以间苯三酚为改性剂,在对前期制备的石蜡/三聚氰胺甲醛(MF)树脂微胶囊复合相变材料进行其壳层的物理及化学结构改性,由于苯环的引入,改善了MF树脂固化后的硬度与脆性,并探究了乳液的Zeta电位、粒径大小及粒径分散性指数(PDI值)对微胶囊储热性能、表面形貌、渗透性能等指标的影响。
Phloroglucinol was employed as the modifier to modify the physical and chemical structure of the shell of the paraffin/melamino-formaldehyde (MF) resin microcapsule composite phase change material(PCM).The results indicated that the introduction of benzene ring improved the hardness and brittleness of cured MF resin.Moreover,the effects of three modification technologies on the indexes such as heat storage performance,surface morphology and permeability of the microcapsules were also investigated.
[1] 何天白,胡汉杰.功能高分子与新材料[M].北京:化学工业出版社,2001.
[2] 刘先之,刘凌志,门永锋.石蜡相变微胶囊的制备与表征[J].应用化学,2012,29(1):9-13.
[3] 崔海亭,杨峰.储热技术及其应用[M].北京:化学工业出版社,2004:207.
[4] 刘菁伟,杨文彬,谢长琼,等.HDPE/EG/石蜡导热定形相变材料的制备及性能[J].材料工程,2015,43(4):42-46.
[5] 余飞,陈中华,曾幸荣.正十二醇相变储热微胶囊的制备与表征[J].高分子材料科学与工程,2009,25(6):135-138.
[6] 叶锋,曲江兰,仲俊喻,等.相变储热材料研究进展[J].过程工程学报,2010,10(6):1231-1241.
[7] 杜晓东,章学来,丁锦宏,等.纳米成核剂对三水醋酸钠蓄热性能的影响[J].建筑节能,2017,45(9):25-28.
[8] 张仁元,柯秀芳.无机盐／陶瓷基复合储能材料的制备和性能[J].材料研究学报,2000,14(6):652-656.
[9] 刘先之,刘凌志,门永锋.石蜡相变微胶囊的制备与表征[J].应用化学,2012,29(1):9-13.
[10] 王鑫,方建华,刘坪,等.改性SiO2杂化层相变微胶囊的制备与表征[J].化工进展,2020,39(4):1431-1439.
[11] 陈爱英,汪学英,曹学增.相变储能材料的研究进展与应用[J].材料导报,2003,17(5):42-44.
[12] 吴淑英,朱冬生,汪南.改善有机储热材料传热性能的研究进展及应用[J].现代化工,2009,29(10):19-23.
[13] 李玉红,焦庆影,夏定国,等.常低温先变储热材料的研究和应用[J].化学教育,2004,25(10):9-13.
[14] 刘树英.国际相变智能调温纤维发展趋势[J].中国纤维,2017(2):126-128.
[15] 陈玲.相变微胶囊的合成及其在导热复合材料中的应用[D].北京:北京化工大学,2011.
[16] 崔海亭,杨峰.储热技术及其应用[M].北京:化学工业出版社,2004:27.
[17] 柯慧珍,逄增媛,宗雪.负载脂肪酸酯的定形相变复合纤维的制备与性能研究[J].功能材料,2014,45(11):11051-11055.
[18] 潘守伟,汪海平.原位聚合制备液体石蜡微胶囊及表征[J].广东化工,2011,38(7):37-38,47.
[19] 王鑫,方建华,刘坪,等.相变材料的研究进展[J].功能材料,2019,50(2):70-75.
[20] 张寅平,胡汉平,孔祥冬.相变贮能——理论和应用[M].合肥:中国科学技术大学出版社,1996.
基金资助
重庆市教育委员会科学技术研究项目(KJQN201912903);重庆市基础科学与前沿技术研究项目(cstc2018jcyAX0306);重庆市自然科学基金面上项目(cstc2019jcyj-msxmX0453)
PDF