摘要
以自制改性纳米TiO2为填料,聚氨酯(PU)作为基体,充分反应后,通过红外光谱和扫描电镜图分析,证实制得改性纳米TiO2/PU复合材料。测试结果表明,当纳米TiO2含量分别为3%、6%和2%时,复合材料的冲击强度、拉伸强度和体积电阻率达到最大值,分别为16.63kJ/m2、45.68MPa和4.8×1016Ω·cm。
Abstract
The modified nano-TiO2/polyurethane(PU) composite was prepared by taking the modified nano-TiO2 as the filler and PU as the matrix.After full reaction,it was confirmed by infrared spectrum and SEM analysis.The results shown that when the content of nano-TiO2 was 3%,6% and 2%,the impact strength,tensile strength and volume resistivity of the composite reached the maximum,which were 16.63kJ/m2,45.68mPa and 4.8×1016Ω·cm,respectively.
关键词
纳米TiO2
/
聚氨酯
/
冲击强度
/
拉伸强度
/
体积电阻率
Key words
nano-TiO2
/
polyurethane
/
impact strength
/
tensile strength
/
volume resistivity
TiO2/PU复合材料的制备及其性能研究[J].
化工新型材料, 2021, 49(4): 116-118 DOI:10.19817/j.cnki.issn1006-3536.2021.04.025
[1] 李定云.紫外(UV)固化涂料挥发性有机化合物(VOC)测量方法探讨[J].化工新型材料,2015,(12):38-42.
[2] Suiemans,Khan S M,Guill N,et al.A comprehensive short review on polyurethane foam[J].Int J Innov Sci Res,2014,12:165-169.
[3] Maganty S,Roma M P,Meschter S J,et al.En-hanced mechanical properties of polyurethane compositecoatings through nanosilica addtion[J].Progr Org Coatings,2016,90:243-251.
[4] Palimi M,Rostami M,Mahdavian M,et al.Surface modification of Fe2O3 nanoparticles with 3-aminopropyltri-methoxysilane (AP TMS):an attempt to investigatesurface treatment on surface chemistry and mechanical properties of polyuretuane/Fe2O3 nanocomposite[J].Appl Surf Sci,2014,320:60-72.
[5] 许凯翔,杨建军.功能型水性聚氨酯建筑涂料的研究现状和最新进展[J].聚氨酯工业,2016,31(2):1-4.
[6] 周虎,李宁,余斌,等.桐酸单甘酯改性水性聚氨酯的制备及其性能[J].聚氨酯工业,2015,30(4):29-32.
[7] 周红军,尹国强,吴婉霜,等.环氧树脂/改性纳米炭黑复合材料固化动力学[J].中国塑料,2011,25(4):33-37.
基金资助
2020年结构化学国家重点实验室基金课题资助(20200027);2019年江苏省住建厅科技项目资助(2019ZD097);江苏省扬州市科技计划-市校合作专项(YZ2018146)