化工新型材料

化工新型材料 ›› 2018, Vol. 46 ›› Issue (11) : 125-128.

新材料与新技术

自模板法制备球形LiMn₂O₄及其电化学性能研究

作者信息 +

Spherical LiMn₂O₄:self-template synthetic route and electrochemical performance

Mu Yanlin, Wang Li, Zhou Yurong, Chen Guanhua, Qiao Lu, Zhao YanLiu, Mengjiao, Gao Daojiang

Author information +

文章历史 +

Received		Published
2017-06-27		2018-11-20
Issue Date	Revised Date
2018-12-04	2017-06-27

PDF (4680K)

摘要

利用液相沉淀法制备MnCO₃前驱体,该前驱体为球形,且分散均匀。利用MnCO₃前驱体作为自模板进一步制备球形LiMn₂O₄,通过优化制备条件,采用X射线衍射仪、扫描电镜和恒电流充放电测试对球形LiMn₂O₄进行测试。结果表明:煅烧温度对材料的结构、形貌以及电化学性能有影响。当煅烧温度为700℃,煅烧时间为8h时可制得结构良好的LiMn₂O₄,其分散性较好,形貌为中空球形。在0.2C倍率下进行充放电测试,首次放电容量可以达到123.6mAh/g,30次循环后容量保持率为93.12%,展现了良好的电化学性能。

Abstract

MnCO₃ precursor was prepared by liquid phase precipitation method.The precursor was spherical and homogeneous distribution,then used as self-template to prepare spherical LiMn₂O₄.The synthetic conditions,morphologies and electrochemical performances were investigated.The results which from the series tests,such as X-ray diffraction (XRD),scanning electronic microscope (SEM) and constant current charge and discharge,indicated that calcination temperatures had influence on the structures,morphologies and electrochemical performance.When the calcination temperature was 700℃ and the calcination time was 8h,the hollow spherical products with good structure and good dispersion were obtained.LiMn₂O₄ microspheres obtained by optimal synthetic route can deliver a discharge capacity of 123.6mAh/g at 0.2C and 93.12% of the initial storage capacity was maintained after 30 cycles,which showed good electrochemical performance.

关键词

锂离子电池 / 正极材料 / 自模板法 / LiMn₂O₄ / 电化学性能

Key words

lithium-ion battery / anode / self-template / LiMn₂O₄ / electrochemical performance

引用本文

引用格式 ▾

自模板法制备球形LiMn₂O₄及其电化学性能研究[J]. 化工新型材料, 2018, 46(11): 125-128 DOI:

登录浏览全文

4963

注册一个新账户忘记密码

参考文献

原文顺序 | 出版日期 | 本文引用

[1] Dunn J B,Gaines L,Sullivan J,et al.The impact of recycling on cradle-to-gate energy consumption and greenhouse gas emissions of automotive lithium-ion batteries[J].Environmental Science & Technology,2012,46(22):12704-12710.
[2] Mahmood N,Tang T,Hou Y.Nanostructured anode materials for lithium ion batteries:progress,challenge and perspective[J].Advanced Energy Materials,2016,6(17):1-22.
[3] Xu J,Dou S,Liu H,et al.Cathode materials for next generation lithium ion batteries[J].Nano Energy,2013,2(4):439-442.
[4] Su L W,Jing Y,Zhou Z.Li ion battery materials with core-shell nanostructures[J].Nanoscale,2011,3(10):3967-3983.
[5] Huang Q,Yang J.Redox flow lithium battery based on the redox targeting reactions between LiFePO₄ and iodide[J].Energy & Environmental Science,2016,9(3):917-921.
[6] Wu X,Li X,Wang Z,et al.Improvement on the storage performance of LiMn₂O₄ with the mixed additives of ethanolamine and heptamethyldisilazane[J].Applied Surface Science,2013,268(3):349-354.
[7] Lesel B K,Ko J S,Dunn B,et al.Mesoporous Li_xMn₂O₄ thin film cathodes for lithium-ion pseudocapacitors[J].ACS Nano,2016,10(8):7572-7581.
[8] Ragavendran K,Chou H L,Lu L,et al.Crystal habits of LiMn₂O₄ and their influence on the electrochemical performance[J].Materials Science and Engineering:B,2011,176(16):1257-1263.
[9] Zhang H,Xu Y L,Liu D.Novel nanostructured LiMn₂O₄ microspheres for high power Li-ion batteries[J].RSC Advances,2014,5(15):11091-11095.
[10] 陈守彬,吴显明,陈上,等.不同锰源制备尖晶石LiMn₂O₄及电化学性能研究[J].应用化工,2016,45(1):18-21.
[11] Xu G J,Liu Z H,Zhang C J,et al.Strategies for improving the cyclability and thermo-stability of LiMn₂O₄-based batteries at elevated temperatures[J].Journal of Materials Chemistry A,2015,3(8):4092-4123.
[12] Han C G,Zhu C Y,Saito G,et al.Improved electrochemical properties of LiMn₂O₄ with the Bi and La co-doping for lithium-ion batteries[J].RSC Advances,2015,5(89):73315-73322.
[13] Fu M H,Huang K L,Liu S Q,et al.Lithium difluoro(oxalato)borate/ethylene carbonate+propylene carbonate+ethyl(methyl) carbonate electrolyte for LiMn₂O₄ cathode[J].Journal of Power Sources,2010,195(3):862-866.
[14] Demirel S,Oz E,Altin S,et al.Enhancement of battery performance of LiMn₂O₄:correlations between electrochemical and magnetic properties[J].RSC Advances,2016,6(49):43823-43831.
[15] Zhang H,Xu Y,Liu D,et al.Structure and performance of dual-doped LiMn₂O₄ cathode materials prepared via microwave synthesis method[J].Electrochimica Acta,2014,125(12):225-231.
[16] Feng X,Zhang J,Yin L.Effect of AlP coating on electrochemical properties of LiMn₂O₄ cathode material for lithium ion battery[J].Materials Research Bulletin,2016,74:421-424.
[17] Huang S,Wu H,Chen P,et al.Facile pH-mediated synthesis of morphology-tunable MnCO₃ and their transformation to truncated octahedral spinel LiMn₂O₄ cathode materials for superior lithium storage[J].Journal of Materials Chemistry A,2015,3(7):3633-3640.
[18] Zhu P,Chu X,Zhou F,et al.Synergistic effect for the preparation of LiMn₂O₄ microspheres with high electrochemical performance[J].RSC Advances,2014,4(7):3293-3298.
[19] Zhou L,Zhou X,Huang X,et al.Designed synthesis of LiMn₂O₄ microspheres with adjustable hollow structures for lithium-ion battery applications[J].Journal of Materials Chemistry A,2013,1(3):837-842.
[20] Ding Y L,Zhao X B,Xie J,et al.Double-shelled hollow microspheres of LiMn₂O₄ for high-performance lithium ion batteries[J].Journal of Materials Chemistry,2011,21(26):9475-9479.
[21] Zhang G,Yu L,Wu H B,et al.Formation of ZnMn₂O₄ ball-in-ball hollow microspheres as a high-performance anode for lithium-ion batteries[J].Advanced Materials,2012,24(34):4609-4613.