Preparation of Cu2O/TiO2 nanotube and photoelectric reduction of CO2 at gas-solid interface

Expand
  • 1. School of Materials and Chemical Engineering,Zhengzhou University of Light Industry,Zhengzhou 450001;
    2. Collaborative Innovation Center of Environmental Pollution Control and Ecological Restoration,Zhengzhou 450001;
    3. Henan Metallurgical Research Institute Co.,Ltd.,Zhengzhou 450001

Received date: 2019-09-24

  Revised date: 2020-09-21

  Online published: 2021-01-21

Abstract

TiO2 nanotubes with different anodic oxidation time were prepared by anodic oxidation method,and Cu2O was deposited on the surface of TiO2 nanotubes by electrochemical method.The composite catalyst Cu2O/TiO2 was characterized by FESEM,XRD and XPS.The photoelectric reduction of CO2 by Cu2O/TiO2 composite catalyst at gas-solid interface was studied by using a self-made photoelectricity catalytic reaction device-“double pool and double interface reactor”.The results showed that the catalytic products were CH4 and CO.The highest CH4 content in the catalytic products was 1.678μL.At its peak,CO can reach 11.499μL.The content of CO in the catalytic products was significantly higher than that of CH4,indicating that the prepared composite catalyst Cu2O/TiO2-2 had good selectivity for the generation of CO products.

Cite this article

Zhang Hongzhong, Qian Xuhui, Wang Lan, Song Yali, Zhou Hanghang, Zhang Huan, Zhang Yifei . Preparation of Cu2O/TiO2 nanotube and photoelectric reduction of CO2 at gas-solid interface[J]. New Chemical Materials, 2020 , 48(12) : 89 -92 . DOI: 10.19817/j.cnki.issn 1006-3536.2020.12.022

References

[1] 陈为,魏伟,孙予罕.二氧化碳光电催化转化利用研究进展[J].中国科学:化学,2017,47(11):1251-1261.
[2] 陈倩倩,顾宇,唐志永,等.以二氧化碳规模化利用技术为核心的碳减排方案[J].中国科学院院刊,2019,34(4):478-487.
[3] 饶旭峰,许杰,刘予宇,等.光电催化还原二氧化碳概览[J].自然杂志,2017,39(4):235-241.
[4] 周天辰,何川,张亚男,等.CO2的光电催化还原[J].化学进展,2012,24(10):1897-1905.
[5] 魏伟,孙予罕,闻霞,等.二氧化碳资源化利用的机遇与挑战[J].化工进展,2011,30(1):216-224.
[6] Dong Y,Nie R,Wang J,et al.Photoelectrocatalytic CO2 reduction based on metalloporphyrin-modified TiO2 photocathode[J].Chinese Journal of Catalysis,2019,40(8):1222-1230.
[7] 赖跃坤,孙岚,左娟,等.氧化钛纳米管阵列制备及形成机理[J].物理化学学报,2004,20(9):1063-1066.
[8] Susman M D,Feldman Y,Vaskevich A,et al.Chemical deposition of Cu2O nanocrystals with precise morphology control[J].ACS Nano,2014,8(1):162.
[9] 张宏忠,李旭燕,杨柳阳,等.光电催化还原CO2为气体燃料的研究进展[J].化工新型材料,2018,46(8):221-224,230.
[10] 张宏忠,张钰,叶长明,等.CO2在铜掺杂的TiO2纳米管中的光催化还原研究[J].化工新型材料,2017,45(11):124-127.
[11] 孙岚,李静,庄惠芳,等.TiO2纳米管阵列的制备、改性及其应用研究进展[J].无机化学学报,2007,23(11):1841-1850.
[12] Chen W,Fan Z,Lai Z.Synthesis of core-shell heterostructured Cu/Cu2O nanowires monitored by in situ XRD as efficient visible-light photocatalysts[J].Journal of Materials Chemistry A,2013,1(44):13862-13868.
[13] 唐一文,陈志钢,张丽莎,等.纳米Cu2O/TiO2异质结薄膜电极的制备和表征[J].无机材料学报,2006,21(2):453-458.
Options
Outlines

/