Synthesis and characterization of CPTMS functionalized MCM-41-Cl super-hydrophobic material

Expand
  • 1. Northwest Oilfield Branch Company,SINOPEC,Urumqi 830011;
    2. College of Chemistry and Chemical Engineering,Xinjiang University,Urumqi 830046;
    3. Key Laboratory of Enhanced Oil Recovery for Fractured and Cavern Reservoirs,SINOPEC,Urumqi 830011

Received date: 2020-01-06

  Revised date: 2021-01-21

  Online published: 2021-05-07

Abstract

Using MCM-41 as a carrier,the silane coupling agent 3-chloropropyltrimethoxysilane(CPTMS) was grafted onto MCM-41 molecular sieve by post-grafting method to prepare functionalized MCM-41-Cl as a new type of super-hydrophobic material.The structure was determined by FT-IR.Malvern laser particle size analyzer,SEM,and the performance was evaluated by an experiment such as a contact angle measuring instrument.The results showed that CPTMS was successfully grafted onto MCM-41.The contact angle of functionalized MCM-41-Cl with water was 157.9°.It was a molecular sieve-based super-hydrophobic material,and MCM-41-Cl was investigated for different oil products.And the organic solvent reached the oil absorption rate when the oil was saturated.It was found that the oil absorption rate of MCM-41-Cl to toluene was as high as 290.98%,showing a good super-hydrophobic oil absorption performance.

Cite this article

He Long, Zeng Meiting, Luo Qinglong, Yang Biao, Dong Ruiqiang, Huang Xueli . Synthesis and characterization of CPTMS functionalized MCM-41-Cl super-hydrophobic material[J]. New Chemical Materials, 2021 , 49(4) : 80 -83 . DOI: 10.19817/j.cnki.issn1006-3536.2021.04.017

References

[1] 龙英才,许太明,孙尧俊,等.MCM-41分子筛的改性、表面结构与吸附性质的研究[J].化学学报,1999,57(9):1014-1021.
[2] Zhao X S,Lu G Q.Modification of MCM-41 by surface silylation with trimethylchlorosilane and adsorption study[J].The Journal of Physical Chemistry B,1998,102(9):1556-1561.
[3] Jaroniec C P,Kruk M,Jaroniec M,et al.Tailoring surface and structural properties of MCM-41 silicas by bonding organosilanes[J].The Journal of Physical Chemistry B,1998,102(28):5503-5510.
[4] 袁楚.MCM-41介孔材料的制备、有机功能化改性及吸附性研究[D].武汉:武汉理工大学,2012.
[5] 蔡超.功能化MCM-41介孔材料的合成与催化性能的研究[D].天津:天津大学化工学院,2011.
[6] 沙海涛,吴云海,方鹏.氨基与MCM-41改性石墨电极氧化还原染料酸性红G[J].环境科技,2017,30(3):47-51.
[7] 韦力,蓝任凯,靖宇,等.五乙烯六胺(PEHA)改性MCM-41的制备及其CO2吸附性能[J].化工进展,2011(S2):143-148.
[8] 张晔,吴东,孙予罕,等.疏水增透SiO2膜的制备及其性能研究[J].物理化学学报,2002,18(4):355-358.
[9] Nicolas M,Guittard F,Géribaldi S.Stable superhydrophobic and lipophobic conjugated polymers films[J].Langmuir,2006,22(7):3081-3088.
[10] Okiel K,El-Sayed M,El-Kady M Y.Treatment of oil-water emulsions by adsorption onto activated carbon,bentonite and deposited carbon[J].Egyptian Journal of Petroleum,2011,20(2):9-15.
[11] 张明杰,许芝.淀粉接枝系高吸水吸油树脂的合成[J].化工新型材料,2007,35(1):59-60.
[12] 张娟芳,吴永民,余江龙.超疏水材料的应用状况和市场前景分析[J].经济师,2014(10):265-266.
[13] 蒋必彪,朱亮.高吸油性树脂的合成与性能[J].高分子材料科学与工程,1996(6):25-28.
[14] 刘秀奇,张国,李海东,等.矿粉/EPDM新型吸油材料的制备及其吸油性[J].弹性体,2007,17(5):49-52.
[15] Atta A M,Arndt K F.Swelling of high oil-absorptive network based on 1-octene and isodecyl acrylate copolymers[J].Journal of Applied Polymer Science,2005,12(2):77-88.
[16] 寇希元,王静,王文华,等.纳米聚丙烯-丙烯酸酯改性材料的制备及其吸油性能研究[J].海洋环境科学,2015,34(4):519-523.
[17] 周继根.超双疏表面的制备及其润湿性研究[D].青岛:青岛理工大学机械工程学院,2010.
[18] 马建华,吴广明,程银兵,等.疏水型SiO2光学增透膜的制备[J].物理化学学报,2001,17(12):1112-1116.
[19] Wu W,Wang X,Wang D,et al.Alumina nanowire forests via unconventional anodization and super-repellency plus low adhesion to diverse liquids[J].Chemical Communications,2009,9(9):1043-1045.
[20] 何丽红,周超,李力,等.硅烷偶联剂表面改性二氧化钛粒子超疏水性能[J].精细化工,2014,31(9):1061-1064.
[21] Sugimura H,Hozumi A,Kameyama T,et al.Organosilane self-assembled monolayers formed at the vapour/solid interface[J].Surface and Interface Analysis,2002,34(1):550-554.
Options
Outlines

/