Study on electrothermal property of rGO-CF conductive asphalt concrete

Expand
  • 1. School of Materials Science and Engineering,Chongqing Jiaotong University,Chongqing 400074;
    2. Sichuan Yanjiang Yijin Expressway Co.,Ltd.,Chengdu 610047

Received date: 2020-04-30

  Revised date: 2021-06-06

  Online published: 2021-09-07

Abstract

In order to prepare conductive asphalt concrete with good electrothermal performance,graphene-carbon fiber(rGO-CF) was used as the conductive phase material.The heat transfer principle of melting snow and ice of the concrete,and analyzed the calculation method of the heat generation and transfer during the snow melting and ice melting process.The Marshall test piece of the concrete was subjected to a temperature increase test,and the optimal rGO was determined according to the cost and the heating efficiency.The dosage was 0.5wt%,and the CF dosage was 0.3% of the aggregate mass.Under this dosage,the heating test and the snow-melting and ice-melting test were conducted on the concrete specimens.And the structure of the concrete was designed and analyzed its feasibility.

Cite this article

Huang Weirong, Yang Yuzhu, Song Peng, Guo Jiangchuan, Zhong Xiaoxia, He Xia . Study on electrothermal property of rGO-CF conductive asphalt concrete[J]. New Chemical Materials, 2021 , 49(8) : 269 -273 . DOI: 10.19817/j.cnki.issn 1006-3536.2021.08.058

References

[1] 傅沛兴.北京道路冬季融雪问题研究[J].市政技术,2001(4):54-59.
[2] 民政部门户网站.民政部通报近期低温雨雪冰冻灾情和救灾工作情况[EB/OL].[2008-02-24].http://www.mca.gov.cn/article/zwgk/mzyw/200802/20080200011960.shtml.
[3] 郭子仪,罗茂盛,范振华.道路除雪化冰技术研究[J].交通科技,2011(5):71-74.
[4] 徐令娜,赵庆新,李炜,等.碳纤维炭黑导电混凝土的接地特性研究[J].硅酸盐通报,2014,33(12):3366-3370.
[5] 欧阳平.三相导电混凝土强度及导电性能实验研究[J].混凝土与水泥制品,2015(9):14-19.
[6] 侯作富,李卓球,王建军.碳纤维导电混凝土融雪化冰的实验研究[J].混凝土与水泥制品,2004(5):42-44.
[7] 闫东星.导电沥青混凝土路用性能及力—电机敏特性研究[J].公路,2019,64(3):33-37.
[8] 项丽.三相导电沥青混合料的制备及性能研究[J].新型建筑材料,2017,44(7):137-140.
[9] 蔡亮.石墨碳纤维导电砼性能实验研究[J].公路与汽运,2017(6):84-86.
[10] 毕鹏.碳纤维增强沥青混凝土路用性能研究[J].中外公路,2019,39(1):226-229.
[11] Johnson D W,Dobson B P,Coleman K S.A manufacturing perspective on graphene dispersions[J].Current Opinion in Colloid & Interface Science,2015,20(5-6):367-382.
[12] He P,Sun J,Tian S,et al.Processable aqueous dispersions of graphene stabilized by graphene quantum dots[J].Chemistry of Materials,2015,27(1):218-226.
[13] 韩宝忠,韩宝国,王艳洁,等.测试导电复合材料直流电阻的四端电极法[J].哈尔滨工业大学学报,2010,42(10):1677-1680.
[14] Coquard R,Baillis D,Grigorova V,et al.Modelling of the conductive heat transfer through nano-structured porous silica materials[J].Journal of Non-Crystalline Solids,2013,363:103-115.
Options
Outlines

/