摘要
采用硅烷偶联剂KH550对石墨烯进行接枝改性,采用溶液共混法制备改性石墨烯/热塑性聚氨酯(TPU)导电复合材料,并对复合材料的微观结构、电学性能及压阻特性进行测量和分析。研究表明:硅烷偶联剂KH550成功接枝至石墨烯的表面,分散性较好,复合材料的渗流阈值在石墨烯添加量为5%(wt,质量分数)附近,在石墨烯添加量为7%(wt,质量分数),压力为1.0MPa条件下,石墨烯/热塑性聚氨酯复合材料的均一化电阻为1.55,循环5次后的电阻为390Ω,具有较好的压阻重复性。
Abstract
graphene was modified by KH550,the conductive graphene/TPU composite thin films were prepared by solution mixing method.The microstructure,electrical properties and piezoresistive characteristics of the film were measured and analyzed.The results showed that silane coupling agent was successfully grafted onto the surface of graphene,The modified graphene can be uniformly dispersed into the TPU matrix.The percolation threshold of the composite was near 5wt%.When the graphene mass content was 7wt%,under the pressure of 1.0MPa,the uniform resistance of composite was 1.55,the resistance was of composites 390Ω after being circulated for 5 times.And composites showed good piezoresistive repeatability.
关键词
石墨烯
/
热塑性聚氨酯
/
压阻特性
Key words
graphene
/
thermoplastic polyurethane
/
piezoresistive property
石墨烯/热塑性聚氨酯导电复合材料的制备及压阻特性研究[J].
化工新型材料, 2019, 47(7): 64-67 DOI:
[1] 王钰.导电橡胶柔性传感器压力/温度特性研究[D].昆明:昆明理工大学,2013.
[2] 陈祥林,丁天怀,黄毅平.新型接近式柔性电祸流阵列传感器系统[J].机械工程学报,2006,42(8):150-153.
[3] Périé T,Brosse A C,Tencé-Girault S,et al.Mechanical and electrical properties of multi walled carbon nanotube/ABC block terpolymer composites[J].Carbon,2012,50(8):2918-2928.
[4] 黄英.基于压力敏感导电橡胶的柔性多维阵列触觉传感器研究[D].合肥:合肥工业大学,2008.
[5] 陈铃.硅橡胶/纳米石墨薄片复合材料在压力场作用下电导非线性研究[D].泉州:华侨大学,2007.
[6] 林森,孙仕勇,申珂璇.石墨烯及其纳米复合材料的制备与应用研究[J].人工晶体学报,2017,46(6):1117-1121.
[7] 褚文娟.高强TPEE/TPU塑料合金的制备及结构与性能研究[D].北京:北京工业大学,2010.
[8] Vicentini D S,Barra G M O,Bertolino J R,et al.Polyaniline/thermoplastic polyurethane blends:preparation and evaluation of electrical conductivity[J].European Polymer Journal,2007,43(10):4565-4572.
[9] 黄建业.聚氨酯/多壁碳纳米管定向微纳纤维丝压敏特性研究[D].杭州:浙江大学,2012.
[10] 樊志敏,郑玉婴,刘先斌,等.功能氧化石墨烯/热塑性聚氨酯复合材料薄膜的制备及阻隔性能[J].复合材料学报,2015,32(3):705-711.
[11] Shin M K,Oh J,Lima M,et al.Elastomeric conductive composites based on carbon nanotube forests[J].Advanced Materials,2010,22(24):2663-2667.
[12] Hou Y,Wang D,Zhang X M,et al.Positive piezoresistive behavior of electrically conductive alkyl-functionalized graphene/polydimethylsilicone nanocomposites[J].Journal of Materials Chemistry C,2013,1(3):515-521.
[13] 马文石,邓帮君.纳米功能化石墨烯/室温硫化硅橡胶复合材料的制备与表征[J].复合材料学报,2011,28(4):40-45.
[14] 江美娟.碳纳米管/硅橡胶复合材料介电与压阻性能研究[D].北京:北京化工大学,2009.
[15] Sheng P,Sichel E K,Gittleman J I.Fluctuation-induced tunneling conduction in carbon-polyvinylchloride composites[J].Physical Review Letters,1978,40(18):1197-1202.