化工新型材料 ›› 2019, Vol. 47 ›› Issue (3) : 247-250. DOI:

开发与应用

红色荧光粉Zr(MoO₄)₂·MoO₃∶Eu³⁺的发光性能和能量转移

隆金桥,刘真珍,阳婷,郑丽雪,欧阳思铭,孙榕励

作者信息 +

Optical property and energy transfer in the red phosphor Zr(MoO₄)₂·MoO₃∶Eu³⁺

Long Jinqiao, Liu Zhenzhen ,Yang Ting, Zheng Lixue, Ouyang Siming, Sun Rongli

Author information +

文章历史 +

PDF (1702K)

摘要

采用共沉淀法制备了一系列Zr(MoO₄)₂·MoO₃∶Eu³⁺,并对荧光粉进行了X射线衍射仪和荧光光谱仪分析。结果表明:荧光粉为一混晶,由Zr(MoO₄)₂和MoO₃组成。荧光粉在465nm的激发下,在617nm处产生强的红光发射,发射光谱在617nm处的强度是激发光谱在465nm处强度的2.26倍。这是因为在465nm的激发下,Eu³⁺的能量从磁偶极中心转移到电偶极中心,使617nm处发光增强。对蓝光激发白光LED而言,Zr(MoO₄)₂·MoO₃∶Eu³⁺是具有一定应用前景的红色荧光粉。

Abstract

A series of Zr(MoO₄)₂·MoO₃∶Eu³⁺ phosphors were prepared by coprecipitation method,and analyzed by XRD and PL.The results showed that the phosphors had mixture crystalline phases of Zr(MoO₄)₂ and MoO₃.The phosphors excited by 465nm,and exhibited strong red emission peak at 617nm.Emission spectrum (PL) intensity at 617nm was 2.26 times as high as excitation spectrum (PLE) intensity at 465nm.It was because that cooperative energy transfers from MD center to ED-Eu³⁺ excited by 465nm,enhanced photoluminescence at 617nm.Zr(MoO₄)₂·MoO₃∶Eu³⁺ was a red-emitting phosphor which had application prospect for blue-based white LED.

关键词

无机化合物 / 能量转移 / 荧光粉 / 光学性能

Key words

inorganic compound / energy transfer / phosphor / optical property

引用本文

引用格式 ▾

红色荧光粉Zr(MoO₄)₂·MoO₃∶Eu³⁺的发光性能和能量转移[J]. 化工新型材料, 2019, 47(3): 247-250 DOI:

