基于非热耦合能级荧光强度比(NTCL-FIR)技术能够极大地提升测温灵敏度,但是采用多项式拟合基于NTCL-FIR数据时,难以给出准确的拟合公式,对于灵敏度的计算将产生较大的误差。通过简单的高温固相法合成了YVO4∶Yb3+/Tm3+/Er3+上转换材料,对样品的结构和形貌进行表征。荧光光谱表明,所制备的材料呈现蓝光(477nm)、绿光(528nm和552nm)和近红外光(801nm)发射,采用色度坐标和相关色温标定样品的发光颜色,并对其发光机制进行分析。通过程序准确地拟合FIR(I528/I477)数据点,并获得其拟合公式。最后,对比基于NTCL-FIR和热耦合能级荧光强度比(TCL-FIR)的测温灵敏度发现,基于NTCL-FIR的绝对灵敏度(0.0290@320K)和相对灵敏度(1.506@316K)度均优于基于TCL-FIR的绝对灵敏度和相对灵敏度。综上所述,YVO4∶Yb3+/Tm3+/Er3+上转换材料在温度传感领域表现出较大的潜力。
The fluorescence intensity ratio technology based on the non-thermally coupled levels can greatly improve the temperature sensitivity,but the experimental spots are not well defined by polynomial fit,thus the calculation of sensitivity will produce a large error.YVO4∶Yb3+/Tm3+/Er3+ up-conversion material was synthesized by simple solid-state method,then the structure and morphology of the samples were characterized respectively.Fluorescence spectra indicated that it presented blue light (477nm),green light (528nm and 552nm) and near-infrared light (801nm) emission under 980nm excitation.Next,using the chromaticity coordinates and related color temperature calibration measured the light color of samples,and its luminescence mechanism was analyzed.The FIR (I528/I477) fitting formula was accurately obtained by means of a program.Finally,comparing the temperature sensitivity based on NTCL-FIR with TCL-FIR,it was found that the absolute sensitivity and relative sensitivity based on NTCL-FIR were 0.0290@320K and 1.506@316K,respectively,which were better than that of based on TCL-FIR.In summary,Yb3+/Tm3+/Er3+ co-doped YVO4 up-conversion material exhibited great potential for temperature probing.
[1] 洪广言.稀土发光材料:基础与应用[M].北京:科学出版社,2011.
[2] 周红,高文海,张渤琦,等.稀土铕掺杂钒酸钇的荧光温度特性研究[J].长春理工大学学报,2021,44(1):7-13.
[3] 孙大伟,李跃军,曹铁平,等.三维网状Dy3+∶YVO4/TiO2复合纤维的制备及光催化产氢性能[J].高等学校化学学报,2019,40(11):2348-2353.
[4] 张立,朱海永,孙瑛璐,等.端面抽运Nd∶YAP/YVO4被动调Q1.2um拉曼激光[J].红外与毫米波学报,2020,39(6):786-790.
[5] 付姚,史月,王朝阳,等.YVO4∶Yb3+,Er3+纳米粒子颜色可控的高色纯度上转换发光[J].发光学报,2017,38(1):7-12.
[6] 张焕君,董兴邦,彭科,等.LaNbO4∶Tm,Yb荧光材料的上转换发光及温度传感特性研究[J].化工新型材料,2020,48(8):263-266.
[7] 姚东,牟小明,刘金亮.上转换发光纳米材料在发光检测方面的研究进展[J].稀土,2020,41(6):117-125.
[8] Zi Y Z,YangZ W,Xu Z,et al.A novel upconversion luminescence temperature sensing material:negative thermal expansion Y2Mo3O12∶Yb3+,Er3+and positive thermal expansion Y2Ti2O7∶Yb3+,Er3+ mixed phosphor[J].Journal of Alloys and Compounds,2021,880(5):160156.
[9] 彭跃红,任韦舟,邱建备.1550nm激发层状BiOCl∶Er3+上转换发光及温度传感特性[J].无机材料学报,2020,35(8):902-908.
[10] Berthou H,Jörgensen C K.Optical-fiber temperature sensor based on upconversion-excited fluorescence[J].Optics Letters,1990,15(19):1100-1102.
[11] Lu H Y,Hao H Y,Shi G,et al.Optical temperature sensing inβ-NaLuF4∶Yb3+/Er3+/Tm3+ based on thermal,quasi-thermal andnon-thermal coupling levels[J].RSC Advances,2016,6(60):55307-55311.
[12] Zhao Y,Wang X S,Zhang Y,et al.Winning wide-temperature-range and high-sensitive thermometry by a multichannel strategy of dual-lanthanides in the new tungstate phosphors[J].Journal of Alloys and Compounds,2020,834:154998.
[13] Liu X,Lei R S,Huang F F,et al.Dependence of upconversion emission and optical temperature sensing behavior on excitation power in Er3+/Yb3+ co-doped BaMoO4 phosphors[J].Journal of Luminescence,2019(210):119-127.
[14] 郑龙江,李雅新,刘海龙,等,Tm3+,Yb3+共掺钨酸钙多晶材料的上转换发光及荧光温度特性[J].物理学报,2013,62(24):108-113.
[15] Brites C D S,Lima P P,Silva N J O,et al.Thermometry at the nanoscale[J].Nanoscale,2012(2):4799-4829.
[16] Xiang G T,Liu X T,Zhang J H,et al.Dual-mode optical thermometry based on the fluorescence intensity ratio excited by a 915nm wavelength in LuVO4∶Yb3+/Er3+@SiO2 nanoparticles[J].InorganicChemistry,2019,58(12):8245-8252.
[17] Han Q,Hao H Y,Yang J S,et al.Optical temperature sensing based on thermal,non-thermal coupled levels and tunable luminescent emission colors of Er3+/Tm3+/Yb3+ tri-doped Y7O6F9 phosphor[J].Journal of Alloys and Compounds,2019(786):770-786.
PDF