将退役复合绝缘子芯棒粉碎,采用硅烷偶联剂对芯棒粉末进行表面改性,再将其同环氧树脂、玻璃纤维共混,通过高温模压的方式制备了改性芯棒粉末掺杂的玻璃纤维增强环氧树脂复合材料,并考察了改性粉末添加量对复合材料性能的影响。结果表明:该复合材料具有良好的力学性能及阻燃性能,可继续制成芯棒部件应用于复合绝缘子中。
The decommissioned composite insulator rod was comminuted and used the silane coupling agent to modify the surface of the mandrel powder,and then blended the powder with the epoxy resin and glass fiber.Glass fiber reinforced epoxy resin composites doped with modified mandrel powder were prepared by the way of high temperature molding.The effects of the amount of modified powder on the properties of the composites were also investigated.The results shown that the composites had good mechanical and flame retardant properties,and it can continue to be mandrel components in composite insulators.
[1] 孙曼灵.环氧树脂应用原理与技术[M].北京:机械工业出版社,2002,88-97.
[2] 李桂林.环氧树脂与环氧涂料[M].北京:化学工业出版社,2003,456-478.
[3] 曹文斌.环氧树脂绝缘件在电力设备中的应用[J].电器制造,200912):28-29.
[4] 王醉寒.玻璃纤维布及碳纤维布增强酚醛环氧树脂复合材料性能研究[D].武汉:武汉工程大学,2015.
[5] 王丽雪,尹志娟,刘海鸥.玻璃纤维增强环氧树脂单向复合材料力学性能分析[J].黑龙江工程学院学报,2009,23(3):73-74.
[6] 张硕,姚宁,吴继平,等.玻璃纤维增强环氧树脂复合材料的力学性能[J].电工材料,2016(1):11-14.
[7] 尹志娟,王丽雪,姜珊.玻璃纤维增强环氧树脂基复合材料的低温性能研究[J].黑龙江工程学院学报,2010,24(1):50-52.
[8] 邵水才,石程程,王知,等.短切玻璃纤维增强环氧树脂胶粘剂的耐温性能研究[J].中国胶粘剂,2014,23(7):17-20.
[9] 皇志富.氧化铝颗粒增强改性环氧树脂基复合材料的制备及其应用研究[D].昆明:昆明理工大学,2001.
[10] 王胜国.环氧树脂颗粒相增韧与均相增韧的研究及比较[D].上海:复旦大学,2002.
基金资助
吉林省电力有限公司招标项目(SGTYHT/15-JS-194)
PDF
(1092KB)