聚酰亚胺纤维是一种新型的特种纤维,具有高强度、高模量、阻燃、耐辐射、耐化学腐蚀等优异性能,聚酰亚胺中空纤维膜因具有大比表面积和高装填密度,在气体分离及醇类脱水等方面得到广泛应用。综述了聚酰亚胺中空纤维的制备方法及应用研究进展。聚酰亚胺中空纤维由聚酰亚胺溶液作为纺丝液或聚酰胺酸溶液作为纺丝液制备而成,通常采用物理或化学改性的方法提高聚酰亚胺中空纤维膜的性能。
Polyimide(PI) fiber is a new kind of special fiber with high strength,high modulus,flame retardant,radiation resistance,chemical corrosion resistance and other excellent properties.PI hollow fiber is widely used in gas separation and alcohol dehydration due to its high specific surface area and loading density.The progress of preparation and application of PI hollow fiber was reviewed.PI hollow fibers were made from PI solution or polyamide acid solution as spinning solution.Physical or chemical modification was usually used to improve the properties of PI hollow fiber membrane.
[1] 徐胜.聚酰亚胺膜的化学改性及其渗透汽化脱水研究[D].武汉:华中科技大学,2019.
[2] 李伯龙.聚酰亚胺中空纤维气体分离膜的制备研究[D].北京:北京化工大学,2019.
[3] 李远.耐溶剂聚酰亚胺纳滤膜的制备研究[D].北京:北京化工大学,2019.
[4] 丁晓莉,曹义鸣,王丽娜,等.聚酰亚胺6FDA-mPDA及其非对称中空纤维膜的气体渗透性能[J].高等学校化学学报,2009,30(6):1240-1244.
[5] 丁孟贤,洪维,王绪强.气体膜分离材料聚酰亚胺:中国,1041373[P].1990-04-18.
[6] 董美美,钟永蕙,曹雪梅,等.脱硫用特种分离膜材料研究——面向油品脱硫的渗透汽化膜和吸附功能膜材料构建[C]//2015年中国化工学会年会论文集.北京:中国化工学会,2015:7.
[7] Xu Liren,Zhang Chen,Rungta Meha,et al.Formation of defect-free 6FDA-DAM asymmetric hollow fiber membranes for gas separations[J].Journal of Membrane Science,2014,459:223-232.
[8] 郑哲豪,韩尚勳,李永茂,等.中空纤维、用于形成中空纤维的掺杂溶液组合物和使用所述掺杂溶液组合物制备中空纤维的方法:中国,102099512A[P].2011-06-15.
[9] 安格兰克M,鲍姆加藤G.由聚合溶液制成的聚酰亚胺膜:中国,102470329A[P].2012-05-23.
[10] 久森弘树,林达也,盛桥诚司,等.非对称中空纤维气体分离膜:中国,102905779A[P].2013-01-30.
[11] 刘春青,德兰H Q.用于天然气升级和氢气提纯的高选择性聚酰亚胺膜:中国,107427761A[P].2017-12-01.
[12] 李悦生,丁孟贤,张劲,等.聚酰亚胺膜的分子结构与透气性能之间关系的研究[J].科学通报,1993(24):2255-2257.
[13] 刘春青,敏科夫R,法希姆S A,等.用于空气分离的高渗透性聚酰亚胺膜:中国,102892485A[P].2013-01-23.
[14] 翁格兰克M,勒格尔H.具有改进性能的由嵌段共聚酰亚胺组成的高选择性聚酰亚胺膜:中国,106029742B[P].2019-04-05.
[15] 王丽娜,刘健辉,李萌,等.一种共聚聚酰亚胺中空纤维气体分离膜的制备方法:中国,103846022A[P].2014-06-11.
[16] Xie Xingming,Duan Cuijia,Wang Lina,et al.Fabrication of an asymmetric 4,4'-oxydiphthalicanhydride-2,4,6-trimethyl-1,3-phenylenediamine/2,6-diaminoto-luene copolyimide hollow fiber membrane and its performance for CO2 separation[J].Industrial & Engineering Chemistry Research,2014,53(11):4442-4452.
