Research on preparation and application of multi band camouflage coating fabric

Expand
  • Shandong Transport Vocational College,Weifang 261000

Received date: 2019-12-10

  Revised date: 2020-11-07

  Online published: 2021-05-10

Abstract

The waterborne multi band camouflage coatings were prepared by using colored pigment,infrared low emissivity filler and waterborne polyurethane resin,and the visible/near infrared/thermal infrared camouflage coatings were prepared by the scraping process.The performance of The coated fabric such as infrared emissivity,spectral reflectance and specular gloss were characterized by dual band emissivity measurement,spectral reflectance tester,gloss meter testing methods.In addition,also on the physical and chemical properties of the coating were tested.The test results shown that the coating colors to meet the 《GJB 1082—1991 camouflage net》,near infrared reflectance spectral reflectance and the application background had the basic realization of the “metamerism” in 380~1100nm range,different color plaque emissivity gradient was more than 0.13.The effective gradient segmentation can being form in infrared imaging.The coating with application background had The fusion results,and visible/near infrared/thermal infrared stealth performance,the indicators reached the practical requirements.

Cite this article

Wu Yuyin, Bu Tiewei, Wang Zhen . Research on preparation and application of multi band camouflage coating fabric[J]. New Chemical Materials, 2021 , 49(3) : 248 -251 . DOI: 10.19817/j.cnki.issn 1006-3536.2021.03.055

References

[1] 成声月,刘朝辉,叶圣天,等.水性红外迷彩涂料的制备及其表征[J].红外与激光工程,2015,44(8):2298-2304.
[2] 唐继海,郑红川,杨骐.织物用水性多波段伪装印花涂料的研究与应用[J].表面技术,2016,45(6):161-166.
[3] 李永波,朱洪立,张宝琴,等.隐身涂料研究现状及发展趋势[J].材料导报,2015,29(26):358-360.
[4] 刘力,仵浩,张成涛,等.武器装备隐身与反隐身技术发展研究[J].情报交流,2014(4):80-82.
[5] 孙娜,胡传炘.伪装网表面工艺与结构的研究[J].中国表面工程,2004(4):46-48.
[6] 肖冰,李军念,陈秦,等.国外军用伪装技术的现状及发展趋势[J].四川兵工学报,2003,24(5):64-66.
[7] 吴进喜.红外伪装篷布的制备与测试[J].辽宁化工,2011,40(1):18-21.
[8] 郝立才,肖红,刘卫.防热红外侦视纺织品的研究进展[J].纺织学报,2014,35(7):158-164.
[9] 马丽芳,时家明,陈宗胜.绿色伪装涂料可见光和近红外反射率的探讨[J].红外技术,2010,32(5):267-272.
[10] 曹义,才鸿年,程海峰,等.林地型伪装网热红外发射率取值分析[J].激光与红外,2008,38(7):671-675.
[11] 曹义,才鸿年,程海峰,等.变形迷彩伪装的技术指标分析[J].红外技术,2008,30(2):118-122.
[12] 张辉,张建春.热红外隐身技术与人体伪装[J].上海纺织科技,2003,31(2):48-51.
[13] 叶圣天,成声月,刘潮辉等.8~14μm波段水性红外隐身涂料的研究[J].2016,45(2):204004-1-204004-6.
[14] 孙国亮.低发射率半导体颜料制备及其在伪装涂料中的应用研究[D].合肥:国防科学技术大学,2008.
[15] 孙瑞,何效凯,高萌,等.金属颜料对涂层可见光隐身性能的影响[J].涂料技术与文摘,2016,37(9):9-13.
[16] 孙瑞,何效凯,高萌,等.铝粉对红外隐身涂料的发射率影响研究[J].中国涂料,2016,31(6):58-62.
Options
Outlines

/