et al.Effect of Zn/Co ratio in MOF-74 type materials containing exposed metal sites on their hydrogen adsorption behaviour and on their band gap energy[J].International Journal of Hydrogen Energy,2011,36(17):10834-10844.
[19] Shi Y,Chu Q,Xiong W,et al.A new type bimetallic NiMn-MOF-74 as an efficient low-temperatures catalyst for selective catalytic reduction of NO by CO[J].Chemical Engineering and Processing-Process Intensification,2021,159:108232.
[20] Furukawa H,Cordova K E,O'Keeffe M,et al.The chemistry and applications of metal-organic frameworks[J].Science,2013,341(6149):1230444.
[21] Huang C,Liu R,Yang W,et al.Enhanced catalytic activity of MnCo-MOF-74 for highly selective aerobic oxidation of substituted toluene[J].Inorganic Chemistry Frontiers,2018,5(8):1923-1932.
[22] Zhang Y B,Furukawa H,Ko N,et al.Introduction of functionality,selection of topology,and enhancement of gas adsorption in multivariate metal-organic framework-177[J].Journal of the American Chemical Society,2015,137(7):2641-2650.
[23] Xie S,Qin Q,Liu H,et al.MOF-74-M(M=Mn,Co,Ni,Zn,MnCo,MnNi,and MnZn) for low-temperature NH3-SCR and in situ DRIFTS study reaction mechanism[J].ACS Applied Materials & Interfaces,2020,12(43):48476-48485.
[24] Villajos J A,Orcajo G,Martos C,et al.Co/Ni mixed-metal sited MOF-74 material as hydrogen adsorbent[J].International Journal of Hydrogen Energy,2015,40(15):5346-5352.
[25] Myers A L,Prausnitz J M.Thermodynamics of mixed-gas adsorption[J].AIChE Journal,1965,11(1):121-127.
[26] Huang W,Zhou X,Xia Q,et al.Preparation and adsorption performance of GrO@Cu-BTC for separation of CO2/CH4[J].Industrial & Engineering Chemistry Research,2014,53(27):11176-11184.
[27] Zhang Z J,Xiang S C,Chen B L.Microporous metal-organic frameworks for acetylene storage and separation[J].CrystEngComm,2011,13(20):5983-5992.
[28] Krishna R,van Baten J M.In silico screening of metal-organic frameworks in separation applications[J].Physical Chemistry Chemical Physics,2011,13(22):10593-10616.
基金资助
广西创新驱动发展专项(科技重大专项)(桂科AA18118010)
PDF