[17] Le Ngoc Lieu,Chung Tai-Shung.High-performance sulfonated polyimide/polyimide/polyhedral oligosilsesquioxane hybrid membranes for ethanol dehydration applications[J].Journal of Membrane Science,2014,454:62-73.
[18] Favvas Evangelos P,Papageorgiou Sergios K,Nolan John W,et al.Effect of air gap on gas permeance/selectivity performance of BTDA-TDI/MDI copolyimide hollow fiber membranes[J].Journal of Applied Polymer Science,2013,130(6):4490-4499.
[19] 胡军,任慧卿,刘洪来,等.多孔颗粒掺杂的聚酰亚胺中空纤维膜、其制备方法及应用:中国,102418168A[P].2012-04-18.
[20] 林立刚,张龙辉,董美美,等.一种硫化物吸附用聚酰亚胺中空纤维膜的制造方法:中国,104174307A[P].2014-12-03.
[21] 宣剑国,许振良,殷静,等.聚酰亚胺中空纤维膜的热亚胺化及碳化的研究[C]//上海市化学化工学会2005年度学术年会论文摘要集.上海:上海市化学化工学会,2005:2.
[22] 武德珍,田国峰,李建华,等.一种聚酰亚胺中空纤维及其制备方法和应用:中国,107778484B[P].2019-08-13.
[23] 武德珍,肖美凤,李建华,等.含氟聚酰亚胺中空纤维膜及其制备方法:中国,108745006B[P].2020-08-07.
[24] 彭响方,伍雨辰,况太荣.一种聚酰亚胺中空纤维制备方法:中国,109972227A[P].2019-07-05.
[25] 甘从军,江雪微,董杰,等.含砜基聚酰亚胺的合成及其中空纤维膜的制备[J].合成纤维工业,2017,40(1):50-53.
[26] Bakeri Gh,Ismail A F,Matsuura T,et al.Effect of PVDF blending on the structure and performance of PEI hollow fiber membrane in CO2 separation process[J].Chemical Engineering Research and Design,2015,104:367-375.
[27] Zhang Yuan,Wang Rong.Novel method for incorporating hydrophobic silica nanoparticles on polyetherimide hollow fiber membranes for CO2 absorption in a gas-liquid membrane contactor[J].Journal of Membrane Science,2014,452:379-389.
[28] Zhang Yuan,Wang Rong,Zhang Lizhi,et al.Novel single-step hydrophobic modification of polymeric hollow fiber membranes containing imide groups:its potential for membrane contactor application[J].Separation and Purification Technology,2012,101:76-84.
[29] Bakeri Gh,Ismail A F,Rana D,et al.Development of high performance surface modified polyetherimide hollow fiber membrane for gas-liquid contacting processes[J].Chemical Engineering Journal (Amsterdam,Netherlands),2012,198-199:327-337.
[30] Sun Shipeng,Wang Kaiyu,Peng Na,et al.Novel polyamide-imide/cellulose acetate dual-layer hollow fiber membranes for nanofiltration[J].Journal of Membrane Science,2010,363(1/2):232-242.
[31] Park Bo-Ryoung,Kim Dae-Hoon,Jo Hang-Dae,et al.H2S removal and CO2/CH4 separation of ternary mixture using polyimide hollow fiber membrane[J].Hwahak Konghak,2011,49(2):250-255.
[32] 任吉中,盛鲁杰,花开胜,等.一种高性能聚酰亚胺中空纤维膜及其制备方法与应用:中国,110404423A[P].2019-11-05.
[33] 徐立仁,沃恩J T,仇武林,等.制造改良聚酰亚胺分离膜的方法:中国,109963641A[P].2019-07-02.
[34] 冯博,徐凯,肖学山,等.氧化石墨烯聚酰亚胺中空纤维膜的合成及海水淡化性能研究[J].水处理技术,2017,43(10):16-19.
[35] 李国民,冯春生,李俊凤,等.共混改性聚酰亚胺中空纤维膜的压缩空气除湿性能研究[J].功能高分子学报,2005(2):194-197.
[36] 蒋春艳.聚合物/钌纳米簇杂化中空纤维膜的制备及性能研究[D].武汉:中南民族大学,2014.
