The reduced graphene oxide/polyaniline/mangano-manganic oxide (RGO/PANI/Mn3O4) composite nanomaterial was successfully prepared.The graphene oxide/polyaniline (GO/PANI) was prepared by chemical oxidative polymerization by using APS as oxidizing agent firstly,then the RGO/PANI/Mn3O4 was obtained by hydrothermal treatment of GO/PANI and Mn(Ac)2·4H2O.The morphology and structure of the materials were characterized and the results showed that Mn3O4 nanoparticles were grown on RGO layer uniformly with PANI as conducting connection layer.
[1] Sun J,Zhang Q C,Wang X N,et al.Constructing hierarchical dandelion-like molybdenum-nickel-cobalt ternary oxide nanowire arrays on carbon nanotube fiber for high performance wearable fiber-shaped asymmetric supercapacitors[J].J Mater Chem A,2017,5(40):21153-21160.
[2] Chen W W,He P,Sun S,et al.Smart electronic textiles[J].Angew Chem Int Ed,2016,55(21):6140-6169.
[3] Yin Z G,Zheng Q D.Controlled synthesis and energy applications of one-dimensional conducting polymer nanostructures:an overview[J].Adv Energy Mater,2012,2:179-218.
[4] Wang G,Tang Q,Bao H,et al.Synthesis of hierarchical sulfonated graphene/MnO2/polyaniline ternary composite and its improved electrochemical performance[J].J Power Sources,2013,241:231-238.
[5] 姚添元.氧化石墨烯/锰氧化物/聚苯胺三元复合电极材料的制备及性能研究[D].南京:南京理工大学,2014.
[6] Yu L,Gan M Y,Ma L.Facile synthesis of MnO2/polyaniline nanorod arrays based on graphene and its electrochemical performance[J].Synth Met,2014,198:167-174.
[7] Kovtyukhova N,Ollivier P,Martin B,et al.Layer-by-layer assembly of ultrathin composite films from micron-sized graphite oxide sheets and polycations[J].Chem Mater,1999,11(3):771-778.
[8] Li S,Wu D Q,Cheng C,et al.Electrochemical supercapacitors from conducting polyaniline-graphene platforms[J].Angew Chem Int Ed,2013,52(46):12105-12109.
[9] Wang W,Li F,Zhao J,et al.Fabrication of graphene/polyaniline composite paper via in situ anodic electropolymerization for high-performance flexible electrode[J].ACS Nano,2009,3(7):1745-1752.
[10] 邓玲娟.过渡金属氧化物/石墨烯纳米电极材料制备及其电容性质研究[D].西安:陕西师范大学,2013.
[11] Hua M Y,Su Y N,Chen S A.Water-soluble self-acid-doped conducting polyaniline:poly(aniline-Co-N-propylbenzenesulfonic acid-aniline)[J].Polymer,2000,41(2):813-815.
[12] Wan M X.A template-free method towards conducting polymer nano-structures[J].Adv Mater,2008,20(15):2926-2932.
[13] Nethravathi C,Rajamathi M,Ravishankar N,et al.Synthesis of graphene oxide-intercalated α-hydroxides by metathesis and their decomposition to graphene/metal oxide composites[J].Carbon,2010,48(15):4343-4350.
[14] Gotoh K,Kinumoto T,Fujii E,et al.Exfoliated graphene sheets decorated with metal/metal oxide nanoparticles:simple preparation from cation exchanged graphite oxide[J].Carbon,2011,49(4):1118-1125.
[15] Li D,Marc B,Scott G.Processable aqueous dispersions of graphene nanosheets[J].Nat Nanotech,2008,3:101-105.
[16] 莫尊理,左丹丹,陈红,等.纳米石墨薄片/聚吡咯复合材料的制备[J].无机化学学报,2007,23(2):265-269.
[17] 陈思明.新型石墨材料的制备及其在电化学领域方面的应用[D].北京:北京化工大学,2010.
基金资助
陕西省自然科学基础研究计划项目(2018JQ2065);宝鸡市科技计划项目(2017JH2-04);宝鸡文理学院博士启动项目(ZK2017031);宝鸡文理学院大学生创新创业训练计划项目(2017dc108)
PDF
(3271KB)