Preparation and property of TiO2/PU composite material

Expand
  • The Department of Chemical Engineering of Yangzhou Polytechnic Institute,Yangzhou 225127

Received date: 2020-01-10

  Revised date: 2021-02-20

  Online published: 2021-05-07

Abstract

The modified nano-TiO2/polyurethane(PU) composite was prepared by taking the modified nano-TiO2 as the filler and PU as the matrix.After full reaction,it was confirmed by infrared spectrum and SEM analysis.The results shown that when the content of nano-TiO2 was 3%,6% and 2%,the impact strength,tensile strength and volume resistivity of the composite reached the maximum,which were 16.63kJ/m2,45.68mPa and 4.8×1016Ω·cm,respectively.

Cite this article

Wang Shengwen . Preparation and property of TiO2/PU composite material[J]. New Chemical Materials, 2021 , 49(4) : 116 -118 . DOI: 10.19817/j.cnki.issn1006-3536.2021.04.025

References

[1] 李定云.紫外(UV)固化涂料挥发性有机化合物(VOC)测量方法探讨[J].化工新型材料,2015,(12):38-42.
[2] Suiemans,Khan S M,Guill N,et al.A comprehensive short review on polyurethane foam[J].Int J Innov Sci Res,2014,12:165-169.
[3] Maganty S,Roma M P,Meschter S J,et al.En-hanced mechanical properties of polyurethane compositecoatings through nanosilica addtion[J].Progr Org Coatings,2016,90:243-251.
[4] Palimi M,Rostami M,Mahdavian M,et al.Surface modification of Fe2O3 nanoparticles with 3-aminopropyltri-methoxysilane (AP TMS):an attempt to investigatesurface treatment on surface chemistry and mechanical properties of polyuretuane/Fe2O3 nanocomposite[J].Appl Surf Sci,2014,320:60-72.
[5] 许凯翔,杨建军.功能型水性聚氨酯建筑涂料的研究现状和最新进展[J].聚氨酯工业,2016,31(2):1-4.
[6] 周虎,李宁,余斌,等.桐酸单甘酯改性水性聚氨酯的制备及其性能[J].聚氨酯工业,2015,30(4):29-32.
[7] 周红军,尹国强,吴婉霜,等.环氧树脂/改性纳米炭黑复合材料固化动力学[J].中国塑料,2011,25(4):33-37.
Options
Outlines

/