[37] 中西俊介,吉永利宗,伊藤健次,等.气体分离膜及其用法:中国,1317362[P].2001-10-16.
[38] Zhang Yuan,Wang Rong.Fabrication of novel polyetherimide fluorinated silica organic-inorganic composite hollow fiber membranes intended for membrane contactor application[J].Journal of Membrane Science,2013,443:170-180.
[39] Lim Siow Kee,Setiawan Laurentia,Bae Tae-Hyun,et al.Polyamide-imide hollow fiber membranes crosslinked with amine-appended inorganic networks for application in solvent-resistant nanofiltration under low operating pressure[J].Journal of Membrane Science,2016,501:152-160.
[40] Setiawan Laurentia,Shi Lei,Wang Rong.Dual layer composite nanofiltration hollow fiber membranes for low-pressure water softening[J].Polymer,2014,55(6):1367-1374.
[41] Sun Shipeng,Hatton T A,Chung Tai-Shung.Hyperbranched polyethyleneimine induced cross-linking of polyamide-imide nanofiltration hollow fiber membranes for effective removal of ciprofloxacin[J].Environmental Science & Technology,2011,45(9):4003-4009.
[42] Li Yi,Chung Tai-Shung.Exploratory development of dual-layer carbon-zeolite nanocomposite hollow fiber membranes with high performance for oxygen enrichment and natural gas separation[J].Microporous and Mesoporous Materials,2008,113(1/2/3):315-324.
[43] Ma Canghai,Koros William J.High-performance ester-crosslinked hollow fiber membranes for natural gas separations[J].Journal of Membrane Science,2013,428:251-259.
[44] Shi Guimin,Wang Yan,Chung Tai-Shung.Dual-layer PBI/P84 hollow fibers for pervaporation dehydration of acetone[J].AIChE Journal,2012,58(4):1133-1145.
[45] Zhou Lubo,Liu Chunqing,Cabrera Carlos A,et al.Staged membrane system for gas,vapor,and liquid separations:US,20100288701A1[P].2010-11-18.
[46] 徐立仁,夏玛R,哈里斯W J,等.改进的制备碳分子筛中空纤维膜的方法:中国,109937084A[P].2019-06-25.
[47] 董香灵,于海军,张靖昱,等.交联法制备聚酰亚胺中空纤维纳滤膜[J].膜科学与技术,2018,38(6):69-75.
[48] 徐立仁.碳分子筛(CMS)中空纤维膜和其始于预氧化聚酰亚胺的制备:中国,106794430B[P].2020-11-06.
[49] Setiawan Laurentia,Wang Rong,Shi Lei,et al.Novel dual-layer hollow fiber membranes applied for forward osmosis process[J].Journal of Membrane Science,2012,421-422:238-246.
[50] Setiawan,Laurentia,Wang Rong,Li Kang,et al.Fabrication of novel poly(amide-imide) forward osmosis hollow fiber membranes with a positively charged nanofiltration-like selective layer[J].Journal of Membrane Science,2011,369(1/2):196-205.
[51] 刘暘,李伯龙,王连才,等.一种改性聚酰亚胺中空纤维气体分离膜及改性方法与应用:中国,106390780A[P].2017-02-15.
[52] Chenar M P,Soltanieh M,Matsuura T,et al.Application of cardo-type polyimide (PI) and polyphenylene oxide (PPO) hollow fiber membranes in two-stage membrane systems for CO2/CH4 separation[J].Journal of Membrane Science,2008,324(1/2):85-94.
[53] 赵子淇,张忠孝,江砚池,等.聚酰亚胺中空纤维膜分离CO2/N2的影响因素分析[J].能源工程,2020(2):61-65.
[54] 张琳,胡斌,王霞,等.PI中空纤维膜分离模拟燃煤脱硫烟气中的CO2[J].中国电机工程学报,2017,37(9):2637-2644.
[55] 孙亚伟.中空纤维膜分离与低温耦合的CO2捕集及特性研究[D].天津:天津大学,2017.
[56] 张琳.基于燃煤湿法脱硫净烟气环境的膜法捕集CO2及其失效特性研究[D].南京:东南大学,2017.
