Study on the preparation technology of PTFE/AF composite

Expand
  • 1. Isotope Institute Co.,Ltd.,Henan Academy of Sciences,Zhengzhou 450015;
    2. Luoyang Bearing Science & Technology Co.,Ltd.,Luoyang 471003

Received date: 2020-03-12

  Revised date: 2020-09-23

  Online published: 2021-01-21

Abstract

Polytetrafluoroethylene (PTFE) was used as the matrix,aramid fiber(AF) was treated by radiation as the reinforcing agent,and the PTFE/AF composite were prepared by molding and high temperature sintering.The effects of AF content,forming pressure,holding time,sintering temperature and holding time on the properties of the composite were studied.The results shown that when AF content was 15%,not only the AF was evenly dispersed in the composite,but also the mechanical properties of the composite were excellent.The suitable preparation process of the composite was that molding pressure 80MPa,pressure holding time 10mins,sintering temperature 385℃,holding time 300mins.

Cite this article

Liu Shubo, Wang Zijun, Zhang Hongna, Yang Mingcheng, Zhang Benshang, Zhang Zhenya . Study on the preparation technology of PTFE/AF composite[J]. New Chemical Materials, 2020 , 48(12) : 48 -51 . DOI: 10.19817/j.cnki.issn 1006-3536.2020.12.012

References

[1] Wang H,Yan L,Gao D,et al.Tribological properties of superamphiphobic PPS/PTFE composite coating in the oilfield produced water[J].Wear,2014,319(1-2):62-68.
[2] 王瑞柳,徐广标,何越超.聚四氟乙烯(PTFE)纤维结构、性能与应用研究进展[J].纺织科学与工程学报,2018,35(3):113-117.
[3] 冉帆,郎伟钦.聚四氟乙烯曲轴后油封的气密性研究[J].柴油机设计与制造,2018,24(4):24-29.
[4] 李红波,苏正涛,杨睿,等.硅灰石与石墨对聚四氟乙烯摩擦磨损性能的影响[J].中国塑料,2018,32(10):32-38.
[5] 杨保利,吴明清,张佩,等.烧结工艺对聚四氟乙烯喷口制品性能的影响[J].绝缘材料,2018,51(10):45-49.
[6] 吴家祥,方向,李裕春,等.PTFE/Al/Al2O3反应材料的力学性能与反应特性[J].工程塑料应用,2018,46(12):105-109.
[7] 龙啸云.聚四氟乙烯自润滑复合土工布的制备与性能研究[D].无锡:江南大学,2018.
[8] 王战辉,马向荣,范晓勇,等.碳纤维填充聚四氟乙烯复合材料力学性能研究[J].当代化工,2018,47(11):2255-2258.
[9] Xu Y,Huang C,Jin X.A comparative study of characteristics of polytetrafluoroethylene fibers manufactured by various processes[J].Journal of Applied Polymer Science,2016,133(26),DOI:10.1002/app.43553.
[10] Wang Y,Tian M,Qu L,et al.Polytetrafluoroethylene yarns with thermal stability and fire retardance by scrolled-membrane spinning[J].The Journal of the Textile Institute,2017,108(2):293-299.
[11] 张瑶,陈蓉,郭少云.SiO2/聚四氟乙烯复合薄膜的制备及力学性能[J].复合材料学报,2019,36(3):624-629.
[12] 王建吉,刘涛.聚酰亚胺填充PTFE复合材料摩擦学性能的研究[J].功能材料,2018,49(9):9072-9077.
[13] 邹若东.聚四氟乙烯复合材料含油摩擦特性研究[J].天津化工,2018,32(3):22-24.
[14] 石国军,李翠,袁月.莫来石与碳纤维协同填充的聚四氟乙烯基复合材料及其摩擦学性能[J].复合材料学报,2016,33(9):1886-1898.
[15] 陈涛,焦明华,田明,等.稀土化合物对PTFE基三层复合材料摩擦磨损性能的影响[J].润滑与密封,2015,40(1):37-40.
[16] 李文娟,游一兰,李笃信,等.PTFE及UHMWPE改性PA6复合材料的摩擦学性能研究[J].摩擦学学报,201,333(2):123-128.
[17] 张振亚,郭文慧,刘树博,等.芳纶浆粕纤维的辐照改性研究[J].河南科学,2019,37(11):1747-1751.
[18] 戴骏.芳纶改性及其增强天然橡胶复合材料的性能研究[D].贵阳:贵州大学,2017.
[19] 张艳华.γ-射线辐照改性对芳纶纤维及其复合材料性能的影响[D].哈尔滨:哈尔滨工业大学,2008.
[20] 高贵,李瑞红,龚俊,等.对偶表面粗糙度对Nano-SiO2改性PTFE复合材料摩擦学性能的影响[J].工程科学与技术,2020,52(2):1-8.
[21] 蒋奔,翟明.塑料模具表面粗糙度变化机理及影响因素分析[J].工程塑料应用,2017,45(6):137-140.
Options
Outlines

/