Preparation and swelling of superabsorbent PAA-based nanocomposite hydrogel

Expand
  • Graduate School,Shanghai University of Engineering Science,Shanghai 201620

Received date: 2020-07-04

  Revised date: 2021-09-27

  Online published: 2021-12-31

Abstract

PAA-based nanocomposite hydrogels (VSNPs-PAA) were synthesized through free radical copolymerization by using self-made vinyl hybrid silica nanospheres (VSNPs) as crosslinking agent,and acrylic acid (AA) as monomer.The effect of the content of silica microspheres on the swelling performance of the hydrogel was studied.The swelling rate of the hydrogel can exceed 5000g/g at 50℃ when the content of the microspheres was about 0.7%.The swelling performance of the hydrogel in different concentrations of salt and urea solutions and different pH solutions was also discussed.It was characterized by fourier transform infrared spectrometer (FT-IR),transmission electron microscopy (TEM) and scanning electron microscope (SEM).

Cite this article

Chen Mingyang, Shen Yong, Xu Lihui . Preparation and swelling of superabsorbent PAA-based nanocomposite hydrogel[J]. New Chemical Materials, 2021 , 49(12) : 183 -188 . DOI: 10.19817/j.cnki.issn 1006-3536.2021.12.039

References

[1] Wang S,Zhang Z,Dong L,et al.A remarkable thermosensitive hydrogel cross-linked by two inorganic nanoparticles with opposite charges[J].J Colloid Interf Sci,2019,538:530-540.
[2] Kazeminejadfard F,Hojjati M R.Preparation of superabsorbent composite based on acrylic acid-hydroxypropyl distarch phosphate and clinoptilolite for agricultural applications[J].J Appl Polym Sci,2019,136:47365.
[3] Chen Y,Chen Y.Thermo and pH-responsive methylcellulose and hydroxypropyl methylcellulose hydrogels containing K2SO4 for water retention and a controlled-release water-soluble fertilizer[J].Sci Total Environ,2019,655:958-967.
[4] Roy A,Maity P P,Bose A,et al.β-Cyclodextrin based pH and thermo-responsive biopolymeric hydrogel as a dual drug carrier[J].Mater Chem Front,2019,3,385.
[5] Zhang F,Ren H,Tong G,et al.Ultra-lightweight poly(sodium acrylate) modified TEMPO-oxidized cellulose nanofibril aerogel spheres and their superabsorbent properties[J].Cellulose,2016,23:3665-3676.
[6] Hu X,Wang Y,Xu M,et al.Development of photo crosslinked sale can composite hydrogel embedding titanium carbide nanoparticles as cell scaffold[J].Int J Biol Macromol,2019,123:549-557.
[7] Bardajee G R,Hosseini S S,Vancaeyzeele C.Graphene oxide nanocomposite hydrogel based on poly (acrylic acid) grafted onto salep:an adsorbent for the removal of noxious dyes from water[J].New J Chem,2019,43:3572-3582.
[8] Fang S,Wang G,Li P.Synthesis of chitosan derivative graft acrylic acid superabsorbent polymers and its application as water retaining agent[J].Int J Biol Macromol,2018,115:754-761.
[9] Ghobashy M M,El-Damhougy B K,Nady N.Radiation crosslinking of modifying super absorbent(polyacrylamide/gelatin) hydrogel as fertilizers carrier and soil conditioner[J].Journal of Polymers and the Environment,2018,26:3981-3994.
[10] Sun S,Mao L,Lei Z.Hydrogels from amorphous calcium carbonate and polyacrylic acid:bio-inspired materials for “mineral plastics”[J].Angew Chem Int Edit,2016,55:11765-11769.
[11] Lei Z,Wang Q,Sun S,et al.A bioinspired mineral hydrogel as a self-healable,mechanically adaptable ionic skin for highly sensitive pressure sensing[J].Adv Mater,2017,29:1700321.
[12] Zhong M,Shi F,Liu Y,et al.Tough superabsorbent poly(acrylic acid) nanocomposite physical hydrogels fabricated by a dually cross-linked single network strategy[J].Chinese Chemical Letters,2016,27:312-316.
[13] Zhong M,Liu X,Shi F,et al.Self-healable,tough and highly stretchable ionic nanocomposite physical hydrogels[J].Soft Matter,2015,11:4235-4241.
[14] Hu X,Liang R,Li J,et al.Mechanically strong hydrogels achieved by designing homogeneous network structure[J].Mater Design,2019,163:107547.
[15] Shi F,Wang X,Guo R,et al.Highly stretchable and super tough nanocomposite physical hydrogels facilitated by coupling of intermolecular hydrogen bond and analogous chemical crosslinking of nanoparticle[J].Mater Chem B,2015,3:1187-1192.
[16] 唐群委,孙慧,敖海勇.高压缩强度聚丙烯酸盐/聚硅氧烷互穿网络水凝胶的制备[J].功能材料,2007,38(12):1993-1996.
[17] 张保东,姚新建,陈康.丙烯酸水凝胶的制备研究[J].周口师范学院学报,2009,26(2):73-75.
[18] 孟立山,李书静,新建.聚丙烯酸水凝胶的制备研究[J].应用化工,2014,43(2):222-224.
[19] 孙慧,林建明,唐群委.聚丙烯酸盐/淀粉半互穿网络水凝胶的两步水溶液合成及性能表征[J].华侨大学学报(自然科学版),2009,30(1):45-52.
[20] 李志军,杨东辉,陈金珠.微波辐照合成聚丙烯酸水凝胶及其性能研究[J].合成技术及应用,2006,21(2):20-22.
[21] Bao Y,Ma J,Li N.Synthesis and swelling behaviors of sodium carboxymethyl cellulose-g-poly(AA-co-AM-co-AMPS)/MMT superabsorbent hydrogel[J].Carbohyd Polym,2011,84:76-82.
[22] Wang W,Wang A.Nanocomposite of carboxymethyl cellulose and attapulgite as a novel pH-sensitive superabsorbent:synthesis,characterization and properties[J].Carbohyd Polym,2010,82:83-91.
Options
Outlines

/