[57] 武鲁航.燃煤电厂烟气CO2膜分离工艺模拟研究[D].青岛:青岛科技大学,2017.
[58] 李鹤,杨博,张春威,等.聚酰亚胺中空纤维膜分离二氧化碳实验研究[J].现代化工,2018,38(10):188-191.
[59] 张春威,杨博,李鹤,等.聚酰亚胺中空纤维膜对油田伴生气中二氧化碳分离性能的研究[J].膜科学与技术,2018,38(4):93-98;106.
[60] 葛昕,李晖,李布青,等.聚酰亚胺中空纤维膜分离CH4/CO2的影响因素分析[J].中国沼气,2017,35(1):13-16.
[61] 梁素钰,王述洋,李二平,等.沼气制取车用天然气级燃料系统[J].农业工程学报,2009,25(6):210-213.
[62] 尼姝丽,王述洋,梁素钰.餐厨垃圾制沼及沼气纯化系统[J].中国沼气,2012,30(4):21-24.
[63] 曹义鸣,王志.抗CO2塑化功能高分子膜材料设计及分离过程研究[Z].大连:中国科学院大连化学物理研究所,2013.
[64] 史惠杰,徐泓,浦鹏,等.膜分离提纯沼气中试试验[J].中国沼气,2015,33(1):36-40.
[65] 中国科学院长春应用化学研究所.压缩空气的膜法脱湿技术[Z].长春:中国科学院长春应用化学研究所,2000.
[66] 中国科学院长春应用化学研究所.用于压缩空气脱湿的聚酰亚胺中空纤维膜组件[Z].2004.
[67] 吴庸烈,刘静芝,李国民,等.压缩空气脱湿用聚酰亚胺中空纤维膜组件中试[Z].2003.
[68] 周迈.第二代高效膜分离提氢装置的应用[J].小氮肥,2006,34(2):2.
[69] 江皓,张松林,浦鹏,等.中空纤维膜技术提纯页岩气生产天然气[C]//第二届中国石油石化节能减排技术交流大会论文集.2015:612-617.
[70] 周国庆.聚酰亚胺中空纤维膜对氙的富集和杂质气体去除性能研究[D].兰州:兰州大学,2016.
[71] 姜尚,孙承贵,贾静璇,等.中空纤维致密膜基吸收法在CO2脱除中的应用[J].高校化学工程学报,2013,27(2):304-308.
[72] 孙承贵.中空纤维致密膜基吸收脱除CO2研究[D].大连:中国科学院研究生院(大连化学物理研究所),2005.
[73] 奥布赖恩W G,内尔基C J,哈克R C.用半透膜从碳氟化合物中分离出二氧化碳:中国,1254329[P].2000-05-24.
[74] 李均方,黄晶,詹平,等.聚酰亚胺中空纤维膜分离He/CH4的试验研究[J].石油与天然气化工,2018,47(5):26-30.
[75] 马切拉斯J T,比克森B,纳尔逊J K.由聚醚酰亚胺和聚酰亚胺聚合物的共混料制膜的方法:中国,1112145[P].1995-11-22.
[76] 马切拉斯J T.由聚酰亚胺聚合物的共混物制备的流体分离膜:中国,1139021[P].1997-01-01.
[77] 中国科学院长春应用化学研究所.聚酰亚胺中空纤维膜用于乙醇气相脱水[Z].长春:中国科学院长春应用化学研究所,2004.
[78] 张可达.芳香聚酰亚胺气体分离膜[J].功能高分子学报,1990(3):231-240.
[79] 李悦生,丁孟贤,徐纪平.聚酰亚胺气体分离膜的进展[J].高分子通报,1991(3):138-146.
[80] 李悦生,丁孟贤,张劲,等.聚酰亚胺膜的分子结构与透气性能之间关系的研究[J].科学通报,1993(24):2255-2257.
[81] 李懋英,李光文.用于生产氮气的聚酰亚胺膜[J].低温与特气,1993(1):28.
[82] 张应焞,韩美.膜式氮发生装置[J].低温与特气,1993(4):73.
基金资助
煤基材料与化学品的行业产业分析与专利预警(H16-02)
PDF