Development and research progress of surface treatment technology for architectural Al profile

Expand
  • 1. College of Marine Engineering,Jimei University,Xiamen 361021;
    2. Guangzhou Synthetic Materials Research Institute Co.,Ltd.,Guangzhou 510665

Received date: 2019-09-05

  Revised date: 2020-09-18

  Online published: 2021-01-21

Abstract

The application performances of three surface treatment technologies for the architectural Al profiles were summarized,compared the advantages and disadvantages among the three technologies.The advantages of powder spraying technology were analyzed under surface treatment of Al profiles,and introduced the researching progress of powder coating regarding to weatherability and low temperature curing.

Cite this article

Lin Lanfang, Peng Jun . Development and research progress of surface treatment technology for architectural Al profile[J]. New Chemical Materials, 2020 , 48(12) : 18 -21 . DOI: 10.19817/j.cnki.issn 1006-3536.2020.12.005

References

[1] 朱祖芳.建筑铝型材的表面处理技术现况及发展趋势[J].电镀与涂饰,2005,24(4):14-17.
[2] 马腾,王振尧,韩薇.铝和铝合金的大气腐蚀[J].腐蚀科学与防护技术,2004,16(3):155-161.
[3] 张燕斌,林佳钰,于佳音.建筑铝型材表面氧化膜的制备及其性能[J].材料保护,2016,49(7):60-62.
[4] 朱祖芳.我国铝型材表面处理工艺的发展回顾及未来思考[J].材料保护,2010,43(4):6-9.
[5] 张燕斌,王荣华.建筑铝型材的表面阳极氧化与耐热性能研究[J].铸造技术,2016,32(8):1567-1571.
[6] 李若林.建筑铝型材阳极氧化低温封孔的应用探讨[J].甘肃冶金,2000,15(2):20-21.
[7] 黄大江.铝合金建筑型材的涂装[J].涂装与电镀,2009,24(5):18-23.
[8] 别锋军.建筑铝型材的电泳涂漆[J].有色金属加工,1998,6(3):1-8.
[9] 何涛.铝型材氧化着色生产线槽液循环系统[J].轻合金加工技术,2005,21(11):33-35.
[10] 刘娅莉,暨调和.铝型材电泳涂装技术及发展[J].涂装与电镀,2002,1(1):41-45.
[11] 朱祖芳.铝合金建筑型材表面处理技术发展和质量评价分析[J].中国金属通报,2007,21(19):3-8.
[12] 张华东.应用在铝型材处理中的粉末喷涂[J].中国涂料,2006,21(6):42-44.
[13] 孙永泰.粉末喷涂在铝型材处理中的应用[J].上海建材,2009,13(1):27-29.
[14] 陈闯,李勇,刘亮,等.户外粉末涂料用聚酯树脂的制备与性能研究[J].涂料技术与文摘,2015,36(2):7-9.
[15] 刘国杰.现代涂料工艺新技术[M].北京:中国轻工业出版社,2000,69-71.
[16] 武利民.涂料技术基础[M].北京:化学工业出版社,1999,21-27.
[17] 李光,丁振刚,高庆福.一种低温固化环氧基丙烯酸透明粉末涂料及其制备方法:中国,105273558A[P].2016-01-27.
[18] 张剑,李国威,邢方圆,等.山东朗法博粉末涂装科技有限公司.户外MDF粉末涂料及其应用:中国,104497810A[P].2015-04-08.
[19] Wu B.Powder coating compositions containing anhydride end-caped crystalline polyesters:US2006/0009591A[P].2006-01-12.
[20] 马洪英.户外低温固化粉末涂料用聚酯树脂的合成及其性能研究[D].南昌:南昌大学,2013.
[21] 马志平,刘亮,何涛,等.β-羟烷基酰胺体系低温固化粉末涂料用聚酯树脂的合成研究[J].涂料工业,2016,46(4):53-57.
[22] 张剑,陈辉,肖建刚.玻璃钢用超耐候低温固化粉末涂料:中国,103709908A[P].2014-04-09.
[23] 邓慕建,祁永华,龚兴宇,等.低温固化粉末涂料用聚酯树脂及其制备方法:中国,102718952A[P].2012-10-10.
[24] 何涛,顾宇昕,谢静,等.高耐候双组分消光粉末涂料用端羧基聚酯树脂的制备及性能研究[J].涂料工业,2014,44(3):1-4.
[25] 巩永忠,陶冶,任环,等.氟碳粉末涂料在建材表面的应用进展[J].涂料工业,2015,45(5):78-81.
[26] 张云伟.一种重防腐超耐候粉末涂料及其制备方法和应用:中国,103173073B[P].2015-06-03.
[27] 魏育福,蔡劲树,蔡英进,等.一种铝型材用氟树脂改性聚酯粉末涂料及其制备方法:中国,103849298A[P].2014-06-11.
[28] 高庆福,梁泳田,李光,等.氟碳-聚酯复合型超耐候粉末涂料的研制[J].涂料技术与文摘,2016,37(4):23-25.
[29] 杨小青,朱梅芳,俞剑峰,等.高耐候卷材涂料用聚酯树脂[J].涂料工业,2006,36(12):35-37.
[30] 郑荣辉,鲍观良,毕海鹏,等.超耐候粉末涂料用聚酯树脂、使用该树脂的粉末涂料及其制备方法:CN104530408A[P].2015-04-22.
[31] Chang Y H,Barbee R B.Weatherablepowdercoatings:US5393609[P].1995-02-28.
[32] 施奇武,黄婉霞,郭刚,等.铝酸酯干法改性纳米TiO2及其在粉末涂料抗老化中的应用[J].高分子材料科学与工程,2009,25(9):113-116.
Options
Outlines

/