Study on the property of PVA fiber reinforced metakaolin hydraulic lime mortar

Expand
  • 1. Northwest Research Institute Co.,Ltd.,China Railway Engineering Corporation, Lanzhou 730000;
    2. Grottoes Protection Technology Base of State Administration of Cultural Heritage,Lanzhou 730000;
    3. Geotechnical Cultural Relics Protection Research Center of Gansu Province,Lanzhou 730000

Received date: 2020-09-01

  Revised date: 2020-11-16

  Online published: 2021-03-03

Abstract

Aiming at the problems of metakaolin hydraulic lime mortar material,such as low tensile strength,low ultimate elongation and brittleness,in order to improve its toughness and stability,enhance its crack resistance,the PVA fiber doped metakaolin hydraulic lime mortar material was designed and prepared.The shrinkage rate,wave velocity,compressive strength,flexural strength and splitting tensile strength of the mortar with different content and length of PVA fiber were studied.The mechanism of PVA fiber in mortar was analyzed by SEM.The results shown that PVA fiber changed the shrinkage and internal structure of the mortar.The flexural strength and splitting tensile strength increased with increasing the fiber amount.The compressive strength decreased with increasing the fiber amount when the fiber length was constant.PVA fiber can obviously improve the integrity of mortar,and kep good original condition after compression.Mechanical riveting cooperation was developed between fiber and mortar,and had good adhesion.

Cite this article

Zhao Xuan, Wang Jie, Wang Fengrui, Zhang Xiaobing, Qiao Zhen, Wang Ruilin . Study on the property of PVA fiber reinforced metakaolin hydraulic lime mortar[J]. New Chemical Materials, 2021 , 49(2) : 249 -253 . DOI: 10.19817/j.cnki.issn 1006-3536.2021.02.057

References

[1] Ravi R,Thirumalini S.Effect of natural polymers from cissus glauca roxb on the mechanical and durability properties of hydraulic lime mortar[J].International Journal of Architectural Heritage,2018,13(11):1-15.
[2] Zhuang X S,Yu X Y.Experimental study on strength characteristics of lime-basalt fiber reinforced expansive soil[J].Applied Mechanics and Materials,2015,744-746:495-498.
[3] Maria L S,Francesca S,Martina Z,et al.Basalt fiber reinforced natural hydraulic lime mortars:a potential bio-based material for restoration[J].Materials & Design,2014,63:398-406.
[4] 袁勇,邵晓芸.合成纤维增强混凝土的发展前景[J].混凝土,2000(12):3-7.
[5] Reza B,Milad A,Ahmad F.Mechanical properties of steel and polymer fiber reinforced concrete[J].Journal of the Mechanical Behavior of Materials,2019,28(1):119-134.
[6] 高淑玲,徐世烺.PVA纤维增强水泥基复合材料拉伸特性试验研究[J].大连理工大学学报,2007,47(2):233-239.
[7] Prasanthni P,Palanisamy T.Mechanical characteristics and structural behaviour of engineered cementitious composites using polyvinyl alcohol fiber[J].Asian Journal of Research in Social Sciences and Humanities,2016,6(7):749-761.
[8] Tehmina A,Nasir S,Muhd F N.Analytical prediction of the mechanical properties of high performance PVA fiber reinforced concrete[J].Applied Mechanics and Materials,2014,3228:345-350.
[9] 高亚宁,史志杰,薛智刚.超高强度聚乙烯醇纤维的生产工艺研究[J].合成纤维,2006,35(6):36-38.
[10] 张景科,王南,樊孟,等.烧料礓石改性遗址土裂隙注浆材料龄期性能试验研究[J].岩石力学与工程学报,2018,37(1):220-229.
[11] Abu-Farsakh G A,Abdel-Jawad Y A,Abu-Laila K.Micromechanical characterization of tensile strength of fiber composite materials[J].Mechanics of Composite Materials & Structures,2000,7(1):105-122.
[12] 陈亚迪,洪丽,蒋津,等.水泥砂浆基体中玄武岩纤维的拔出试验研究[J].硅酸盐通报,2019,38(9):2985-2991.
Options
Outlines

/