Preparation and property of three-composition thermochromic microcapsule

Expand
  • Beijing Key Laboratory of Clothing Materials R&D and Assessment,Beijing Engineering Research Center of Textile Nanofiber,Beijing Institute of Fashion Technology,Beijing100029

Received date: 2019-02-11

  Online published: 2022-11-01

Abstract

A thermochromic compound was prepared by using crystal violet lactone,bisphenol A and tetradecanol as raw materials.Through orthogonal experiments,the ratio between the three was determined to be m(crystal violet lactone)∶m(bisphenol A)∶m(tetradecanol)=1∶4∶70,and stirring temperature was 70℃ and stirring time was 2h,the thermochromic compound prepared under these conditions had the best discoloration effect.The microcapsules were prepared by the complex coacervation method using the thermochromic compound as the core material and gelatin-arabin gum as the wall material.The preparation conditions were as follows:the emulsification speed was 3500r/min,and the curing time was 3h,the spherical microcapsules with surface smooth were obtained.Prepartion of thermochromic microcapsule with good color-changing properties,heat resistance and acid-base resistance.

Cite this article

Mao Dongyu, Liu Hongru, Wang Xiaochun . Preparation and property of three-composition thermochromic microcapsule[J]. New Chemical Materials, 2020 , 48(7) : 76 -80 . DOI: 10.19817/j.cnki.issn 1006-3536.2020.07.018

References

[1] 焦剑,姚军燕.功能高分子材料[M].北京:化学工业出版社,2016.
[2] 徐栋,陈宏书,王结良.变色材料的研究进展[J].兵器材料科学与工程,2011,34(3):87-91.
[3] 葛婧媛,杨文芳.变色材料在纺织品上的应用[J].染整技术,2007,29(10):5-9.
[4] 李文戈,朱昌中,王文芬,等.可逆热致变色材料[J].功能材料,1997(4):337-341.
[5] 韩路路,毕良武,赵振东,等.微胶囊的制备方法研究进展[J].生物质化学工程,2011,45(3):41-46.
[6] 高燕.热致变色微胶囊的制备及在纺织上的应用研究[D].上海:东华大学,2015.
[7] 王东辉,赵裕蓉.微胶囊的应用及研究进展[J].化工新型材料,1999(7):11-14.
[8] 杨佳,侯占群,贺文浩,等.微胶囊壁材的分类及其性质比较[J].食品与发酵工业,2009,35(5):122-127.
[9] 于永,高艳阳.三芳甲烷苯酞类可逆热致变色材料[J].化工技术与开发,2006,35(10):26-29.
[10] 张宝砚,李远明,姜功臣,等.以孔雀绿内酯为变色剂的可逆示温涂料的研究[J].化工新型材料,1996(10):9-10.
[11] Seeboth A,Klukowska,Ruhmann R,et al.Thermochromic polymer materials[J].Chinese Journal of Polymer Science,2007,25(2):123-135.
Outlines

/