针对环氧沥青材料在钢桥面铺装中的应用,制备了增韧型环氧沥青混合料。测试了树脂用量对沥青混合料马歇尔稳定度和施工可操作时间的影响,并评价了不同树脂用量下增韧型环氧沥青混合料的高温稳定性、低温抗裂性、水稳定性能及抗疲劳性能。结果表明:增韧型环氧树脂用量对沥青混合料的性能有显著影响,当其用量为40%时,增韧型环氧沥青混合料具有优异的路用性能,且施工可操作时间较长。增韧型环氧沥青混合料能够满足钢桥面铺装对材料性能的要求。
For the application of epoxy asphalt materials in steel bridge deck pavement,toughened epoxy asphalt mixture was prepared.The effects of toughened epoxy resin dosages on marshall stability and operating time of asphalt mixture were tested,and high temperature stability,low temperature anti-cracking performance,water stability and fatigue performance of toughened epoxy asphalt mixture under different resin dosages were evaluated.The results showed that toughened epoxy resin dosage had a significant effect on asphalt mixture performance.When resin dosage was 40%,toughened epoxy asphalt mixture had excellent pavement performance,and its had a longer operating time.The toughened epoxy asphalt mixture could meet the material performance requirements of steel bridge deck pavement.
[1] Lu Q,Bors J.Alternate uses of epoxy asphalt on bridge decks and roadways[J].Construction & Building Materials,2015,78:18-25.
[2] Qian Z D,Chen C,Jiang C L,et al.Development of a lightweight epoxy asphalt mixture for bridge decks[J].Construction & Building Materials,2013,48(19):516-520.
[3] 刘建明,闫亚鹏,李旭,等.钢桥面铺装环氧树脂沥青混合料性能研究[J].中外公路,2013,33(3):296-299.
[4] 丛培良,刘建飞,赵志强,等.混凝土桥面铺装用环氧沥青的制备与性能研究[J].郑州大学学报(工学版),2014,35(6):78-81.
[5] Xu P J,Zhu X T,Cong P L,et al.Modification of alkyl group terminated hyperbranched polyester on paving epoxy asphalt[J].Construction & Building Materials,2018,165:295-302.
[6] Yang J,Lu H Z,Yuan D Q,et al.Evaluation of modification effect epoxy resin based on performance of asphalt mixtures[J].Journal of Southeast University (English Edition),2007,23(1):122-126.
[7] Hao Z H,Li L,Liao X,et al.Preparation and toughening performance investigation of epoxy resins containing carbon nanotubes modified with hyperbranched polyester[J].Polymer Bulletin,2017(4):1-14.
[8] 陈利东,李璐,郝增恒.聚氨酯-环氧树脂复合改性沥青混合料的研究[J].公路工程,2013,38(2):214-218.
[9] 张争奇,张苛,李志宏,等.环氧沥青混凝土增柔增韧改性技术[J].长安大学学报(自然科学版),2015,35(1):1-7.
[10] 钱振东,王睿,陈团结.橡胶粉掺量对环氧沥青及其混合料性能的影响[J].建筑材料学报,2014,17(2):331-335.
[11] 丛培良,余剑英,吴少鹏.环氧沥青及其混合料性能的影响因素[J].武汉理工大学学报,2009(19):7-10.
[12] 郝增恒,李璐,盛兴跃,等.基于高温固化的环氧沥青开发及性能表征[J].化工新型材料,2017,45(10):208-210,214.
[13] 王志祥,吴传海,许新权.预拌碎石对GMA浇注式沥青混凝土高温性能的影响[J].公路交通科技,2018(1):14-21.
[14] 周晓华,宗海,王晓,等.环氧沥青混合料低温性能研究[J].公路,2006(1):179-182.
基金资助
重庆市杰出青年基金(cstc2014jcyjjq30002);重庆市科技创新领军人才支持计划(CSTCCXLJRC201720);国家自然科学基金(51702282)
PDF
(1387KB)