Study on GO modified inorganic hydrate ternary shape-stabilized PCM

Expand
  • School of Materials Science and Engineering,Jilin Jianzhu University,Changchun 130118

Received date: 2019-09-23

  Revised date: 2020-09-28

  Online published: 2021-01-27

Abstract

Two low eutectic mixtures of inorganic hydrated salt ternary phase change material(PCM) were prepared,then using porous expanded perlite to adsorb it by vacuum adsorption method.The thermal conductivity of the PCM was improved by graphene oxide(GO).The shape-stabilized PCM were prepared by encapsulation with HDPE.The samples were analyzed by SEM,IR,DSC and XRD.The effects of adsorption amount and GO content on the thermal properties of the PCM were studied.The results shown that when the adsorption capacity of PCM was 74.8% and 72.4%,the thermal properties of phase change perlite in the two systems were the best.The phase change temperatures were 30℃ and 49℃,and the phase change enthalpies were 82J/g and 134J/g.Under the optimal adsorption capacity,when the content of GO was 0.6%,the thermal properties of the PCM in the two systems were the best.Excellent,the phase transition temperature were 28℃ and 42℃,and the phase change enthalpies were 77J/g and 122J/g.

Cite this article

Xiao Liguang, Li Bing, Wang Jingwei . Study on GO modified inorganic hydrate ternary shape-stabilized PCM[J]. New Chemical Materials, 2021 , 49(1) : 77 -80 . DOI: 10.19817/j.cnki.issn 1006-3536.2021.01.017

References

[1] 肖力光,宋双.智能调温相变材料研究综述[J].吉林建筑大学学报,2016,33(2):43-46.
[2] 肖力光,李冰.相变材料在建筑节能领域的应用及研究[J].北方建筑,2019(4):51-55.
[3] 史巍,王传涛.相变材料研究综述[J].硅酸盐通报,2015,34(12):3517-3522.
[4] 蒋自鹏,铁生年.膨胀石墨/芒硝复合定形相变材料制备及性能研究[J].材料导报,2016,30(12):55-60.
[5] 刘磊,彭犇,邱桂博,等.不同载体的Na2SO4·10H2O基定形相变材料的制备和热性能研究[J].人工晶体学报,2017,46(12):2374-2379,2385.
[6] Chen C Z,Chen J,Jia Y F,et al.Binary shape-stabilized phase change materials based on poly(ethylene glycol)/polyurethane composite with dual-phase transition[J].Journal of Materials Science,2018,53(24).
[7] 程耀飞.石蜡/多孔火山岩复合相变材料的制备及性能表征[J].化工新型材料,2016,44(8):204-206.
[8] Zhang X G,Yin Z Y,Meng D Z,et al.Shape-stabilized composite phase change materials with high thermal conductivity based on stearic acid and modified expanded vermiculite[J].Renewable Energy,2017,112.
[9] Xiao L G.A new kind of shape-stabilized phase change materials[J].Journal of Wuhan University of Technology(Materials Science Edition),2011,26(3):491-494.
[10] Xiao L G,Zhao M Y,Hu H L.Study on graphene oxide modified inorganic phase change materials and their packaging behavior[J].Journal of Wuhan University of Technology(Materials Science),2018,33(4):788-792.
Options
Outlines

/