聚丙烯酸酯类吸油树脂因具有良好的吸油性、保油性而备受关注,目前研究大多集中在块材或粉末上,对微球状树脂的研究较少。微球因其加工更加方便、吸油倍率更高而备受关注。采用悬浮聚合法,通过调节软硬单体比例,维持反应体系稳定性,制备了分散性好的吸油树脂微球。以甲基丙烯酸十八烷基酯(SMA)、丙烯酸丁酯(BA)和苯乙烯(ST)为单体,二乙烯苯(DVB)为交联剂,偶氮二异丁腈(AIBN)为引发剂,环己烷(CYH)为致孔剂,合成 P(SMA-co-BA-co-ST)高吸油树脂微球。采用红外光谱(FT-IR)、扫描电镜(SEM)、光学显微镜(OM)、热重分析(TG)等手段对树脂微球进行表征。结果表明:所得树脂微球分散性好、粒径均匀,比表面积大。系统分析了各因素对树脂吸油性能的影响,确定最佳反应条件:m[SMA∶BA]=3∶1、ω(ST)=25%、ω(DVB)=0.2%、ω(AIBN)=1.25%、ω(PVA)=1.25%、ω(CYH)=20%,对CCl4、CHCl3、CH2Cl2的饱和吸油倍率分别为33.50g/g、35.48g/g、22.26g/g,高于同类树脂的吸油性能,本研究将为吸油树脂的合成提供新的思路。
Abstract
Polyacrylate oil absorption resin has attracted much attention because of its good oil absorption and preservation.At present,most of the research focuses on block or powder,while less research on microsphere resins.Microspheres attract much attention for their easier processing and higher oil absorption ratio. In this topic, the suspension polymerization method was used to maintain the stability of the reaction system by adjusting the proportion of soft and hard monomers, and to prepare well-dispersed oleoresin microspheres. P(SMA-co-BA-co-ST) high oil-absorbing resin microsphere was synthesized by using octadecyl methacrylate (SMA), butyl acrylate (BA) and styrene (ST) as monomers,divinylbenzene (DVB) as crosslinking agent,2-methylpropionitrile (AIBN) as initiator; and cyclohexane (CYH) as porogenic agent. The resin microsphere was characterized by FT-IR, SEM, OM, and TGA. The results showed the obtained resin microspheres had good dispersity,uniform particle size and larger specific surface area.The effects of various factors on the oil absorption resin performance were systematically analyzed, and the optimal reaction conditions were determined: m[SMA∶BA]=3∶1, ω(ST)=25%, ω(DVB)=0.2%, ω(AIBN)=1.25%, ω(PVA)=1.25%, ω(CYH)=20%. The saturated oil absorption ratios for CCl4,CHCl3 and CH2Cl2 were 33.50g/g, 35.48g/g, 22.26g/g, respectively, which were higher than those of similar resins. This study provided a new idea for the synthesis of oil absorbent resins.
关键词
吸油树脂微球
/
悬浮聚合法
/
苯乙烯
/
吸油倍率
/
丙烯酸酯
Key words
oil-absorption resin microspheres
/
suspension polymerization
/
styrene
/
oil absorption ratio
/
acrylate
新型多组分聚丙烯酸酯类高吸油树脂微球的合成及性能研究[J].
化工新型材料, 2023, 51(9): 198-203 DOI:10.19817/j.cnki.issn1006-3536.2023.09.036
[1] Waluyo,Wahyudi D,Amdani,et al.The impact of oil spill to the total petroleum hydrocarbon(Tph) concentration in fishes at North Coastal of Karawang Regency,West Java Province[J].Journal of Materials Science,2020,2(2):11-18.
[2] Aldosari K R.The applicability of the international and regional efforts to prevent oil pollution:comparative analysis between the Arabian Gulf Region and the North Sea[M].Sustainability in the Maritime Domain,2021:199-221.
[3] Bu X,Chen S,Li D,et al.Flower-like hollow MoS2 microspheres/acrylic resin composites for enhanced oil contaminants removal from water[J].Separation Science and Technology,2019,55(7):1227-1238.
[4] 马梁,王佳惠,韩露,等.高吸油树脂处理放射性废液的研究进展[J].化学推进剂与高分子材料,2021,19(1):29-33.
[5] 裴泽豪,朱姿颖,苟洋,等.丙烯酸酯系吸油树脂的制备与性能研究[J].黑龙江科学,2021,12(10):23-25.
[6] Perera H J,Goyal A,Banu H,et al.Low-cost fluorinated diatomaceous earth polyurethane foam for the absorption of oil[J].MRS Energy & Sustainability,2022,9(1):94-104.
[7] Zhou J,Zhang Y,Jia G,et al.A multifunctional sponge incorporated with TiO2 and graphene oxide as reusable absorbent for oil/water separation and dye absorption[J].New Journal of Chemistry,2021,45(10):4835-4842.
[8] 孟令岽,郑红伟,吴喜娜,等.基于丙烯酸酯类高吸油树脂的复合涂层制备及其性能研究[J].中国涂料,2021,36(6):24-28.
[9] 闫峰,沈一丁,马国艳,等.丙烯酸酯共聚高吸油树脂的合成及性能[J].精细化工,2018,35(12):2137-2141.
[10] Kong L,Ma L,Jin H,et al.Synthesis of a novel oil-absorption resin and optimization of its performance parameters using response surface design[J].Polymers for Advanced Technologies,2019,30(6):1441-1452.
[11] Du Y,Fang P,Chen J,et al.Synthesis of reusable macroporous St/BMA copolymer resin and its absorbency to organic solvent and oil[J].Polymers for Advanced Technologies,2016,27:393-403.
[12] Zhang T,Hu F,Zhang C,et al.A novel multi-wall carbon nanotubes/poly(n-butylacrylate-co-butyl methacrylate) hybrid resin:synthesis and oil/organic solvents absorption[J].Fibers and Polymers,2017,18(10):1865-1873.
[13] Zhou F,Zhang J,Xie P F,et al.Acrylate copolymer-based super oil absorption resins:effects of steric hindrance of the monomer[J].Chemical Papers,2020,74(5):1477-1486.
[14] Alaa A,Psk A,Dgp A,et al.Synthesis and application of porous oil-sorbent microspheres:characterization,retention capacity and sorption kinetics-Science Direct[J].Separation and Purification Technology,2020,234:116095.
[15] 海靖杰,白波,杨丽衡,等.白刺籽粕接枝高吸油树脂NSM-g-P(MMA-co-BA)的制备与性能[J].材料导报,2015,29(20):28-32.
基金资助
武汉工程大学研究生教育创新基金项目(CX2021348)