Photoelectric sensing property of TiO2 core-shell microsphere for formaldehyde

Expand
  • 1. College of Pharmacy,Qiqihar Medical University,Qiqihar 161006;
    2. College of Pathology,Qiqihar Medical University,Qiqihar 161006;
    3. College of Adult and Continuing Education,Qiqihar Medical University,Qiqihar 161006;
    4. College of Basic Medical,Qiqihar Medical University,Qiqihar 161006

Received date: 2019-05-24

  Revised date: 2020-06-29

  Online published: 2020-10-20

Abstract

TiO2 core-shell microspheres were prepared by a simple one-step hydrothermal method.The obtained TiO2 was an anatase crystal phase and had an irregular core-shell structure,and the surface of the microspheres was composed of regular octahedral particles.The gas sensitivity test results shown that the sample had an excellent response to formaldehyde gas,and a significant photocurrent response to 10 ppm of formaldehyde gas,and has the largest response to 30 ppm of formaldehyde gas.The charge microscopic kinetics of the sample shown excellent photogenerated charge carrier separation and transmission efficiency.Good gas sensitivity may be related to its rough surface and large specific surface area.The special morphology promoted the adsorption of gas and provided numerous surface-active sites to catalyze the reaction with formaldehyde.

Cite this article

Zhang Hongguang, Wang Guowei, Wang Meng, Wang Yu, Xia Chunhui, Fu Shuang . Photoelectric sensing property of TiO2 core-shell microsphere for formaldehyde[J]. New Chemical Materials, 2020 , 48(9) : 137 -140 . DOI: 10.19817/j.cnki.issn 1006-3536.2020.09.029

References

[1] 朱珠,黄婷婷,杨德虎.浅谈室内装修造成的污染及防治措施[J].江西建材,2019,4:188-190.
[2] Chiang C M,Huang K C,Lee C C,et al.Establish sorptive test system and validation of the reduction indoor HCHO concentrations by building material in Taiwan[J].Adv Mater Res-Switz,2011,314:1435-1440.
[3] 吴洁,芮广虎,宋人杰,等.AHMT法测定制药设备表面甲醛残留[J].中国药师,2014,17(2):330-332.
[4] Fox J M,Shuttleworth G,Martin F.Methodology to reduce formaldehyde exposure during laboratory fumigation[J].Int J Environ Heal R,2013,23(5):400-406.
[5] 曾志强,周牧野,李容,等.碘氧化铋硅藻泥净化室内空气甲醛性能研究[J].广州化工,2019,47(8):55-57.
[6] Zyrichidou I,Balis D,Koukouli M E,et al.Adverse results of the economic crisis:a study on the emergence of enhanced formaldehyde (HCHO) levels seen from satellites over Greek urban sites[J].Atmos Res,2019,224:42-51.
[7] Zhu K M,Ma S Y.Preparations of Bi-doped SnO2 hierarchical flower-shaped nanostructures with highly sensitive HCHO sensing properties[J].Mater Lett,2019,236:491-494.
[8] Li H,Chu S S,Ma Q,et al.Hierarchical WO3/ZnWO4 1D fibrous heterostructures with tunable in-situ growth of WO3 nanoparticles on surface for efficient low concentration HCHO detection[J].Sensor Actuat B-Chem,2019,286:564-574.
[9] Liu D,Shi P,Ren W,et al.Fabrication and characterization of La0.8Sr0.2CrO3/In2O3 thin film thermocouple for high temperature sensing[J].Sensor Actuat a-Phys,2018,280:459-465.
[10] Alchaar R,Makhlouf H,Abboud N,et al.Enhanced UV photosensing properties of ZnO nanowires prepared by electrodeposition and atomic layer deposition[J].J Solid State Electr,2017,21(10):2877-2886.
[11] Kathalingam A,Kim H S.Fabrication of two-terminal devices using solution-synthesized Cu-doped ZnO nanorods and their photosensing properties[J].Opt Mater Express,2018,8(9):2832-2842.
[12] Ramos R A,Boratto M H,Scalvil V A.On the photo-induced electrical conduction related to gas sensing of the Sb∶SnO2/TiO2 heterostructure[J].Sensor Actuat a-Phys,2018,281:250-257.
[13] Zhang X J,Deng N,Chen X J,et al.Metal-Doped In2O3 nanosphere arrays with enhanced gas-sensing property[J].Nano,2019,14(3):195-201.
[14] Jiang X D,Xu W C,Yu L.Photocatalytic decomposition of gaseous HCHO over Ag modified TiO2 nanosheets at ambient temperature[J].Nanomaterials-Basel,2019,9(3):365-369.
[15] Wu G F,Zhao C H,Zhou X,et al.The interaction between HCHO and TiO2 (101) surface without and with water and oxygen molecules[J].Appl Surf Sci,2018,455:410-417.
Options
Outlines

/