通过浸没沉淀相转化法制备聚砜超滤膜。通过多巴胺和牛磺酸对聚砜超滤膜表面进行亲水改性,制备了抗污染聚砜复合超滤膜。采用傅里叶红外光谱对复合膜的组成进行了分析,通过接触角测试了改性前后复合膜的亲水性能,通过扫描电子显微镜研究了复合膜的形态结构,通过对牛血清白蛋白的抗污染测试研究了复合改性膜的抗污染性能。结果表明:改性聚砜复合膜的性能得到显著改善,水通量由195.5L/(m2·h)增大到316.4L/(m2·h),截留率较未改性时有所增强。同时亲水性能和抗污染性能得到了极大的提高,通量恢复率由43.1%增大到65%。
The polysulfone ultrafiltration membrane was prepared by the immersion precipitation phase inversion method.The surface of the membrane was hydrophilically modified by dopamine and taurine to prepare an anti-fouling polysulfone composite ultrafiltration membrane.The hydrophilic properties of the modified membrane were determined by contact angle.The composition of the membrane was analyzed by fourier transform infrared spectroscopy.The morphology of the membrane was studied by scanning electron microscope.The antipollution performance of the composite modified membrane was studied by the anti-pollution test of bovine serum albumin.The results showed that the performance of modified polysulfone composite membrane was effectively improved.The water flux increased from 195.5L/(m2·h) to 316.4L/(m2·h),and the retention rate was higher than that of the unmodified ultrafiltration membrane.At the same time,the hydrophilic and anti-pollution performance were greatly improved.The flux recovery rate increased from 43.1% to 65%.
[1] 吴国成.膜分离技术在水处理环境工程中的有效利用[J].中小企业管理与科技,2019(8):165-166.
[2] 陈长松,赵国华.膜分离技术在水处理方面的应用[J].胶体与聚合物,2018,36(4):186-189.
[3] 刘纳,康彩霞,李双凌,等.膜分离技术在工业含盐废水处理中的应用[J].节能环保,2018(11):10-11.
[4] Wang H,Zhang D.Research progress in control method of water treatment membrane fouling[C].Xi'an,China:International Conference on Civil,Transportation and Environment.2016.
[5] 王华,刘艳飞,彭东明,等.膜分离技术的研究进展及应用展望[J].应用化工,2013,42(3):532-534.
[6] Yi Z,Zhu L,Zhao Y,et al.An extending of candidate for the hydrophilic modification of polysulfone membranes from the compatibility consideration:the polyethersulfone-based amphiphilic copolymer as an example[J].Journal of Membrane Science,2012,15:48-52.
[7] 梁博,黄小华,孙树东,等.聚砜类膜和膜材的改性[J].现代塑料加工应用,2005,17(3):62-64.
[8] 潘巧明,王琪,俞三传.聚砜中空纤维膜改性及其应用研究[J].水处理技术,2006,32(2):49-50.
[9] Meyer J,Ulbricht M.Poly(ethlene oxide)-block-poly(methyl methacrylate) diblock copolymers as functional additive for poly(vinylidene fluoride) ultrafiltration membranes with tailored separation performance[J].Journal of Membrane Science,2018,545:301-311.
[10] Xu Z Z,Liao J Y,Tang H,et al.Antifouling polysulfone ultrafiltration membranes with pendent sulfonamide groups[J].Journal of Membrane Science,2017,548:481-489.
[11] Zarghamia Soheil,Mohammadia Toraj,Sadrzadehb Mohtada.Preparation,characterization and fouling analysis of in-air hydrophilic/underwater oleophobic bio-inspired polydopamine coated PES membranes for oily wastewater treatment[J].Journal of Membrane Science,2019,582:402-413.
[12] 付晓燕.污水处理膜技术-抗污染聚砜超滤膜研究[J].环境保护与循环经济,2020,40(7):23-25.
[13] Kasemset S,Wang L,He Z W,et al.Influence of polydopamine deposition conditions on hydraulic permeability,sieving coefficients,pore size and pore size distribution for a polysulfone ultrafiltration membrane[J].Journal of Membrane Science,2017,522:100-115.
[14] Wu H Q,Liu Y J,Huang J,et al.Preparation and characterization of antifouling and antibacterial polysulfone ultrafiltration membranes incorporated with a silver-polydopamine nanohybrid[J].Journal of Applied Polymer Science,2018,135(27):46430.
[15] Diraki A,Mackey H,McKay G,et al.Removal of oil from oil-water emulsions using thermally reduced graphene and graphene nanoplatelets[J].Chemical Engineering Journal,2018,137:47-59.
[16] 王雪,徐佳,蒋钰烨,等.新型抑菌聚砜超滤膜的制备及性能[J].高等学校化学学报,2012,33(9):2129-2134.
[17] Liu S S,Fang F,Wu J J,et al.The anti-biofouling properties of thin-film composite nanofiltration membranes grafted with biogenic silver nanoparticles[J].Desalination,2016,375:121-128.
[18] 徐又一,蒋金泓,朱利平,等.多巴胺的自聚-附着行为与膜表面功能化[J].膜科学与技术,2011,31(3):32-37.
[19] 贾慧莹,蒋志青,马建伟,等.多巴胺氧化自聚改性聚四氟乙烯纤维制备及其性能[J].2019,40(1):14-18.
[20] Mu Y F,Zhu K,Luan L S,et al.Fabrication of hybrid ultrafiltration membranes with improved water separation properties by incorporating environmentally friendly taurine modified hydroxyapatite nanotubes[J].Journal of Membrane Science,2019,577:274-284.
PDF