为了提高氟化聚磷腈橡胶的力学性能,对其配方和硫化条件进行了研究。研究发现,硫化剂和硫化工艺对聚磷腈硫化胶的力学性能有显著影响。一段热压硫化温度为160℃时,用过氧化物和硫磺分别作为硫化剂的聚磷腈硫化胶最大抗拉强度可达7.9MPa和8.7MPa,断裂伸长率分别为155%和221%。而经过149℃二段热空气硫化后,用过氧化物和硫磺分别作为硫化剂的聚磷腈硫化胶最大抗拉强度达到了9.5MPa和10.7MPa,但断裂伸长率有所下降。将一段和二段硫化温度优化为140℃和149℃后,聚磷腈硫化胶的最大抗拉强度和断裂伸长率则可达10.2MPa和271%。
Abstract
To improve the mechanical properties of fluorinated polyphosphazene rubber (FPZ),the vulcanization formula and process were studied.The results shown that the different vulcanization reagents and the vulcanization processes had great influence on the mechanical properties of the FPZ.Among them,the maximum tensile strength of FPZ (160℃) after peroxide and sulfur vulcanization reached 7.9MPa and 8.7MPa,respectively.The elongation at break reached 155% and 221%,respectively.When the secondary vulcanization process under 149℃ was introduced,the corresponding maximum tensile strength was able to reach 9.5MPa and 10.7MPa,respectively.However,the elongation at break of FPZ shown some reduction.After optimizing the first and second vulcanization temperatures to 140℃ and 149℃,the maximum tensile strength and elongation at break reach 10.2MPa and 271%,respectively.
关键词
氟化聚磷腈
/
硫化工艺
/
二段硫化
/
力学性能
Key words
fluorinated polyphosphazene
/
vulcanization process
/
secondary vulcanization
/
mechanical property
氟化聚磷腈硫化胶的制备及力学性能研究[J].
化工新型材料, 2022, 50(8): 198-201 DOI:10.19817/j.cnki.issn1006-3536.2022.08.038
[1] Gleria M,Bertani R,Jaeger R D.Fluorinated polyphosphazenes:a survey[J].Journal of Inorganic & Organometallic Polymers,2004,14(1):1-28.
[2] Gleria M,Jaeger R D.Polyphosphazenes:a review[J].Topics in Current Chemistry,1970,250:165-251.
[3] 葛徐涛,张双琨,苗振威,等.氟代烷氧基聚磷腈弹性体的合成及性能研究[J].固体火箭技术,2017,39(1):95-99.
[4] 杜明欣,苗振威,宫志欣,等.氟化聚磷腈的合成及其力学性能与耐油性研究[J].化工新型材料,2019,47(1):231-238.
[5] Singler R E.Historical overview of the army contributions to phosphazene chemistry[J].Journal of Inorganic & Organometallic Polymers & Materials,2006,16(4):307-309.
[6] Zhang Shuangkun,Ji Qiang,Hongchun,et al.Evaluation of poly(diaryloxyphosphazene) elastomer for heat shielding insulations and morphology of charred layers[J].High Performance Poly-mers,2016,29(4):450-457.
[7] Tian Z,Xiao L,Manseri A,et al.Limits to expanding the PN-F series of polyphosphazene elastomers[J].Polymer Engineering & Science,2013,54(8):1827-1832.
[8] 吕百龄.实用橡胶手册[M].北京:化学工业出版社,2010.
[9] 杨清芝.实用橡胶工艺学[M].北京:化学工业出版社,2005.
[10] 刘伟,孙向南,王声媛,等.二段硫化对氟橡胶性能的提高及耐热性的影响[J].特种橡胶制品,2006,27(3):32-35.
[11] 江畹兰.配方和工艺因素对硅橡胶性能的影响[J].世界橡胶工业,2007,34(3):17-18.