剪切增稠液流变性能的影响因素研究

^2*

作者信息 +

Influence factor of rheological property on STF

Chen Hongxia¹, Cao Haijian², Huang Xiaomei²

Author information +

文章历史 +

Received		Published
2018-06-01		2019-11-20
Issue Date	Revised Date
2019-12-04	2018-06-01

PDF (2155K)

摘要

分别以直径85nm、700nm的纳米SiO₂粒子作为分散相,PEG200、PEG400、PEG600作为分散介质,通过超声波震荡和机械搅拌的方式制备不同黏度的剪切增稠液(STF)。采用JEM-2100HR型透射电镜观察纳米SiO₂粒子的外观形貌,利用Nano-ZS90型粒径分析仪测试纳米SiO₂粒子的直径及分布,采用MCR302型流变仪测试STF的稳态流变性能。结果表明,直径85nm的纳米SiO₂粒子易团聚,直径700nm的纳米SiO₂粒子不易团聚。在一定剪切速率范围内,STF体系的黏度随着剪切速率的增加呈现出“先变稀再增稠”的现象。STF体系的初始黏度、突变黏度、最大黏度均随着纳米SiO₂粒子质量分数或PEG分子量的增加而增加;STF体系的突变剪切速率则随着纳米SiO₂粒子质量分数或PEG分子量的增加而下降。

Abstract

Nano silica particles (nano-SiO₂ particles) with diameter of 85nm and 700nm used as the dispersed phase and PEG 200,PEG400 and PEG600 used as the dispersion medium,respectively.Different system Shear thickening fluid (STF) were prepared by method of mechanical stirring and ultrasonic shock.The morphology and agglomeration of nano-SiO₂ particles were observed by JEM-2100HR transmission electron microscope.Particle diameter and distribution of nano-SiO₂ particles were tested by Nano-ZS90 grain size analyzer.And steady rheological properties of STF were tested by MCR302 rheometer.The results shown that the agglomeration of nano-SiO₂ particles with diameter of 85nm was obvious,and net structures were observed too,while that of 700nm was not obvious.In certain range of shear rate,viscosity of STF appeared the phenomenon of first thinning then thickening with the increase of shear rate.Initial viscosity,mutation viscosity and biggest viscosity of STF all increased,while mutation shear rate decreased with the increase of nano-SiO₂ particles' concentration or PEG's molecular weight.

关键词

剪切增稠液 / 分散相 / 分散介质 / 流变性能 / 剪切速率 / 剪切黏度

Key words

shear thickening fluid (STF) / dispersed phase / dispersion medium / rheological property / shear rate / shear viscosity

引用本文

引用格式 ▾

剪切增稠液流变性能的影响因素研究[J]. 化工新型材料, 2019, 47(11): 137-140 DOI:

登录浏览全文

4963

注册一个新账户忘记密码

参考文献

原文顺序 | 出版日期 | 本文引用

[1] Hassan T A,Rangari V K,Jcclani S.Sonochcmical synthesis and rhcological properties of shear thickening silica dispersions[J].Ultrasonics Sonochcmistry,2010,17(5):917-952.
[2] Yu K J,Cao H J,Qian K,et al.Synthesis and stab resistance of shear thickening fluid (STF) impregnated glass fabric composites[J].Fibres & Textiles in Eastern Europe,2012,20(6A):126-128.
[3] Lomakin E V,Mossakovsky P A,Bragov A M,et al.Investigation of impact resistance of multilayered woven composite barrier impregnated with the shear thickening fluid[J].Archive of Applied Mechanics,2011,81(12):2007-2020.
[4] Li X,Cao H L,Gao S,et al.Preparation of body armour material of Kevlar fabric treated with colloidal silica nanocomposite[J].Plastics,Rubber and Composites,2008,37(5-6):223-226.
[5] Lee Y S,Wagner N J.Dynamic properties of shear thickening colloidal[J].Rheologica Acta,2003,42(3):199-208.
[6] 陈潜,何倩云,刘梅,等.剪切增稠液的力学性能与机理[J].固体力学学报,2016,37(6):518-537.
[7] 吴磊,沈谈笑,曾栌贤,等.超声法制备剪切增稠液及其稳态流变行为的研究[J].合成纤维工业,2016,39(3):16-20.
[8] 熊芳,周大利,顾建文,等.Kevlar纤维布/剪切增稠液复合材料制备及防刺性能[J].四川兵工学报,2013,34(4):130-133.
[9] 景晓颖,陆振乾,孙宝忠.剪切增稠液流变性能及其复合材料动态冲击压缩性能[J].东华大学学报(自然科学版),2014,40(3):253-257.
[10] Egres R G,Wagner N J.The rheology and microstructure of acicular preciptated calcium carbonatecolloidal suspensions through the shear thickening transition[J].Journal of Rhrology,2005,49(3):719-746.
[11] 王天坤,俞科静,钱坤,等.2D、3D织物结构对STF/UHMWPE复合材料高速冲击性能影响的研究[J].化工新型材料,2016,44(8):108-109.
[12] Lomakin E V,Mossakovsky P A,Bragov A M,et al.Investigation of impact resistance of multilayered woven composite barrier impregnated with the shear thickening fluid[J].Archive of Applied Mechanics,2011,81(12):2007-2020.