Anatase TiO2 with exposed {101} facets was discussed in the influence of temperature to the photocatalysis.The thermocatalysis for benzene degradation was tested.The photocatalysis and photothermocatalysis were contrasted between anatase TiO2 with exposed {101} facets and {001} facets.The results indicated that with the increase of the temperature,the photocatalysis for benzene degradation improved.There was synergetic effect between photocatalysis and thermocatalysis.The CO2 specific production rate of photothermocatalysis for benzene degradation increased 7.19 times higher than that of photocatalysis.Anatase TiO2 with exposed {101} facets showed higher photocatalytic activity and lower photothermocatalytic activity for benzene degradation than anatase TiO2 with exposed {001} facets.
Ren Lu, Mao Mingyang, Jiang Ke
. Photothermocatalysis of anatase TiO2 with exposed {101} facet for benzene degradation[J]. New Chemical Materials, 2020
, 48(7)
: 196
-200
.
DOI: 10.19817/j.cnki.issn 1006-3536.2020.07.045
[1] 唐其文,吴艳.挥发性有机物VOCs监测方法及治理[J].环境与发展,2018,30(6):159-161.
[2] Mamaghani A H,Haghighat F,Lee C S.Photocatalytic oxidation technology for indoor environment air purification:the state-of-the-art[J].Applied Catalysis B-Environmental,2017,203:247-269.
[3] Shu Y J,Ji J,Xu Y,et al.Promotional role of Mn doping on catalytic oxidation of VOCs over mesoporous TiO2 under vacuum ultraviolet (VUV) irradiation[J].Applied Catalysis B-Environmental,2018,220:78-87.
[4] Jin Z,Wang L,Hu Q X,et al.Hydrophobic zeolite containing titania particles as wettability-selective catalyst for formaldehyde removal[J].ACS Catalysis,2018,8(6):5250-5254.
[5] Shayegan Z,Lee C S,Haghighat F,TiO2 photocatalyst for removal of volatile organic compounds in gas phase-a review[J].Chemical Engineering Journal,2018,334:2408-2439.
[6] Ren L,Li Y Z,Mao M Y,et al.Significant improvement in photocatalytic activity by forming homojunction between anatase TiO2 nanosheets and anatase TiO2 nanoparticle[J].Appllied Surface Science,2019,490:283-292.
[7] Weon S,Choi W.TiO2 nanotubes with open channels as deactivation-resistant photocatalyst for the degradation of volatile organic compounds[J].Environmental Science & Technology,2016,50(5):2556-2563.
[8] Lu Z,Zeng L,Song W,et al.In situ synthesis of C-TiO2/g-C3N4 heterojunction nanocomposite as highly visible light active photocatalyst originated from effective interfacial charge transfer[J].Applied Catalysis B-Environmental,2017,202:489-499.
[9] Zhang L,Qin M,Yu W,et al.Heterostructured TiO2/WO3 nanocomposites for photocatalytic degradation of toluene under visible light[J].Journal Electrochemical Society,2017,164(14):1086-1090.
[10] Alami W E,Sousa D G,Gonzalez J M D,et al.TiO2 and F-TiO2 photocatalytic deactivation in gas phase[J].Chemical Physics Letters,2017,684:164-170.
[11] Haselmann G M,Eder D.Bimodal mesoporous TiO2 supported Pt,Pd and Ru catalysts and their catalytic performance and deactivation mechanism for catalytic combustion of Dichloromethane (CH2Cl2)[J].ACS Catalysis,2017,7(7):4668-4675.
[12] Lyu J Z,Shao J W,Wang Y H,et al.Construction of a porous core-shell homojunction for the photocatalytic degradation of antibiotics[J].Chemical Engineering Journal,2019,358:614-620.
[13] Chen X B,Liu L,Yu P Y,et al.Increasing solar absorption for photocatalysis with black hydrogenated titanium dioxide nanocrystals[J].Science,2011,331(6018):746-750.
[14] Ren L,Mao M Y,Li Y Z,et al.Novel photothermocatalytic synergetic effect leads to high catalytic activity and excellent durability of anatase TiO2 nanosheets with dominant {001} facets for benzene abatement[J].Applied Catalysis B-Environmental,2016,198:303-310.
[15] Li Y Z,Huang J C,Peng T,et al.Photothermocatalytic synergetic effect leads to high efficient detoxification of benzene on TiO2 and Pt/TiO2 nanocomposite[J].Chem Cat Chem,2010,2(9):1082-1087.
[16] Kong M,Li Y,Chen X,et al.Tuning the relative concentration ratio of bulk defects to surface defects in TiO2 nanocrystals leads to high photocatalytic efficiency[J].Journal of the American Chemical Society,2011,133(41):16414-16417.
[17] Ren L,Li Y Z,Hou J T,et al.The pivotal effect of the interaction between reactant and anatase TiO2 nanosheets with exposed {001} facets on photocatalysis for the photocatalytic purification of VOCs[J].Applied Catalysis B-Environmental,2016,181:625-634.
[18] Yang H G,Sun C H,Qiao S Z,et al.Anatase TiO2 single crystals with a large percentage of reactive facets[J].Nature,2008,453:638-642.
[19] Tong H F,Zhou Y Y,Chang G,et al.Anatase TiO2 single crystals with dominant {001} facets:synthesis,shape-control mechanism and photocatalytic activity[J].Appllied Surface Science,2018,444:267-275.
[20] Yu J G,Low J X,Xiao W,et al.Enhanced photocatalytic CO2-reduction activity of anatase TiO2 by coexposed {001} and {101} facets[J].Journal of the American Chemical Society,2014,136:8839-8842.