以苯乙烯、丙烯酸为单体,引入疏水性荧光染料罗丹明6G(Rh6G),采用微乳聚合法制备羧基聚苯乙烯荧光微球,并分析了表面活性剂、引发剂、丙烯酸用量对产物粒径分布的影响,考察了羧基聚苯乙烯荧光微球的浓度对荧光强度的影响。通过粒度分析仪、扫描电子显微镜、红外光谱仪、紫外吸收光谱以及荧光光谱仪对样品的纳米特性、形貌、结构和荧光性能进行了表征。结果表明,用微乳聚合法制备出50～250nm的羧基聚苯乙烯荧光微球,粒径均一且呈单分散性。紫外光谱图测试表明,在533nm左右有吸收峰。荧光光谱测试表明,羧基功能化的荧光聚苯乙烯微球浓度≤0.01%,其荧光最大激发峰为527nm,最大发射峰在555nm处;浓度高于0.01%时,荧光光谱出现红移,且荧光强度减弱。
Carboxylate-modified polystyrene(PS) fluorescent microspheres were synthesised by microemulsion polymerization using rhodamine 6G (Rh6G) as hydrophobic fluorescent dye,acrylic acid and styrene as monomer.The effects of surfactant,initiator and acrylic acid monomer on the particle size distribution were analyzed.The structure,morphology and performance of carboxylate-modified PS fluorescent microspheres were characterized by DLS,SEM,FT-IR,UV and fluorescence spectrum.The microspheres with the size from 50nm to 250nm were obtained.The absorption peak was around 533nm by UV spectrogram.Fluorescence spectra results showed that the concentration of the microspheres had an important effect on the fluorescence intensity.When the concentration was no more than 0.01%,the maximum fluorescence excitation peak was 527nm,and the maximum emission peak was 555nm.When the concentration was above 0.01%,the fluorescence spectrum was redshift,and the fluorescence intensity was decreased.
[1] Rubio-Rios A,Aguilar-Castillo B A,Flores-Gallardo S,et al.Effect of synthesis variables on the fluorescence properties of CdSe-polystyrene latexes[J].Journal of Polymer Research,2012,19(3):9833.
[2] 熊大伟,姚金水,陈淑祥,等.连续法制备单分散聚苯乙烯微球及粒径影响因素的研究[J].塑料工业,2011,39(11):24-27.
[3] 聂微,王颜红,张红,等.聚苯乙烯荧光微球的制备及性能考察[J].沈阳药科大学学报,2013,35(5):329-334.
[4] Chen R,Li H,Zhang,H,et al.Development of a lateral flow fluorescent microsphere immunoassay for the determination of sulfamethazine in milk[J].Analytical and Bioanalytical Chemistry,2013,405(21):6783-6789.
[5] 张小燕,周齐洋.彩色羧基荧光微球的制备[J].中国医疗器械信息,2017,23(9):45-48.
[6] Leng L,Li Y,Liu Y Y,et al.Fluorescent determination of mercury(ⅱ) using rhodamine B immobilized on polystyrene microspheres[J].Analytical Letters,2017,50(18):2944-2958.
[7] 刘清浩,郭金春,段鹏,等.一步制备羧基聚苯乙烯共聚荧光微球及其表征[J].化学与黏合,2015,37(6):429-433.
[8] Zhao Y,Chen W,Peng C F,et al.Facile preparation of fluorescence-encoded microspheres based on microfluidic system[J].Journal of Colloid and Interface Science,2010,353(2):337-342.
[9] Qu J B,Li S H,Xu Y L,et al.Inherently fluorescent polystyrene microspheres as a fluorescent probe for highly sensitive determination of chromium(Ⅵ) and mercury(Ⅱ) ions[J].Sensors and Actuators B-Chemical,2018,27:127-134.
[10] 赵春山,毛娇,张鸿林,等.苯乙烯共聚荧光微球的制备[J].化学与黏合,2014,36(2):115-117.
[11] Li J,Li X,Wang C,et al.Preparation and properties of CsVO3/polymercompositematerial[J].Journal of Functional Materials,2014,45(3):106-109.
[12] Tang B,Li H.Separation and quantitation of isomeric caffeoylquinic acids in honeysuckle products by low-pH microemulsion electro-kinetic chromatography using tartrate as a chiral selector[J].Analytical Methods,2016,8,189-196.
[13] 汪雨,刘丹丹,张洁洁,等.羧基聚苯乙烯荧光微球的制备及其溶胀机制[J].功能材料,2017,6(48):06193-06198.
[14] 朱佳媚.一种荧光共聚物微球及其制备方法:中国,CN201711449333.2[P].2017-12-28.
[15] 盛扬,段宗权,张嵘.一种纳米荧光微球的制备方法:中国,CN201711380012.1[P].2016-12-13.
[16] 陈苏,朱亮亮,王彩凤.聚合物荧光微球的制备方法:中国,CN201310219573.9[P].2013-06-03.
[17] 朱雯.单分散聚苯乙烯微球的制备与表征[J].江苏技术师范学院学报,2012,18(2):55-58.
[18] 郭金春,刘清浩,孟越,等.功能化聚苯乙烯共聚荧光微球的制备与表征[J].高分子材料科学与工程,2013,29(4):145-151.
[19] 于娜,刘崇举,单妍,等.尺寸可控的单分散聚苯乙烯微球的制备[J].青岛科技大学学报(自然科学版),2010,31(4):351-360.
[20] Liand Z,Almeide E.Paper based point-of-care testing disc for multiplex whole cell bacteria analysis[J].Biosensors and Bioelectronics,2011,26:4342-4348.
[21] Verena H,Katharina L.Preparation of fluorescent carboxyl and amino functionalized polystyrene particles by miniemulsion polymerization as markers for cells[J].Macromolecular Chemistry Physics,2005,206:2440-2449.
[22] 何锡文,史长虹,张贵珠,等.罗丹明6G的溶液状态和荧光特性的研究[J].分析化学,1993,21(9):1008-1012.
[23] 张瑞华,崔建升,孟素英.罗丹明6G荧光特性及其在荧光淬灭法中的应用[J].河北工业科技,2014,31(3):252-261.
基金资助
国家自然科学基金项目(21401051);湖北省自然科学基金(2014CFB595)
PDF
(2627KB)