摘要
以高分子量聚丙烯腈(PAN)聚合物为研究对象,根据正交试验设计方案,采用NaOH碱法水解工艺,制备出了具有不同絮凝能力的絮凝剂。从正交试验结果得到影响PAN水解产物絮凝性的强弱顺序为:碱度>温度>喂料配比>时间。采用影响显著性最明显的因素制得的PAN水解产物具有较好的絮凝效果,且其红外谱图与市售聚丙烯酰胺(PAM)具有较好的相似性。
Abstract
Using NaOH as reaction catalyst,high molecular weight polyacrylonitrile (PAN) copolymer was hydrolysized with orthogonal experiment method.And the flocculants with different flocculating ability were prepared.The results of orthogonal experiment showed that the order of influencing the flocculation of PAN hydrolysate was [NaOH]>temperature>feed ratio>time.The PAN hydrolysate prepared by the most significant factors had the better flocculation effect,whose FT-IR spectra was similar to the commercial polyacrylamide (PAM).
关键词
高分子量聚丙烯腈
/
碱法水解
/
絮凝
/
正交试验
Key words
high molecular weight polyacrylonitrile
/
alkali hydrolysis
/
flocculating
/
orthogonal experiment
高分子量聚丙烯腈的碱法水解工艺研究[J].
化工新型材料, 2019, 47(7): 187-189 DOI:
[1] 李海静.絮凝剂处理污水的现状及对策研究[J].环境保护与循环经济,2012(6):53-56.
[2] 韩晶,张小燕,余中.我国水处理剂的研究与应用现状展望[J].精细石油化工,2001(3):38-43.
[3] 徐强.水解条件对聚丙烯腈水解产物结构和性能的影响[D].济南:山东轻工业学院,2010.
[4] 范福海,郝艳玲,张虹.水解腈纶废丝制备吸水性树脂[J].应用化工,2008,37(5):523-525.
[5] 范福海,郝艳玲.腈纶废丝改性水解物的制备及其絮凝效果[J].应用化工,2004,33(4):28-30.
[6] 董秀延,范福海,郝艳玲.对腈纶废丝碱法水解产物接枝后絮凝性能的研究[J].应用化工,2009,38(4):551-552.
[7] 中华人民共和国石油天然气行业标准.SY/T 5233—2014钻井液用絮凝剂评价程序[S].北京:国家能源局,2014-10-15.
[8] 李留忠,于元章,李永华,等.废腈纶水解物的制备与表征[J].高分子材料科学与工程,2003,19(4):169-172.
[9] 赵亚奇.水相沉淀聚合工艺制备碳纤维用高分子量聚丙烯腈[D].济南:山东大学,2010.
基金资助
河南省高等学校重点科研项目计划(15A430017)