水凝胶材料与生物组织相似,已被广泛应用于生物医药、组织工程等医学领域。以壳聚糖(CS)和透明质酸钠(SH)为主要原料,利用1-乙基-(3-二甲基氨基丙基)碳二亚胺盐酸盐/N-羟基琥珀酰亚胺(EDC/NHS)活化透明质酸钠来与壳聚糖偶联制备出了化学交联的CS/SH偶联水凝胶。测试并分析偶联水凝胶微观形貌,红外光谱,细胞增殖,溶胀比,力学性能和降解速率。结果表明:制备的偶联水凝胶材料在皮肤、创伤修复、软骨、药物载体等领域具有很大前景。
Hydrogel materials are similar to biological tissues and have been widely used in biomedical,tissue engineering and other medical fields.Chitosan(CS) and sodium hyaluronate(SH) were used as the main raw materials,and hyaluronic acid was activated by EDC/NHS.Sodium was coupled with chitosan to prepare a chemically crosslinked CS/SH coupled hydrogel.And its microstructure,infrared spectrum,cell proliferation,swelling ratio,mechanical properties and degradation rate were tested and analyzed.The experimental results shown that the CS and SH had great potential in the preparation of non-toxic crosslinked hydrogel materials.
[1] 孙健翔,谭佩欣,冯小丽,等.高韧性ALG-Ca/PAM双网络水凝胶的制备与表征[J].四川大学学报(自然科学版),2015,52(3):645-650.
[2] Xu Y,Xie J,Gao H,et al.Interpenetration enhancing of chitosan-PEGLM double network(DN) hydrogel and its properties[J].Macromolecular Research,2015,23(1):2-12.
[3] Ullah F,Othman M B H,Javed F,et al.Classification,processing and application of hydrogels:a review[J].Mater Sci Eng C Mater Biol Appl,2015,57:414-433.
[4] Ahmad M,Manzoor K,Ikram S.Versatile nature of hetero-chitosan based derivatives as biodegradable adsorbent for heavy metal ions:a review[J].International Journal of Biological Macromolecules,2017,105(Pt1):190-203.
[5] Guilherme M R,Aouada F A,FajardoAR,et al.Superabsorbent hydrogels based on polysaccharides for application in agriculture as soil conditioner and nutrient carrier:a review[J].European Polymer Journal,2015,72:S0014305715002335.
[6] Alla S G A,Sen M,El-Naggar A W M.Swelling and mechanical properties of superabsorbent hydrogels based on Tara gum/acrylic acid synthesized by gamma radiation[J].Carbohydrate Polymers,2012,89(2):478-485.
[7] Rao S B,Sharma C P.Use of chitosan as a biomaterial:studies on its safety and hemostatic potential[J].Journal of Biomedical Materials Research,1997,34(1):21-28.
[8] Al-Qadi S,Grenha A,Remuñán-López C.Microspheres loaded with polysaccharide nanoparticles for pulmonary delivery:preparation,structure and surface analysis[J].Carbohydrate Polymers,2011,86(1):25-34.
[9] Liu Y,Wu Y,Lin H,et al.Study on an injectable biomedical paste using cross-linked sodium hyaluronate as a carrier of hydroxyapatite particles[J].Carbohydrate Polymers,2018,195:378-386.
[10] Hans M L,Lowman A M.Biodegradable nanoparticles for drug delivery and targeting[J].Current Opinion in Solid State & Materials Science,2002,6(4):319-327.
[11] Thomson R C,Wake M C,Yaszemski M J,et al.Biodegradable polymer scaffolds to regenerate organs[J].Adv Polym Sci,1995,122:245-274.
[12] Ahmed E M.Hydrogel:preparation,characterization,and applications:a review[J].Journal of Advanced Research,2015,6(2):105-121.
[13] Hennink W E,Van Nostrum C F.Novel crosslinking methods to design hydrogels[J].Advanced Drug Delivery Reviews,2012,64(1):223-236.
[14] Angele P,Abke J,Kujat R,et al.Influence of different collagen species on physico-chemical properties of crosslinked collagen matrices[J].Biomaterials,2004,25(14):2831-2841.
[15] Lee C R,Grodzinsky A J,Spector M.The effects of cross-linking of collagen-glycosaminoglycan scaffolds on compressive stiffness,chondrocyte-mediated contraction,proliferation and biosynthesis[J].Biomaterials,2001,22(23):3145-3154.
[16] Pieper J S,Van Der Kraan P M,Hafmans T,et al.Crosslinked type Ⅱ collagen matrices:preparation,characterization,and potential for cartilage engineering[J].Biomaterials,23(15):3183-3192.
[17] Yim E K F,Wan A C A,Visage C L,et al.Proliferation and differentiation of human mesenchymal stem cell encapsulated in polyelectrolyte complexation fibrous scaffold[J].Biomaterials,2006,27(36):6111-6122.
[18] Luca S,Emanuele C V,Paolo S,et al.Potential of electrospun poly(3-hydroxybutyrate)/collagen blends for tissue engineering applications[J].Journal of Healthcare Engineering,2018,2018:1-13.
PDF