摘要
以三聚氰胺和多聚甲醛为原料,研究了溶剂组成、原料配比、反应时间和固含量等工艺条件对纺丝原液成纤性、纤维性能的影响。结果表明:在n(F)/n(M)=2.5、固含量60%、W(DMF)∶W(H2O)=1∶1、反应温度90℃、反应时间150min的工艺条件下制备的纺丝液,不添加助成纤剂即可直接湿法纺丝或干法纺丝,湿法纺丝工艺制备的纤维的断裂强度为1.36cN/dtex、断裂伸长率为8.65%,干法纺丝工艺制备的纤维的断裂强度为1.39cN/dtex、断裂伸长率为9.13%。
Abstract
Using melamine and paraformaldehyde as raw materials,the effects of technological conditions such as the solvent composition,the molar ratio of raw material,reaction time,solid content on the spinability of spinning dope and properties of fibers were studied.Results showed that under the conditions of n(F)/n(M)=2.5,60% of solid content,W(DMF)∶W(H2O)=1∶1,reaction temperature 90℃ and reaction time 150min,the spinning dope can be directly wet spun or dry spun without additive,the tensile strength and elongation at break of fiber of wet spun were 1.36cN/dtex and 8.65%,the tensile strength and elongation at break of fiber of dry spun were 1.39cN/dtex and 9.13%,respectively.
关键词
三聚氰胺纤维
/
助成纤剂
/
湿法纺丝
/
干法纺丝
Key words
melamine fiber
/
additive
/
wet spinning
/
dry spinning
无助成纤剂三聚氰胺纤维的研制[J].
化工新型材料, 2020, 48(6): 166-170 DOI:
[1] 姜刚.三聚氰胺纤维纺丝原液的制备[D].南京.南京理工大学,2003.
[2] Maity S,Singha K,夏于旻.三聚氰胺纤维的合成、性能和应用[J].国际纺织导报,2013,41(6):4.
[3] 汪家铭.三聚氰胺延伸产品蜜胺纤维的国内外技术进展[J].乙醛醋酸化工,2009(1):37-38.
[4] 李璐璐,杨彦功.三聚氰胺纤维发展现状及其改性进展[J].合成纤维工业,2014,37(2):56-59.
[5] 周迎松,于俊荣,沈燕,等.苯代三聚氰胺改性三聚氰胺甲醛/聚乙烯醇纤维的结构与性能[J].高分子材料科学与工程,2017,33(2):50-55.
[6] 毕慧平.三聚氰胺纤维改性及工艺研究[D].南京:南京理工大学,2004.
[7] 李东勇.三聚氰胺纤维的研制[D].北京:中国科学院大学,2017.
[8] 严翔,董书娟,许维星,等.MF树脂羟甲基化度对MF/PVA共混纤维结构及性能的影响[J].合成纤维工业,2013,36(1):20-23.
[9] 李曼曼.基于半互穿网络体系的三聚氰胺甲醛树脂改性研究[D].南京:南京理工大学,2015.
[10] 相益信.三聚氰胺甲醛树脂泡沫的研究[D].青岛:青岛科技大学,2011.