摘要
研究了膨化温度、膨化时间对可膨胀石墨膨化体积及氧化失重率的影响,基于正交试验方法研究了温度对石墨线性能的影响,通过扫描电镜观察膨胀石墨与玻璃纤维以及粘结物界面在高温灼烧后的变化,通过研究得出随着灼烧温度的升高,石墨线的断裂负荷逐渐减小,耐温失量和直流电阻变化率均在标准范围内;当灼烧时间较短时,同时温度在750℃下,石墨线各项性能的变化率均在10%以内,可以得出,在断路器防护动作时间内,防雷接地用石墨基柔性接地体在遇到短路故障大电流作用下其耐受温度可达到750℃。研究结果对制备导电性能良好的石墨基柔性接地材料,提高石墨基柔性接地体导电、大电流耐受性能有指导意义。
Abstract
The effects of expansion temperature and expansion time on the expansion volume and oxidation weight loss rate of expandable graphite were studied.Based on the orthogonal test method,the effects of temperature on the properties of graphite line were studied.The changes of the interface between expanded graphite,glass fiber(GF) and binder after high temperature burning were characterized by SEM.The results shown that with the increase of burning temperature,the breaking load of the line decreased gradually.The temperature loss resistance and DC resistance change rate were within the standard range.When the burning time was short and the temperature was at 750℃,the change rate of each performance of the graphite line was within 10%.It can be concluded that within the protective action time of the circuit breaker,the withstand temperature of the graphite based flexible grounding body for lightning protection can be Up to 750℃.The results were of great significance for the preparation of graphite based flexible grounding materials with good conductivity and the improvement of the conductivity and high current withstand performance of graphite based flexible grounding materials.
关键词
石墨基柔性接地材料
/
导电性
/
工艺参数
/
石墨玻纤复合线
/
电阻率
Key words
graphite based flexible grounding material
/
conductivity
/
process parameter
/
flexible graphite line
/
resistivity
温度对防雷接地用石墨玻纤复合材料性能的影响[J].
化工新型材料, 2020, 48(4): 125-128 DOI:
[1] 谢苏江.柔性石墨及其复合密封材料的研究和发展[J].化工设备与防护,2004(4):50-52.
[2] 吴如品.柔性石墨复合材料的制备研究[D].南京:理工大学,2012.
[3] 任京成,沈万慈.柔性石墨材料和膨胀石墨材料的现状及发展趋势[J].非金属矿,1999(5):5-7.
[4] 康飞宇.柔性石墨的生产和发展[J].新型炭材料,1993(3):15-17.
[5] 苏晖.柔性石墨导热性的研究[D].武汉:武汉理工大学,2010.
[6] 张国良.柔性石墨高温导电性能的应用[J].中国设备工程,1991(9):32-32.
[7] 李喆,谭力,张坤,等.柔性石墨复合接地材料在输电线路杆塔接地网中的应用研究[J].国网技术学院学报,2017,20(4):4-10.
[8] 胡元潮,阮江军,龚若涵,等.柔性石墨复合接地材料及其在输电线路杆塔接地网中的应用[J].电网技术,2014,38(10):2851-2857.
[9] 姜海生.石墨型接地装置在架空输电线路中的应用[J].中国高新技术企业,2013(6):100-102.
[10] 韦扬志,丁卫东,张国锋,等.石墨基柔性接地材料及其在南方复杂地质环境防雷接地的应用[J].化工新型材料,2018,46(12):252-255.
[11] 冯健中,游长江,鲁光,等.不饱和聚酯/玻璃纤维复合材料的研究[J].广州化学,2006,31(3):45-56.
[12] 谢苏江,蔡仁良.纤维增强柔性石墨——橡胶密封材料的制备及性能研究[J].新型炭材料,1997(4):56-60.
[13] 林海丹,董巍,列剑平,等.复合型硅烷偶联剂的制备及表征[J].分子科学学报,2018,34(6):486-489.
[14] 张士华,陈光,崔崇,等.偶联剂处理对玻璃纤维/尼龙复合材料力学性能的影响[J].复合材料学报,2006,23(3):31-36.