Preparation and property of colorful nano-silver antibacterial agent

Expand
  • 1. Department of Materials and Food,University of Electronic Science and Technology of China Zhongshan Institute,Zhongshan 528402;
    2. Zhongshan Agricultural Products Quality Supervision and Inspection Institute,Zhongshan 528405;
    3. Department of Materials Science and Engineering,Tsinghua University,Beijing 100086

Received date: 2019-03-12

  Online published: 2022-11-01

Abstract

Three kinds of silver colloids with colors of yellow,purple,and blue,respectively,were synthesized at room temperature with silver nitrate as raw material,sodium citrate as surface modifier,ascorbic acid or borohydride as reducing agent.Transmission electron microscopy (TEM) results demonstrated that there were irregular silver nanoparticles,small triangular silver nanoplates and nanoparticles,and large triangular silver nanoplates in the yellow,purple and blue silver colloids,respectively.In order to reveal the three kinds of silver colloids antibacterial substance,escherichia coli as antimicrobial object was used.The experimental results showed that three kinds of silver colloids had good antibacterial properties.Among them,the antibacterial property of silver nanoparticles was the best,followed by small silver nanoplates,and the antibacterial property of large silver nanoplates was the weakest.The antibacterial properties of silver nanostructures with different morphologies were related to the activity and specific surface area of silver nanostructures.

Cite this article

Mou Dengke, Zhou Huansen, Zhong Jianjun, Jia Xiaofei, Feng Minling, Zhao Yuzhen, Wang Yuehui . Preparation and property of colorful nano-silver antibacterial agent[J]. New Chemical Materials, 2020 , 48(7) : 93 -95 . DOI: 10.19817/j.cnki.issn 1006-3536.2020.07.022

References

[1] Yin J,YangY,Hu Z,et al.Attachment of silver nanoparticles(AgNPs) onto thin film composite (TFC) membranes through covalent bonding to reduce membrane biofouling[J].Journal of Membrane Science,2013,441(16):73-82.
[2] Tobaldi D M,Piccirillo C,Pullar R C,et al.Silver-modified nano-titania as an antibacterial agent and photocatalyst[J].Journal of Physical Chemistry C,2014,118(9):751-4766.
[3] 曹雪玲,陆书来,张东杰,等.纳米银作为抗菌剂的抗菌性能研究[J].吉林化工学院学报,2014,34(11):30-34.
[4] Lu W,Wao K,Wang J,et al.Ionic liquids-water interfacial preparation of triangular Ag nanoplates and their shape-depend-entantibacterialactivity[J].Journal of Colloid and Interface Science,2015,437:35-41.
[5] Zapata P A,Larrea M,Tamayo L,et al.Polyethylene/silver-nanofiber composites:a material for antibacterial films[J].Mat Sci Eng C,2016,69:1282-1289.
[6] Ma P,Jiang L,Yu M,et al.Green antibacterial nanocomposites from poly(lactide)/poly(butylene dipateco-terephthalate)/Nanocrystal cellulose-silver nanohybrids[J].ACS Sustainable Chem Eng,2016,4(12):6417-6426.
[7] Amritpal K,Simran P,Vivek K,et al.Synergetic effect of vancomycin loaded silver nanoparticles for enhanced antibacterial activity[J].Colloids and Surfaces B,Biointerfaces,2018,176:62-69.
[8] Tominaga C,Shitomi K,Miyaji H,et al.Antibacterial photocurable acrylic resin coating using a conjugate between silver nanoclusters and alkyl quaternary ammonium[J].ACS Applied Nano Materials,2018,1(9):4809-4818.
[9] Qu Z C,Zhang Y,Liu S W.Preparation and antibacterial properties of silver nanoparticles[C].Shenzhen,China:Proceedings of the 2017 2nd International Conference on Advances in Materials Mechatronics and Civil Engineering (ICAMMCE 2017),2017.
[10] Zhang W L,Zhao X J,Jiang,Y Y,et al.Citrus pectin derived silver nanoparticles and their antibacterial activity[J].Inorganic and Nano-Metal Chemistry,2017,47(1):15-20.
[11] 赖文忠,赵威,杨容,等.用双还原法制备三角形银纳米片及其光学性能[J].物理化学学报,2010,26(4):1177-1183.
Outlines

/