Preparation and property of SBR/AF composite modified by maleic anhydride graft compatibilizer

Expand
  • 1. School of Physics and Electronic Science,Guizhou Education University,Guiyang 550018;
    2. College of Materials and Metallurgy,Guizhou University,Guiyang 550025;
    3. School of Materials Science and Engineering,Hainan university,Haikou 570228;
    4. Guizhou Iinstitute of Technology,Guiyang 550005

Received date: 2020-06-11

  Revised date: 2020-09-01

  Online published: 2021-01-21

Abstract

Styrene butadiene rubber(SBR)/aramid fiber(AF) composites were prepared by adding compatibilizers with different state and grafting ratio of maleic anhydride.The tensile strength,tear strength,energy storage of material cross section and interface,and fiber dispersity of the composites were studied.The results showed that the aramid fiber with different compatibilizers dispersed uniformly in SBR,and the interfacial bonding property was improved.The tensile strength and elongation at break of the composite increased by nearly 42% and 32.3% respectively when MLPB-2 with high grafting ratio was added.The longitudinal tear and transverse tear of MLPB-1 composite with low grafting ratio increased by 34.1% and 38.1%,respectively.The results shown that the modification effect of viscosity flow compatibilizer was better than that of solid powder compatibilizer.The composite of MLPB compatibilizer was better than that of single MLPB compatibilizer.When the total amount of MLPB-2 compatibilizer was 3phr and the content of MLPB-2 compatibilizer was 2.25phr,the composite had the best comprehensive properties.

Cite this article

Xiang Kun, Luo Zhu, Xu Nai, Li Yang, Xiong Deyong, Zhou Zhuwen, Liu Gaofu . Preparation and property of SBR/AF composite modified by maleic anhydride graft compatibilizer[J]. New Chemical Materials, 2020 , 48(12) : 57 -60 . DOI: 10.19817/j.cnki.issn 1006-3536.2020.12.014

References

[1] 杨清芝.现代橡胶工艺学[M].北京:中国石化出版社,1997,35-33.
[2] 杨清芝,李俊山,张殿荣.实用橡胶工艺学[M].北京:化学工业出版社,2012,4-6.
[3] 郝元恺,肖加余.高性能复合材料学[M].北京:化学工业出版社,2012,9.
[4] 王杰,吴卫东,周洪福,等.短纤维对丁苯橡胶复合材料性能的影响[J].化工新型材料,2020,48(2):224-227,231.
[5] 刘珍,韩雷,赵永仙,等.共单体对GMA熔融接枝iPB-1的影响[J].现代塑料加工应用,2013(5):11-14.
[6] Yin Lianpeng,Zhou Zongtao,Luo Zhu,et al.Reinforcing effect of aramid fibers on fatigue behavior of SBR/aramid fiber composites[J].Polymer Testing,2019,80(8):1-8.
[7] Rajaee P,Ghasemi F A,Fasihi M,et al.Effect of styrene-butadiene rubber and fumed silica nano-filler on the microstructure and mechanical properties of glass fiber reinforced unsaturated polyester resin[J].Composites Part B,2019,173(5):1-43.
[8] Khafidh M,Schipper D J,Masen M A,et al.Tribological behavior of short-cut aramid fiber reinforced SBR elastomers:the effect of fiber orientation[J].Journal of Mechanical Engineering and Sciences (JMES),2018,12(2):3700-3711.
[9] Sapsrithong P,Puksattee K,Saewjaidee K,Pensuk N,et al.The influence of fiber surface treatment and SBR as impact modifier on rheological behavior and mechanical properties of wood plastic composite from acrylate-styrene-acrylonitrile and bagasse[J].Key Engineering Materials,2017,73(7):281-286.
[10] 金仲,罗筑,李斌,等.相容剂HTPB-g-MA的合成及对芳纶增强天然橡胶复合材料性能的影响[J].高分子材料科学与工程,2016,32(1):6-12.
[11] 金仲,夏忠林,罗筑,等.接枝改性对芳纶纤维增强天然橡胶复合材料性能的影响[J].高分子材料科学与工程,2015,31(8):56-61.
Options
Outlines

/