以金刚石为基体,经真空放电等离子体烧结(SPS),通过改进的Hummers法合成金刚石@氧化石墨烯(D@GO)中间体,利用NaBH4还原Pd2+生成钯纳米颗粒静电吸附于中间体后制备了金刚石@氧化石墨烯@钯纳米颗粒(D@GO@PdNPs)复合材料。通过一系列的表征技术对复合材料进行形貌结构、化学成分、分散度和热稳定性分析。结果表明:D@GO复合材料中的介孔结构成功地防止了钯纳米颗粒子的团聚,单晶钯纳米颗粒均匀分散在含有立方金刚石成分的GO片层结构上,当温度达到600℃时复合材料质量仍保持在72.5%。将合成的D@GO@PdNPs复合材料对硝基化合物进行催化实验,发现对4-硝基苯酚(4-NP)和2-硝基苯胺(2-NA)具有较高的催化效果,在连续8个催化循环后,催化4-NP的转化率仍然约95%,并且催化2-NA的转化率仍然约90%。
The diamond@graphene oxide(D@GO) intermediate was synthesized by the improved hummers method using diamond as the matrix through vacuum discharge plasma sintering(SPS).The diamond@oxide graphene@palladium nanoparticles(D@GO@PdNPs) composites were prepared by using NaBH4 to reduce Pd2+ to form palladium nanoparticles for electrostatic adsorption on intermediates.Through a series of characterization techniques,the morphology,chemical composition,dispersion and thermal stability of the materials were analyzed.The results showed that the mesoporous structure in the(D@GO) composite successfully prevented the reunification of palladium nanoparticles.Single crystal palladium nanoparticles were evenly dispersed in the graphene oxide sheet structure containing cubic diamond components,and the composite mass remained at 72.5% when the temperature reached 600℃.The catalytic experiments of the synthetic D@GOS@PdNPs nanocomposites on nitro compounds showed that the catalytic effects of 4-nitrophenol(4-NP) and 2-nitroaniline(2-NA) were high.After eight consecutive catalytic cycles,the conversion rate of catalytic 4-NP was still greater than 95%,and the conversion rate of catalytic 2-NA was still greater than 90%.
[1] Zhang Y J,He P Y,Chen H,et al.Development of an eco-efficient CaMoO4/electroconductive geopolymer composite for recycling silicomanganese slag and degradation of dye wastewater[J].J Clean Prod,2019,208:1476-1487.
[2] Kampouri S,Nguyen T N,Spodaryk M,et al.Concurrent photocatalytic hydrogen generation and dye degradation using MIL-125-NH2 under visible light irradiation[J].Adv Funct Mater,2018,28:1806368.
[3] Anasori B,Lukatskaya M R,Gogotsi Y.2D metal carbides and nitrides (MXenes) for energy storage[J].Nat Rev Mater,2017,2:16098.
[4] Esumi K,Isono R,Yoshimura T.Preparation of PAMAM- and PPI-metal (silver,platinum,and palladium) nanocomposites and their catalytic activities for reduction of 4-nitrophenol[J].Langmuir,2004,20:237-243.
[5] Pérez-Lorenzo M.Palladium nanoparticles as efficient catalysts for Suzuki cross-coupling reactions[J].J Phys Chem Lett,2012,3:167-174.
[6] Wang C,Yin J,Han S,et al.Preparation of palladium nanoparticles decorated polyethyleneimine/polycaprolactone composite fibers constructed by electrospinning with highly efficient and recyclable catalytic performances[J].Catalysts,2019,9(6):559.
[7] Domènech B,Muñoz M,Muraviev D N,et al.Polymer-stabilized palladium nanoparticles for catalytic membranes:ad hoc polymer fabrication[J].Nanoscale Res Lett,2011,6:406.
[8] Lin Y,Qiao Y,Wang Y,et al.Self-assembled laminated nanoribbon-directed synthesis of noble metallic nanoparticle-decorated silica nanotubes and their catalytic applications[J].J Mater Chem,2012,22:18314-18320.
[9] Hermans S,Bruyr V,Devillers M.A templating effect of carbon nanomaterials on the synthesis of Pd nanoparticles by covalent grafting onto surface O-groups[J].J Mater Chem,2012,22:14479-14486.
[10] Mourdikoudis S,Montes-García V,Rodal-Cedeira S,et al.Highly porous palladium nanodendrites:wet-chemical synthesis,electron tomography and catalytic activity[J].Dalton Trans,2019,48:3758-3767.
[11] Huang Q,Yu D,Xu B,et al.Nanotwinned diamond with unprecedented hardness and stability[J].Nature,2014,510(7504):250.
[12] Jiao T,Zhao H,Zhou J,et al.Self-assembly reduced graphene oxide nanosheet hydrogel fabrication by anchorage of chitosan/silver and its potential efficient application toward dye degradation for wastewater treatments[J].ACS Sustainable Chemistry & Engineering,2015,3(12):3130-3139.
[13] Zhao Y,Wang Y,Dong L,et al.Core-shell structural nanodiamond@TiN supported Pt nanoparticles as a highly efficient and stable electrocatalyst for direct methanol fuel cells[J].Electrochimica Acta,2014,148:8.
[14] Zhao X N,Ma K,Jiao T F,et al.Fabrication of hierarchical layer-by-layer assembled diamond-based core-shell nanocomposites as highly efficient dye absorbents for wastewater treatment[J].Scientific Reports,2017,7:44076.
[15] Zhao X,Jiao T,Xing R,et al.Preparation of diamond-based AuNP-modified nanocomposites with elevated catalytic performances[J].RSC Advances,2017,7(79):49923-49930.
[16] Ji Y,Ghosh K,Shu X Z,et al.Electrospun three-dimensional hyaluronic acid nanofibrous scaffolds[J].Biomaterials,2006,27:3782-3792.
[17] Sang Y T,Cui Y Q,Li Z,et al.Electrochemical reaction of nitrobenzene and its derivatives on glassy carbon electrode modified with MnFe2O4 colloid nanocrystal assemblies[J].Sens Actuators B,2016,234:46-52.
PDF
(2692KB)