以海南椰壳纤维为原料,采用浸渍法活化、管式炉炭化等过程制备椰壳活性炭,然后以浓硫酸为磺化剂,磺化制备了具有多孔特征的椰壳炭固体酸。并对制得的椰壳炭固体酸进行了结构表征。通过乙酸和正丁醇的酯化反应,对催化剂的性能进行了测试,考察了催化剂制备过程中物料比、灼烧温度、炭化时间、磺化剂用量等因素对催化反应的影响。结果表明:在椰壳纤维原料与活化剂氢氧化钾的质量配合比为1∶1,炭化温度为450℃,炭化时间为2h,椰壳活性炭与磺化剂投量配合比为1g∶20mL,磺化时间为2h条件下,制得的磺化椰壳固体酸的催化性能最好,并在催化乙酸与正丁醇的酯化反应中2h转化率达到96.6%。
Abstract
Carbon-based solid acid catalysts were prepared by sulfonation of porous coconut shell carbon which was prepared from coconut shell fiber by impregnation-activation and calcination in tube furnace.The structures of the solid acids were characterized by IR,XRD,SEM and so on.The performance of catalysts were verified by esterification of acetic acid and n-butanol,and the effects of the procedure such as material ratio,calcination temperature,calcination time,amount of sulfonating agent and sulfonation time on the esterification were investigated.It's shown when the ratio of coconut shell fiber material and activator KOH was 1∶1,the carbonization temperature of 450℃,the calcination time was 2h,the coconut shell activated carbon with a sulfonating agent dosage was 1g∶20mL,sulfonation time was 2h,the conversion rate in the catalytic esterification of acetic acid and butanol reached 96.6%.
关键词
椰壳纤维
/
活性炭
/
固体酸催化剂
/
酯化反应
Key words
coconut shell fiber
/
activated carbon
/
solid acid catalyst
/
esterification
磺化椰壳炭固体酸催化剂的制备及催化酯化反应研究[J].
化工新型材料, 2019, 47(8): 181-184 DOI:
[1] Chen W H,Chen J C,Liu J C,et al.Assessment of the practices and contributions of China's green industry to the socio-economic development[J].J Clean Prod,2017,153:648-656.
[2] Fujii H.Decomposition analysis of green chemical technology inventions from 1971 to 2010 in Japan[J].J Clean Prod,2016,112:4835-4843.
[3] 刘猛帅,徐智策,赵地顺,等.离子液体催化合成丁二酸二甲酯[J].化工学报,2012,63(4):1089-1094.
[4] 张凤媛.SO2-4-TiO2-SiO2固体超强酸及其催化酯化反应的研究[D].兰州:兰州大学,2006.
[5] Gandhi N N,Patil N S,Sawant S B,et al.Lipasecatalyzed esterification[J].Catal Rev,2000,42:439-480.
[6] 董维华.固体酸催化剂研究进展[J].广州化工,2015,43(18):7-8.
[7] 白浩,刘学军,孙群宁.固体酸催化剂的研究进展[J].广东化工,2013,40(23):110-112.
[8] 李虎,杨松,张秋云.制备生物柴油的固体酸催化剂研究进展[J].化工进展,2013,32(3):575-583.
[9] Abdullah A Z,Razali N.Production of lactic acid from glycerol via chemical conversion using solid catalyst:a review[J].Appl Catal A-Gen,2017,543:234-246.
[10] 陈洁,蒋剑春,徐俊明.催化酯化反应中固体酸催化剂研究进展[J].精细石油化工进展,2009,10(3):32-37.
[11] 徐琼.生物质炭磺酸的制备及催化性能研究[D].长沙:湖南师范大学,2008.
[12] Goodwin J G,Lu C Q,Lopez D E,et al.Activation and deactivation characteristics of sulfonated carbon catalysts[J].J Catal,2008,254,332-338.
[13] 乌日娜.生物质炭基固体酸催化剂的制备及催化性能研究[D].大连:大连理工大学,2009.
[14] 余鹰,周文富.生物质竹屑活性炭磺酸官能化固体酸催化剂的制备[J].化学与生物工程,2010,27(2):83-86.
[15] 陈纪忠,沈忠权,余锡孟.新型磺化竹炭材料催化酯化反应[J].化工学报,2015,66(8):3072-3077.
[16] 马常耕,苏晓华.生物质能源概述[J].世界林业研究,2005,18(6):32-38.
[17] Amirantea R,Distasoa E,La Scalab M,et al.Experimental prototype development and performance analysis of a small-scale combined cycle for energy generation from biomass[J].Energy Procedia,2017,126:659-666.
基金资助
海南省自然科学基金项目(20162017);海南省高等学校教育教学改革研究项目(Hnjg2016ZD-5);海南大学教育教学研究课题立项项目(hdjy1613);海南大学大学生创新创业基金资助项目(Hdcxcyxm201703)