摘要
以改性煤矸石为载体,以Ti(SO4)2为钛源,采用水热法制备纳米TiO2/改性煤矸石复合材料,并以其为吸附剂,用于甲基橙模拟印染废水的吸附实验。研究了复合材料中TiO2的质量分数、吸附剂用量、吸附时间、模拟废水浓度和pH对吸附性能的影响。正交试验结果表明,TiO2质量分数为25%,吸附剂用量为3g,模拟废水浓度为 5mg/L,pH为4,在25℃恒温条件下,震荡吸附210min,甲基橙的吸附去除率达到94.83％。吸附过程符合准二级动力学模型和Langmuir吸附等温线,属于单分子层吸附。用X射线衍射(XRD)、傅里叶变换红外光谱(FT-IR)和扫描电镜(SEM)对吸附剂进行表征,结果显示,TiO2以锐钛矿型结构形式被成功负载于改性煤矸石表面,复合材料表面的羟基和钛氧键等官能团提高了对甲基橙的吸附脱色性能。
Abstract
With the modified coal gangue as the carrier,Ti(SO4)2 as the titanium source,nano-TiO2/modified coal gangue composites were prepared by hydrothermal method.The composites were used as the adsorbent,in the adsorption test of printing and dyeing wastewater simulated by methyl orange.The effects of TiO2 content,adsorbent dosage,adsorption time,simulated wastewater concentration and pH on the adsorption properties of the composites were studied.The results of orthogonal test showed that the mass fraction of TiO2 was 25%,the amount of adsorbent was 3 grams,the concentration of simulated wastewater was 5 mg/L,the pH was 4,and under the condition of constant temperature of 25℃ for 210 min,the removal rate of methyl orange reached 94.83%.The adsorption process was in accordance with the quasi-second-order kinetic model and Langmuir adsorption isotherm,which belonged tomonolayer adsorption.The adsorbent was characterized by X-ray diffraction (XRD),Fourier transform infrared spectroscopy (FT-IR) and scanning electron microscopy (SEM).The results showed that TiO2 was successfully loaded on the surface of modified gangue in the form of anatase structure,and the functional groups such as hydroxyl group and TiO2 bonded on the surface of composite material improved the adsorption and decolorization performance of methyl orange.
关键词
二氧化钛
/
煤矸石
/
复合材料
/
甲基橙
Key words
TiO2
/
coal gangue
/
composite
/
methyl orange
纳米TiO2/改性煤矸石复合材料的制备及性能研究[J].
化工新型材料, 2021, 49(4): 142-147 DOI:10.19817/j.cnki.issn1006-3536.2021.04.031
[1] 路绍琰,张亚南,王亮,等.印染废水脱色处理实验研究[J].盐科学与化工,2019,48(10):30.
[2] 雷建红.煤矸石的污染危害与综合利用分析[J].能源与节能,2017,139(4):90-147.
[3] 王婷,牛文静.改性煤矸石吸附染料废水中甲基橙性能的研究[J].皮革与化工,2018,35(6):16-20.
[4] 张晓婉,李巧玲.改性煤矸石/TiO2光催化剂的制备及其光催化性能研究[J].化工新型材料,2019,47(10):171-176.
[5] 谢娟,夏润南,赵树春,等.ZnO/煤矸石复合光催化剂的制备与性能研究[J].矿产综合利用,2019,8(4):126-129.
[6] 周洋凯,罗义,李延博,等.改性膨润土对印染废水中染料的吸附效果研究[J].安徽师范大学学报(自然科学版),2018,41(3):252-255.
[7] 李慧如,何玉凤,李芳蓉,等.黄原酸化膨润土对甲基橙的吸附性能研究[J].化工新型材料,2013,41(1):70-72.
[8] 黄晓丽.粉煤灰改性及其对甲基橙废水的应用研究[D].西安:陕西师范大学,2014.
[9] 李杰.花生壳对水中染料吸附性能的研究[D].郑州:郑州大学,2011.
[10] 吴新华,石慧,阳小宇.壳聚糖/纳米TiO2超声降解甲基橙废水[J].绿色科技色,2015(6):173-175.
[11] 李胜英,郭呈若,李富丽,等.碳量子点/TiO2复合材料的制备及性能研究[J].化工新型材料,2019,47(2):90-93.
[12] Jing L,Zhou W,Tian G,et al.Surface tuning for oxide-based nanomaterials as efficient photocatalysts[J].Chemical Society Reviews,2013,42(24):9509-9549.
[13] Belver C,Breen C,Clegg F,et al.A variable-temperature diffuse reflectance infrared fourier transform spectroscopy study of the binding of water and pyridine to the suface of acid-activated metakaolin[J].Langmuir,2005,(21):2129-2136.
[14] 海英.TiO2/改性煤系高岭土纳米复合材料的制备及其吸附性能研究[D].呼和浩特:内蒙古师范大学,2016.
[15] 邓军,李贝,肖旸,等.基于热重-傅里叶红外光谱联用的煤矸石自燃特性及微观表征[J].西安科技大学学报,2017,37(1):1-6.
[16] 苏洁.煤矸石复合材料制备及其吸附性能的研究[D].包头:内蒙古科技大学,2015.
[17] Saha B,Das S,Saikia J,et al.Preferential and enhanced adsorption of different dyes on iron oxide nanoparticles:a comparative study[J].Journal of Physical Chemistry C,2011,115(16):8024-8033.
[18] 陈玉,郑时旺.改性膨润土对废水中甲基橙的吸附性能研究[J].河南农业科学,2014,43(1):83-86.
[19] 王丹萍.改性煤矸石/TiO2复合材料的制备及其光催化性能的研究[D].太原:中北大学,2015.
[20] Chibowski S,Paszkiewicz M.Studies of some properties and the structure of polyethylene glycol (PEG) macromolecules adsorbed on a TiO2surface[J].Adsorpt Sci Technol,2001,19,397-407.
[21] 李梅静.CdS/Na2Ti3O7、CdS/TiO2纳米线的制备及其性能研究[D].长春:吉林大学,2014.
基金资助
2019年自治区级大学生创新创业训练计划立项项目(201910605092)