登录浏览全文

4963

注册一个新账户忘记密码

参考文献

原文顺序 | 出版日期 | 本文引用

[1] Sun X Y,Hao Z D,Li C J,et al.Enhanced orange-red emission by using Mo codoped in Ba₂WO₆∶Eu³⁺,Li⁺ phosphor under near UV exctiation[J].J Lumin,2013,134(1):191-194.
[2] Liu Y,Lu Z G,Gu Y Y,et al.Hydrothermal-assisted ion exchange synthesis and photoluminescence of Li⁺ and Eu³⁺ co-dopednaLa(WO₄)₂ as near-UV type red phosphors[J].J Lumin,2012,5(132):1220-1225.
[3] Shen X Q,Li L L,He F L,et al.Effects of doped Li⁺ and Eu³⁺ ions contento structured luminescent properties of La_xSr_1-2x(MoO₄)∶Eu^3+x red emitting phosphors for white LEDs[J].Mater Chem Phys,2012,132:471-475.
[4] Yang Z P,Liu Y F,Wang L W,et al.Luminescence,properties of the single white emitting phosphor Eu²⁺,Mn²⁺ co-doped Ca₂SiO₃Cl₂[J].Acta Phys Sin,2007,56(4):546-550.
[5] Huh Y,Park J,Kweon S,et al.Phosphor converted three band white LED[J].Bull Korean Chem Soc,2004,25:1585-1588.
[6] Chen F M,Liu X H.Structure and photoluminescence properties of La₂Mo(W)O₆∶Eu³⁺ as red phosphors for white LED applications[J].Opt Mater,2013,35:2716-2720.
[7] Tian Y,Qi X H,Wu X W,et al.Luminescent properties of Y₂(MoO₄)₃∶Eu³⁺ red phosphors with flower like shape prepared via coprecipitation method[J].J Phys Chem,2009,113:10767-10772.
[8] Cheng L H,Zhong H Y,Sun J S,et al.Flux and concentration effecton Eu³⁺ doped Gd₂(MoO₄)₃ phosphor[J].J Rare Earths,2008,26(2):211-214.
[9] Pang M L,Liu X M,Lin J.Luminescence properties of R₂MoO₆∶Eu³⁺(R=Gd,Y,La) phosphors prepared by pechini sol-gel process[J].J Mater Res,2005,10(20):2676-2681.
[10] Meng F G,Zhang X M,Li H,et al.Synthesis and spectral characteristics of La₂MoO₆∶Ln³⁺(Ln=Eu,Sm,Dy,Pr,Tb) polycrystals[J].J Rare Earths,2012,30(9):866-870.
[11] Jin H J,Wu H,Tian L I.Improved luminescence of Y₂MoO₆∶Eu³⁺ by doping Li⁺ ions for light emitting diode application[J].J Lumin,2012,132:1188-1191.
[12] 朱德生,姜锋.NH₄Cl助熔合成CaMoO₄∶Eu³⁺红色荧光粉及其发光性质[J].功能材料,2017,48(3):03232-03237,03242.
[13] 任凯,张建夫,常艺,等.Ca²⁺_(1-x)Na⁺_xMoO₄∶Eu³⁺荧光粉的合成及发光性能的研究[J].周口师范学院学报,2016,33(5):98-101.
[14] 冯颖,童义平,文思.微波辅助溶胶-凝胶法合成Gd_0.4(MoO₄)₃∶1.6Eu³⁺红色荧光粉及其发光性能的研究[J].人工晶体报,2016,54(4):1024-1028.
[15] 欧阳艳,张晓蓉,许艳红,等.共沉淀法合成NaLa(MoO₄)₂∶Eu³⁺红色荧光粉及其发光性能的研究[J].化工新型材料,2016,44(8):128-130,134.
[16] 张振乾,马晶,赵婉男,等.NaGd(MoO₄)₂∶Eu³⁺发光粉的水热合成与发光性质[J].硅酸盐通报,2016,35(11):3541-3545.
[17] 王桂萍,王桂燕.La₂(MoO₄)₃∶Eu³⁺纳米红色荧光粉的合成及其发光特性[J].精细化工,2017,34(7):725-729.
[18] Zhang X,Li W,Seo H J.Concentration dependence of energy transfer between Eu²⁺ ions occupying two crystallographic sites in Ba_1.6Ca_0.4P₂O₇[J].Electrochem Soc,2011,158:J155-J157.
[19] Mondal S S,Behrens K,Matthes P R,et al.White light emission of IFP-1 by in situ co-doping of the MOF pore system with Eu³⁺ and Tb³⁺[J].J Mater Chem C,2015,3:4623-4631.
[20]Yang L,Zhou L,Huang Y,et al.Ag-catalyzed synthesis of europium borate Eu-(BO₂)₃ nanoeires,groeth mechanism and luminescent properties[J].Mater Res Bull,2011,46:239-243.
[21] Peter A J,Banu I B S.Enhanced photoluminescence of Li₃Ba₂Gd₃(MoO₄)₈∶Eu³⁺ red phosphor synthesized by mechanochemically assisted direct solid state reaction method at room temperature[J].Mater Sci Mater Electron,2015,26:2045-2052.
[22] Wu H M,Chen H,Liu Y F,et al.Highly uniform NaLa(MoO₄)₂∶Eu³⁺ microspheres:microwave-assisted hydrothermal synthesis,growthmechanism and enhanced luminescent properties[J].J Mater Sci Mater Electron,2014,25:3109-3115.
[23] Liao J H,Zhou D,Yang B,et al.Sol-gelpreparation and photoluminescence properties of CaLa₂(MoO₄)₄∶Eu³⁺ phosphors[J].Lumin,2013,134:533-538.
[24] Ghosh P,Mudring A V.Phase selective synthesis of quantum cutting nanophosphors and the observation of a spontaneous room temperature phase transition[J].Nanoscale,2016,8:8160-8169.
[25] You F T,Huang S H,Liu S M,et al.VUV excited luminescence of MGdF₄∶Eu³⁺(M=Na,K,NH₄)[J].Lumin,2004,110:95-99.
[26] Tian B N,Chen B J,Tian Y,et al.Visible quantum cutting in BaGd₂ZnO₅∶Eu³⁺ phosphor[J].Ceram Int,2012,38:3537-3540.
[27] Zhang S Y,Huang Y L,Nakai Y,et al.The luminescence characterization and thermal stability of Eu²⁺ ions-doped NaBaPO₄ phosphor[J].Am Ceram Soc,2011,94:2987-2992.
[28] Yu X,Xu X H,Yu H L,et al.Persistence energy transfer between inequivalent Eu²⁺ ions in CaAl₂Si₂O₈∶Eu²⁺[J].Mater Res Bull,2012,47:2696-2699.
[39] 何冬丽,吕树臣,曲秀荣,等.Gd₂(WO₄)₃∶Eu³⁺,Sm³⁺纳米晶的制备及Sm³⁺对Eu³⁺特征发射的敏化作用[J].发光学报,2013,34(2):171-177.
[30] 吴中立,张艳秋,陈宝玖.KLa(MoO₄)₂∶Sm³⁺,Eu³⁺荧光粉中能量传递研究[J].稀有金属材料与工程,2015,44(10):2476-2480.