分别采用氧化镁(MgO)、氧化钙(CaO)、氧化锌(ZnO)与丙烯酸(AA)原位生成丙烯酸盐改性氢化丁腈橡胶(HNBR),研究不同金属氧化物对原位生成技术改性HNBR的影响。采用傅里叶红外光谱分析3种原位生成不同丙烯酸盐改性HNBR的结构;采用扫描电子显微镜观测丙烯酸盐在HNBR中的分布;并采用平衡溶胀法表征了未改性HNBR与3种改性HNBR的总交联密度、共价交联密度与离子交联密度,并对比其力学性能。结果表明:原位生成丙烯酸盐在HNBR中产生的离子键与过氧化物引发的共价键协同作用,形成“离子型共价键合”使HNBR性能得到很大程度的提升;不同金属氧化物与HNBR相容性的差别影响了丙烯酸盐在基体中的含量与分散,导致离子交联密度不同,继而影响复合材料的力学性能;原位生成的3种丙烯酸盐中,丙烯酸锌(ZnDA)对HNBR的改性效果最好,在基体中分散均匀,相容性好,离子交联密度与总交联密度最高,力学性能最好;丙烯酸镁(MgDA)次之;丙烯酸钙(CaDA)最差。
Abstract
Hydrogenated nitrile-butadiene rubber(HNBR) was modified by in-situ formation of acrylate with magnesium oxide(MgO),calcium oxide(CaO),zinc oxide(ZnO) and acrylic acid (AA).The effect of different metal oxides on HNBR modified by in-situ synthesis was studied.Fourier transform infrared spectroscopy (FT-IR) was used to analyze the structure of HNBR modified by three kinds of in-situ synthesized acrylates.The distribution of acrylate in HNBR was observed by scanning electron microscope(SEM).The total crosslinking density,covalent crosslinking density and ionic crosslinking density of pure HNBR and three kinds of modified HNBR were characterized by the method of equilibrium swelling,and compared their mechanical properties.The results shown that the ionic bond formed by in-situ acrylate in HNBR and the covalent bond initiated by peroxide cooperate to form “ionic covalent bonding” which greatly improved the performance of HNBR.The difference of compatibility between different metal oxides and HNBR affected the content and dispersion of acrylate in the matrix,resulting in different ionic crosslinking density,which further affected the mechanical properties of the composite.Among the three kinds of in-situ synthesized acrylates,ZnDA had the best modification effect on HNBR,with uniform dispersion in the matrix and good compatibility.The ionic crosslinking density and total crosslinking density were the highest,and the mechanical properties were the best.MgDA was the second,and CaDA was the worst.
关键词
金属氧化物
/
原位生成
/
丙烯酸盐
/
氢化丁腈橡胶
/
交联密度
/
离子型共价键合
/
力学性能
Key words
metal oxide
/
in-situ formation
/
acrylate
/
HNBR
/
crosslinking density
/
ionic covalent bonding
/
mechanical property
不同金属氧化物在原位生成技术改性HNBR中的作用研究[J].
化工新型材料, 2022, 50(1): 183-186 DOI:10.19817/j.cnki.issn1006-3536.2022.01.037
[1] Zhang J,Zhang H,Pang J.Improved understanding on the reinforcement of low-temperature hydrogenated nitrile butadiene rubber composites by in situ polymerization of unsaturated metal methacrylate:influences of salt cation[J].RSC Advances,2016,6:104416-104424.
[2] 颜晋钧.氢化丁腈橡胶的应用及现状[J].橡胶科技市场,2008(10):11-13.
[3] 詹正云,辛丽红,任文坛.Zhanber@HNBR在高温-长时间条件下的耐老化和耐油试验研究[J].世界橡胶工业,2017,44(11):12-16.
[4] 杜斌,闫功臣,李伟东,等.氢化丁腈橡胶在油田介质中的性能变化研究[J].橡胶科技,2018,16(10):16-19.
[5] 王玉瑛.氢化丁腈橡胶生产技术及市场发展[J].化工新型材料,2005,33(2):5-7.
[6] 陈秀霞,李涛,王文艳,等.HNBR补强填充体系的研究[J].弹性体,2013,23(2):30-35.
[7] 陈明林.纳米白炭黑复合材料的制备及其填充HNBR的性能研究[D].北京:北京化工大学,2019.
[8] 赵艳芬,苏正涛,王珊,等.碳纳米管增强HNBR橡胶及其对橡胶性能的影响[J].弹性体,2020,30(3):41-45.
[9] 王小蕾,张振山,王春芙,等.石墨烯/氢化丁腈橡胶纳米复合材料的制备及性能[J].合成橡胶工业,2019,42(5):398-402.
[10] 王滕滕,钟国伦,周丽玲.氢化丁腈橡胶共混改性技术研究进展[J].化工新型材料,2012,40(7):15-17.
[11] 林桂.纳米粉体在橡胶基质中的聚集和分散研究[D].北京:北京化工大学,2004.
[12] Wen S,Zhou Y,Yao L.In situ self-polymerization of unsaturated metal methacrylate and its dispersion mechanism in rubber-based composites[J].Thermochimica Acta,2013,571:15-20.
[13] Wei Z,Lu Y,Meng Y.Improved understanding of in-situ polymerization of zinc dimethacrylate:the solid bulk polymerization[J].Polymer,2012,53(6):1409-1417.
[14] 任文坛.原位合成丙烯酸盐制备吸水膨胀橡胶及其性能的研究[D].上海:上海交通大学,2004.